Catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, preparation method and application thereof

A low-temperature catalysis and catalyst technology, applied in the direction of metal/metal oxide/metal hydroxide catalyst, combustion method, physical/chemical process catalyst, etc., can solve the problems of many by-products, limited application, secondary pollution, etc., and achieve Strong resistance to chlorine poisoning, improved catalytic activity, and long life

Active Publication Date: 2022-03-22
EAST CHINA UNIV OF SCI & TECH
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, V 2 o 5 -TiO 2 -V in the base catalyst 2 o 5 It is toxic and easy to cause secondary pollution, which limits its application
Although other types of catalysts such as solid acid catalysts have some applications, they have not been widely promoted due to low activity or many by-products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, preparation method and application thereof
  • Catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, preparation method and application thereof
  • Catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5

[0022] The preparation of embodiment 1~5 nanometer cerium oxide carrier supported tungsten catalyst

[0023] The commercially available ammonium tungstate is formulated into an aqueous solution with a concentration of tungsten element of 60g / L, as shown in Table 1, in Examples 1 to 5, the corresponding volume of ammonium tungstate aqueous solution is respectively impregnated into 1g of nano-cerium oxide carrier (according to comparative example 1 method of preparation). Stir evenly, stand overnight in the air at room temperature, place in a 110°C oven to dry for 12 hours, and then roast. The specific roasting process is: start heating at 50°C, and program the temperature at a rate of 100°C / hour (continuing 4 hours in total). Hours), calcined at 450°C for 2 hours, the obtained powder is the tungsten catalyst supported by nano-cerium oxide carrier.

[0024] By weight, Example 1 has a tungsten oxide loading of 1%, denoted as 1wt% W / CeO 2 ; The tungsten loading of Example 2 is 2...

Embodiment 6

[0027] Example 6: Catalytic combustion of catalysts with different tungsten loadings

[0028] Use the catalyzer of embodiment 1~5 and comparative example 1 to carry out the low-temperature catalytic combustion test of chlorobenzene respectively, all combustion tests are carried out in fixed-bed microreactor (3mm inner diameter quartz), and the consumption of catalyzer is 200mg, and temperature adopts K-type thermoelectric Even automatic control. Chlorobenzene is injected into the vaporization chamber by using 100 series KDS120 micro-injection pump from Stoelting Company of the United States, and then mixed with air into the reactor for combustion. The total flow is controlled by a mass flow meter, the concentration of chlorobenzene is 1000ppm, the amount of waste gas treated per gram of catalyst per hour is 30L, the linear velocity of the gas passing through the reactor is 100m / hour, and the reaction pressure is normal pressure. The relation of the conversion rate of chlorobe...

Embodiment 7

[0030] The chlorobenzene catalytic combustion of embodiment 7 different concentrations

[0031]According to the method of embodiment 6, change chlorobenzene concentration into 500ppm and 2000ppm and carry out combustion test respectively on the catalyst of embodiment 3, all the other reaction conditions are constant, combustion result is as shown in table 2.

[0032] Table 2 Catalyzed Combustion Results of Different Concentrations of Chlorobenzene on the Catalyst of Example 3

[0033]

[0034] It can be seen from Table 2 that when the concentration of chlorobenzene is 500-2000ppm, the catalysts of Example 3 all have relatively high catalytic activity, and can be widely used for catalytic combustion and elimination of chlorinated aromatic hydrocarbons with different concentrations. The catalytic activity increased in the catalytic combustion of chlorobenzene at a lower concentration, and its catalytic activity decreased slightly with the increase of chlorobenzene concentrati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, which is composed of carrier nano-cerium oxide and loaded tungsten, wherein the tungsten exists in the form of tungsten oxide, and the loading capacity of tungsten element is calculated by weight. 1 to 20%. The invention also discloses a preparation method of the catalyst and an application of the catalyst in low-temperature catalytic combustion of chlorinated hydrocarbons. Compared with nano-cerium oxide without tungsten, the catalyst has significantly improved catalytic activity, has excellent catalytic activity for chlorinated aliphatic hydrocarbons and chlorinated aromatic hydrocarbons, and has strong chlorine poisoning resistance and long service life, etc. It can be widely used in the low-temperature catalytic purification of chlorinated hydrocarbons produced in textile, pharmaceutical, leather and wood processing. The preparation method of the catalyst of the invention has simple process and low raw material price.

Description

technical field [0001] The invention belongs to the technical field of catalytic combustion of organic compounds, and in particular relates to a catalyst for low-temperature catalytic combustion of chlorinated hydrocarbons, a preparation method thereof and an application in low-temperature catalytic combustion of chlorinated hydrocarbons. Background technique [0002] Chlorine-containing volatile organic compounds (CVOCs) can not only cause serious harm to human health, but the 12 persistent organic pollutants listed first in the United Nations Environment Program International Treaty are all chlorine-containing organic compounds. Many countries have formulated strict environmental regulations for the emission of CVOCs. Chlorine-containing volatile hydrocarbons are divided into non-aromatic aliphatic hydrocarbon chlorides, such as dichloroethane, trichloroethylene, methyl chloride and polychloromethane, and aromatic hydrocarbon chlorides, such as chlorobenzene and dichlorobe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/30F23G7/07
CPCF23G7/07B01J23/002B01J23/30
Inventor 谷宇峯王幸宜戴启广
Owner EAST CHINA UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap