Melting process of casting aluminum bar for aluminum profile

A technology of aluminum profiles and aluminum rods, applied in spray booths, spray devices, etc., can solve problems affecting the purity, smoothness and strength of aluminum profiles

Active Publication Date: 2018-05-18
奋安铝业股份有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] This invention patent improves the efficiency of aluminum rod melting and casting, but the technical solution of this invention is similar to other aluminum rod melting and casting processes on the market. There are oxide layers formed inside and on the surface of the cast aluminum rod, because the oxide layer of the aluminum rod is relatively hard and difficult to Melting, when the aluminum rod is subsequently pressurized to process the aluminum profile, the oxide layer of the aluminum rod will increase the extrusion process requirements and affect the quality parameters of the aluminum profile such as purity, smoothness and strength as impurities

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] In order to further explain the technical solutions of the present invention, specific examples are given below to illustrate in detail.

[0038] The smelting process of a fused cast aluminum rod for an aluminum profile of the present invention comprises the following steps:

[0039] (1) put the aluminum raw material into the smelting furnace, feed nitrogen into the smelting furnace, and discharge the air in the smelting furnace;

[0040] (2) Use a smelting furnace to melt aluminum raw materials into molten aluminum, and use ultrasonic waves to uniformly vibrate and stir the molten aluminum;

[0041] (3) Discharging the impurities on the surface of the molten aluminum and the bottom layer of the molten aluminum respectively, while using heated nitrogen to discharge the air in the aluminum rod casting device and preheating the aluminum rod casting device;

[0042] (4) Squeeze molten aluminum liquid into the aluminum rod mold tube of the aluminum rod casting device from ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a melting process of a casting aluminum bar for aluminum profile. Aluminum raw materials are put into a smelting furnace, nitrogen is injected into the smelting furnace, and airin the smelting furnace is discharged; the aluminum raw materials are melted into molten aluminum liquid by using the smelting furnace, and the molten aluminum liquid is evenly vibrated and stirred by using ultrasonic waves; impurities on the surface of the molten aluminum liquid and impurities on the bottom layer of the molten aluminum liquid are separately discharged, and air in an aluminum barcasting device is discharged by using the heated nitrogen and the aluminum bar casting device is preheated; the molten aluminum liquid is extruded from bottom to top into an aluminum bar die tube ofthe aluminum bar casting device; redundant molten aluminum liquid is collected; an aluminum bar is formed by cooling the aluminum bar die tube and the molten aluminum liquid inside the aluminum bar die tube; an anti-oxidation coating is formed by spraying anti-oxidation coating on the surface of the aluminum bar; and the aluminum bar is taken out. According to the melting process of the casting aluminum bar for the aluminum profile, impurities are obviously decreased, the oxidation degree is reduced, and the quality of the aluminum bar and aluminum profile products is enhanced.

Description

technical field [0001] The invention relates to the field of aluminum rod melting and casting technology, in particular to a melting technology for melting and casting aluminum rods used for aluminum profiles. Background technique [0002] The melting and casting process of aluminum rods is well known. For example, the Chinese invention patent CN201310538784.9 discloses a melting and casting process of aluminum rods. The process includes the following steps: S1, preparing aluminum ingots and auxiliary materials, and sequentially adding them to the melting furnace; Smelting aluminum ingots and auxiliary materials at a temperature of 900°C to 970°C to obtain molten aluminum, the temperature of the molten aluminum is between 700°C to 760°C; S3, stirring and removing slag after the aluminum ingots are fully melted; S4 1. Refining by putting the refining agent into the duster and blowing in nitrogen gas. After refining, the temperature of the aluminum solution is between 730°C an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B21/06B22D21/04B05B16/00
CPCB22D21/04C22B21/064
Inventor 黄秀华黄奋
Owner 奋安铝业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products