A kind of sculpture cement preparation device for arts and crafts

A preparation device and technology for arts and crafts, which is applied in the field of sculpture cement preparation devices for arts and crafts, can solve problems such as low adhesion, easy mildew, and easy cracking of large sculptures, and achieve the effect of convenient operation and use, and high automation

Inactive Publication Date: 2020-09-15
ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Sculpture is a kind of handicraft that we often see in our life. Most of the sculptures are made of sculpture clay. At present, many sculptures use natural clay and auxiliary materials to make sculpture clay. These clays have low adhesion to steel bars and other materials. Large-scale sculptures are prone to cracking, and molded products are prone to defects or damage. There are also some sculpture cements made of paper pulp, clay and adhesives. suitable for educational use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sculpture cement preparation device for arts and crafts
  • A kind of sculpture cement preparation device for arts and crafts
  • A kind of sculpture cement preparation device for arts and crafts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment one: 80 parts of carboxymethyl cellulose CMC, 95 parts of carboxymethyl cellulose CMS, 10 parts of dioctyl isophthalate, 50 parts of glycerol, 2.8 parts of sodium benzoate, 100 parts of light calcium carbonate, carbonic acid Magnesium 60 parts, talcum powder 225 parts, titanium dioxide 120 parts, purified water 370 parts. The sculpture cement is preferably made of the raw materials in this weight part, and the prepared sculpture cement has the advantages of uniform color, slight fragrance, good adhesion, and no pollution.

Embodiment 2

[0021] Embodiment two: 95 parts of carboxymethyl cellulose CMC, 80 parts of carboxymethyl cellulose CMS, 7 parts of dioctyl isophthalate, 60 parts of glycerol, 0.6 part of sodium benzoate, 120 parts of light sodium calcium carbonate, carbonic acid Magnesium 80 parts, talcum powder 120 parts, titanium dioxide 130 parts, purified water 390 parts. The sculpture clay is preferably made of the raw materials of this weight part. The prepared sculpture clay has uniform color, slight fragrance, extremely low toxicity, less impurities, cold resistance (-17 ° 2 hours), heat resistance (45 ° 2 hours), etc. advantage.

Embodiment 3

[0022] Embodiment three: 110 parts of carboxymethyl cellulose CMC, 110 parts of carboxymethyl cellulose CMS, 4 parts of dioctyl isophthalate, 40 parts of glycerol, 5 parts of sodium benzoate, 110 parts of light sodium calcium carbonate, carbonic acid Magnesium 70 parts, talcum powder 130 parts, titanium dioxide 225 parts, purified water 350 parts. The sculpture cement is preferably made of the raw materials of this weight part. The prepared sculpture cement has extremely low toxicity, less impurities, cold resistance (-17 ° 2 hours), heat resistance (45 ° 2 hours), good adhesion, and no pollution And other advantages, the arts and crafts sculptures made of this clay are not afraid of wind and rain, and are not easy to crack and deform.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses sculpture cement gum for arts and crafts. The sculpture cement gum is prepared from the following raw materials in parts by weight: 80-100 parts of carboxymethyl cellulose CMC,80-100 parts of carboxymethyl cellulose CMS, 4-10 parts of dioctyl isophthalate, 40-60 parts of glycerol, 0.6-5 parts of sodium benzoate, 100-120 parts of light shortite, 60-80 parts of magnesium carbonate, 120-130 parts of talcum powder, 120-130 parts of titanium dioxide and 350-390 parts of purified water. The sculpture cement gum prepared has the advantages of being uniform in color and luster, slight in fragrance, extremely low in toxicity, fewer in impurities, resistant to cold and heat, good in adhesion force, free of pollution and the like. Art and craft sculpture prepared from the cement gum has the advantages of being resistant to wind and rain, not liable to crack and deform, suitable for long-term storage and the like, and is further suitable for teaching use.

Description

technical field [0001] The invention relates to a technique for preparing sculpture glue, in particular to a preparation device for sculpture glue for arts and crafts. Background technique [0002] Sculpture is a kind of handicraft that we often see in our life. Most of the sculptures are made of sculpture clay. At present, many sculptures use natural clay and auxiliary materials to make sculpture clay. These clays have low adhesion to steel bars and other materials. Large-scale sculptures are prone to cracking, and molded products are prone to defects or damage. There are also some sculpture cements made of paper pulp, clay and adhesives. It is not suitable for teaching use. Contents of the invention [0003] The invention provides a device for preparing sculpture cement for arts and crafts, which is used to solve the defects in the prior art. [0004] The present invention is achieved through the following technical solutions: [0005] A sculpture cement preparation d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L1/28C08K13/02C08K5/098C08K3/26C08K3/34C08K3/22
CPCC08K2003/2241C08K2003/265C08K2003/267C08L1/286C08L2205/025C08K13/02C08K5/098C08K3/26C08K3/34C08K3/22
Inventor 张丽娟轩玉琴穆冰玉温丽琴陈嘉钰
Owner ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap