Transparent ceramic material and preparation method thereof

A technology of transparent ceramics and raw materials, applied in the field of ceramic materials, can solve the problems of poor quality of finished products, short production cycle, low preparation temperature, etc.

Inactive Publication Date: 2018-03-16
桂林市晟博科技服务有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with glass, transparent ceramics have high strength, high toughness, and better resistance to surface damage; compared with single crystals, transparent ceramics have lower prepar...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of transparent ceramic material of the present embodiment, comprises the raw material of following weight part: 65 parts of silicon dioxide, 15 parts of aluminum oxide, 0.3 part of ferric oxide, 0.5 part of calcium oxide, 1 part of potassium oxide, 1 part of oxide Lanthanum, 3 parts magnesium oxide, 2 parts lithium oxide, 2 parts phosphorus trioxide, 6 parts calcium nitride.

[0018] The preparation method of the transparent ceramic material of the present embodiment comprises the following steps:

[0019] (1) Get the transparent ceramic raw materials in the above weight parts, mix them uniformly, add a binder and extrude to obtain a semi-finished product;

[0020] (2) Raise the temperature of the extruded semi-finished product to 1500°C, and immediately cool it down to 380°C, and keep it warm for 50 hours;

[0021] (3) Vacuum sinter the semi-finished product after heat preservation for 5 hours, the vacuum sintering temperature is 1600° C., and the transparent c...

Embodiment 2

[0027] A kind of transparent ceramic material of the present embodiment, comprises the raw material of following weight part: 75 parts of silicon dioxide, 20 parts of aluminum oxide, 0.4 part of ferric oxide, 0.8 part of calcium oxide, 1.5 parts of potassium oxide, 2 parts of oxide Lanthanum, 4 parts magnesium oxide, 3 parts lithium oxide, 3 parts phosphorus trioxide, 7 parts calcium nitride.

[0028] The preparation method of the transparent ceramic material of the present embodiment comprises the following steps:

[0029] (1) Get the transparent ceramic raw materials in the above weight parts, mix them uniformly, add a binder and extrude to obtain a semi-finished product;

[0030] (2) Raise the temperature of the extruded semi-finished product to 1600°C, and immediately cool it down to 500°C, and keep it warm for 70 hours;

[0031] (3) Vacuum sinter the semi-finished product after heat preservation for 8 hours, the vacuum sintering temperature is 1700° C., and the transpare...

Embodiment 3

[0037] A kind of transparent ceramic material of the present embodiment, comprises the raw material of following weight part: 80 parts of silicon dioxide, 25 parts of aluminum oxide, 0.5 part of ferric oxide, 1 part of calcium oxide, 2 parts of potassium oxide, 4 parts of oxide Lanthanum, 5 parts of magnesium oxide, 5 parts of lithium oxide, 4 parts of phosphorus trioxide, 8 parts of calcium nitride.

[0038] The preparation method of the transparent ceramic material of the present embodiment comprises the following steps:

[0039] (1) Get the transparent ceramic raw materials in the above weight parts, mix them uniformly, add a binder and extrude to obtain a semi-finished product;

[0040] (2) Raise the temperature of the extruded semi-finished product to 1700°C, and immediately cool it down to 700°C, and keep it warm for 120 hours;

[0041] (3) Vacuum sinter the semi-finished product after heat preservation for 12 hours, the vacuum sintering temperature is 1900° C., and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a transparent ceramic material and a preparation method thereof. The transparent ceramic material comprises, by weight, 65-80 parts of silica, 15-25 parts of alumina, 0.3-0.5part of ferric oxide, 0.5-1 part of calcium oxide, 1-2 parts of potassium oxide, 1-4 parts of lanthana, 3-5 parts of magnesium oxide, 2-5 parts of lithium oxide, 2-4 parts of phosphorus trioxide and 6-8 parts of calcium nitride. The transparent ceramic material has the advantages of high light transmittance, few ceramic production processes, low energy consumption and low cost.

Description

technical field [0001] The invention relates to a ceramic material, in particular to a transparent ceramic material and a preparation method thereof. Background technique [0002] Daily-use ceramic products are easy to wash and keep clean, have good thermal stability and slow heat transfer; in addition, ceramic products have stable chemical properties and are durable, with fewer pores and low water absorption. However, compared with glass, transparent ceramics have high strength, high toughness, and better resistance to surface damage; compared with single crystals, transparent ceramics have lower preparation temperatures, shorter production cycles, and are superior in large size and structural design. Single crystal is easier to realize, and the finished quality of existing transparent ceramic products is poor. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a transparent ceramic material and a preparation meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/14C04B35/622C04B35/64
CPCC04B35/14C04B35/622C04B35/64C04B2235/3201C04B2235/3203C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3227C04B2235/3272C04B2235/34C04B2235/3852C04B2235/5445C04B2235/6562C04B2235/6565C04B2235/6567C04B2235/661C04B2235/9653
Inventor 王君李力刘谋军
Owner 桂林市晟博科技服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap