A kind of polycation anti-mud type polycarboxylate superplasticizer and preparation method thereof

A polycationic, mud-resistant technology, applied in the field of concrete admixtures, can solve the problems of large adsorption and poor use effect of polycarboxylate superplasticizer, and achieve the effect of inhibiting adsorption, difficult desorption and high positive charge density.

Active Publication Date: 2020-06-23
武汉优城科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large adsorption of polycarboxylate by clay due to its layered structure, the effect of polycarboxylate superplasticizers in raw materials with high mud content is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polycation anti-mud type polycarboxylate superplasticizer and preparation method thereof
  • A kind of polycation anti-mud type polycarboxylate superplasticizer and preparation method thereof
  • A kind of polycation anti-mud type polycarboxylate superplasticizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This example provides a polycationic anti-mud type polycarboxylate superplasticizer and its preparation method:

[0037] The first step: preparation of unsaturated anti-mud type monomer C solution

[0038] Put 174 parts of hydroxyethyl acrylate into the reactor, and add dropwise a hydrochloric acid solution containing 142 parts of tetraethylenepentamine at 30°C for 1 hour to obtain the unsaturated mud-resistant monomer C solution.

[0039] The general formula of the unsaturated anti-mud type monomer C is:

[0040]

[0041] where R 1 for H, R 2 for CH 2 CH 2 .

[0042] The second step: preparation of polycation anti-mud type polycarboxylate superplasticizer

[0043] Put 2400 parts of polyether macromonomer TPEG (prenyl alcohol polyoxyethylene ether, molecular weight 2400) in the reactor, add water to dissolve; 144 parts of acrylic acid and the prepared unsaturated anti-mud type monomer C solution, mix and dissolve , recorded as X component; 16 parts of hydrogen...

Embodiment 2

[0045] This example provides a polycationic anti-mud type polycarboxylate superplasticizer and its preparation method:

[0046] The first step: preparation of unsaturated anti-mud type monomer C solution

[0047] Put 65 parts of hydroxypropyl acrylate into the reactor, and add dropwise a hydrochloric acid solution containing 94 parts of tetraethylenepentamine at 60°C for 2 hours to obtain the unsaturated mud-resistant monomer C solution.

[0048] The general formula of the unsaturated anti-mud type monomer C is:

[0049]

[0050] where R 1 for H, R 2 for (CH 3 )CHCH 2 .

[0051] The second step: preparation of polycation anti-mud type polycarboxylate superplasticizer

[0052] Put 2400 parts of polyether macromonomer HPEG (methallyl polyoxyethylene ether, molecular weight 2400) in the reactor, add water to dissolve; 288 parts of acrylic acid and the prepared unsaturated anti-mud type monomer C solution, mix Dissolved, recorded as X component; 18 parts of hydrogen pero...

Embodiment 3

[0054] This example provides a polycationic anti-mud type polycarboxylate superplasticizer and its preparation method:

[0055] The first step: preparation of unsaturated anti-mud type monomer C solution

[0056] Put 97.5 parts of hydroxyethyl methacrylate into the reactor, and add dropwise a hydrochloric acid solution containing 106.5 parts of tetraethylenepentamine at 45°C for 1.5 hours to obtain the unsaturated mud-resistant monomer C solution.

[0057] The general formula of the unsaturated anti-mud type monomer C is:

[0058]

[0059] where R 1 for CH 3 , R 2 for CH 2 CH 2 .

[0060] The second step: preparation of polycation anti-mud type polycarboxylate superplasticizer

[0061] Put 2400 parts of polyether macromonomer VPEG (4-hydroxybutyl vinyl polyoxyethylene ether, molecular weight 2400) in the reactor, add water to dissolve; 216 parts of acrylic acid and the prepared unsaturated anti-mud type monomer C solution , mix and dissolve, and record it as compon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multi-cation mud-resisting type polycarboxylic acid water reducer and a preparation method thereof. The multi-cation mud-resisting type polycarboxylic acid water reducer is prepared by polymerizing a polyether macro-monomer A, unsaturated carboxylic acid / unsaturated carboxylic acid anhydride B, and an unsaturated mud-resisting type monomer C in a water solution, wherein the unsaturated mud-resisting type monomer C is prepared by taking unsaturated hydroxyl ester and a hydrochloric acid solution of tetraethylenepentamine to react. The mud-resisting type polycarboxylicacid water reducer disclosed by the invention can be hydrolyzed under an alkaline condition to release a multi-cation type long-chain organic matter, physical and chemical properties of clay mineralscan be changed, expansion of the expansion type clay minerals is inhibited, and the consumption of polycarboxylic acid and water by mineral surfaces and crystal layers is reduced, so that the utilization performance of the polycarboxylic acid water reducer in a high-mud-content material is ensured, and the mud-resisting effect is realized; the problem that the clay minerals in a high-mud-content sand gravel material influences the utilization performance of the polycarboxylic acid water reducer is solved.

Description

technical field [0001] The invention belongs to the technical field of concrete admixtures, in particular to a polycationic anti-mud type polycarboxylate water reducer and a preparation method thereof. Background technique [0002] The addition of chemical admixtures can greatly improve the durability, workability, applicability, economy and strength of concrete, and provide a strong guarantee for the quality of large-scale projects. Therefore, its wide application is known as the successor to reinforced concrete and prestressed concrete. The 3rd major breakthrough in concrete technology after concrete. [0003] Polycarboxylate superplasticizer has become the most important product in the current concrete admixture market due to its advantages such as low dosage, high water reducing rate, good slump retention, strong molecular structure adjustability, and environmental protection. Polycarboxylate superplasticizer is a comb-shaped water-soluble polymer, which is composed of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/06C08F222/22C08F4/40C04B24/26C04B103/30
CPCC04B24/267C04B2103/302C08F4/40C08F283/065C08F220/06C08F222/22
Inventor 代柱端陈健董耀武周晓阳
Owner 武汉优城科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com