A kind of luminous ceramic glazed tile and its preparation method

A technology of luminescent ceramics and glazed tiles, applied in the field of architectural ceramics, can solve the problems of luminescent powder failure, damage to the internal structure of luminescent powder, and high refractoriness of luminescent powder, and to prevent passers-by from falling, strong controllability and high refractoriness. Effect

Active Publication Date: 2020-11-13
FOSHAN OCEANO CERAMICS +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that under high temperature conditions, the luminescent powder in the glaze is easily eroded by the high-temperature flux, which destroys the internal structure of the luminescent powder and causes the luminescent powder to fail.
In addition, since the synthesis temperature of luminescent powder is generally above 1300°C, the luminescent powder has high refractoriness and is not easy to be melted and flattened in the glaze layer, resulting in uneven glaze surface.
Therefore, luminescent powder has not been applied in high-temperature ceramic glazed tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A luminescent ceramic glazed tile comprises a body layer, an underglaze layer, a floral glaze layer, a luminous layer and a polished glaze layer from bottom to top.

[0028] The luminescent layer is composed of luminescent powder doped with a base material with a rare earth activator, and its particle size is 80 mesh.

[0029] The green body layer includes the following chemical components in terms of raw material weight percentage: 67% SiO 2 , 21% Al 2 o 3 , 1% Fe 2 o 3 , 0.4% TiO 2 , 0.5% CaO, 0.3% MgO, 3% K 2 O, 3% Na 2 O.

[0030] The bottom oil layer comprises the following chemical components in terms of raw material weight percentage: 68% SiO 2 , 22% Al 2 o 3 , 0.1% Fe 2 o 3 , 0.3% TiO 2 , 1.5% CaO, 1.5% MgO, 3% K 2 O, 2% Na 2 O, 0.1% ZrO 2 , 0.5% ZnO.

[0031] The glaze layer comprises the following chemical components in terms of raw material weight percentage: 45% SiO 2 , 8% Al 2 o 3 , 0.1% Fe 2 o 3 , 0.1% TiO 2 , 10% CaO, 4.5% MgO, 2% K...

Embodiment 2

[0041] A luminescent ceramic glazed tile comprises a body layer, an underglaze layer, a floral glaze layer, a luminous layer and a polished glaze layer from bottom to top.

[0042] The luminescent layer is composed of a luminescent powder doped with a rare earth activator as a base material, and its particle size is 120 mesh.

[0043] The green body layer includes the following chemical components in terms of raw material weight percentage: 69% SiO 2 , 19% Al 2 o 3 , 2% Fe 2 o 3 , 0.1% TiO 2 , 1% CaO, 0.1% MgO, 5% K 2 O, 1.5% Na 2 O.

[0044] The bottom oil layer comprises the following chemical components in terms of raw material weight percentage: 68% SiO 2 , 20% Al 2 o 3 , 0.3% Fe 2 o 3 , 0.1% TiO 2 , 2% CaO, 1% MgO, 4% K 2 O, 1% Na 2 O, 0.2% ZrO 2 , 0.3% ZnO.

[0045] The glaze layer comprises the following chemical components in terms of raw material weight percentage: 47% SiO 2 , 7% Al 2 o 3 , 0.3% Fe 2 o 3 , 0.05% TiO 2 , 12% CaO, 3% MgO, 3% K 2 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a luminescent ceramic glazed tile, which comprises a green body layer, a ground glaze layer, a fancy glaze layer, a luminous layer and a glaze polishing layer from the bottom up. The luminous layer is composed of luminescent powder with grain fineness of 80-120 meshes. According to the invention, the luminous layer is independently arranged between the fancy glaze layer andthe glaze polishing layer, coarse grain luminescent powder with appropriate granularity is adopted as the raw material, luminescent properties inside the luminescent powder can be ensured after corrosion of the coarse grain luminescent powder surface layer, and the problem that a high temperature flux easily erodes the traditional luminescent powder and destroys the internal structure of luminescent powder, and results in luminescent powder failure can be overcome. The invention also discloses a preparation method of the luminescent ceramic glazed tile, the method has the advantages of simple process and strong controllability, also can perform mild polishing treatment on the surface of the ceramic glazed tile in virtue of the high refractoriness of luminescent powder, makes the coarse grain luminescent powder have the characteristics of anti-skid particles, and endows the luminescent ceramic glazed tile with anti-skid function.

Description

technical field [0001] The invention relates to the field of architectural ceramics, in particular to a functional ceramic. Background technique [0002] With the continuous improvement of living standards, people have higher and higher requirements for architectural ceramics, not only pursuing their practicability, but also paying more and more attention to their decoration and functionality. Luminescent ceramic tiles introduce afterglow luminescent materials into ceramic tiles, so that after absorbing external energy, the ceramic tiles have the characteristics of continuous luminescence under dark conditions. Luminous ceramic tiles can be widely used in stairs, aisles and public places with a lot of traffic, so that they can be used as light sources or guides in case of power failure or emergency. Due to the poor luminescence performance of luminescent materials at high temperature, the current luminescent ceramic tiles are mainly concentrated in low-temperature ceramic t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/14C04B41/89C03C8/00
CPCC03C8/00C04B35/14C04B41/009C04B41/52C04B41/89C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3232C04B2235/3272C04B2235/963C04B2235/9646C04B41/504C04B41/4572C04B41/4545C04B41/5022
Inventor 柯善军倪成林官钰洁
Owner FOSHAN OCEANO CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products