TiO2-Pd-PPy compound photocatalyst and preparation method and application thereof

A technology of tio2-pd-ppy and compound light, which is applied in the direction of catalyst activation/preparation, organic compound/hydride/coordination complex catalyst, physical/chemical process catalyst, etc., can solve the problem that the precise positioning load of Pd and PPy cannot be realized , poor photocatalytic performance of photocatalyst, complex synthesis conditions and other problems, to achieve high commercial application prospects, simple and fast synthesis method, good photocatalytic activity effect

Active Publication Date: 2017-04-26
SHANDONG UNIV
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, TiO 2 The preparation method of -Pd-PPy composite photocatalyst is time-consuming
In addition to the complex synthesis conditions, the precise positioning of Pd and PPy cannot be achieved, and the photocatalytic performance of the prepared photocatalyst is also poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TiO2-Pd-PPy compound photocatalyst and preparation method and application thereof
  • TiO2-Pd-PPy compound photocatalyst and preparation method and application thereof
  • TiO2-Pd-PPy compound photocatalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Weigh TiO 2 Add 300 mg of (P25) into 100 mL of deionized water, and sonicate for 5 minutes to form a uniform suspension. Under constant stirring conditions, the TiO 2 Add 250 μL palladium chloride (PdCl 2 , 0.0564mol / L) and 1.2×10 -2 -3.0×10 -2 mg pyrrole (Py) monomer. Among them, relative to TiO 2 , the mass fractions of Pd and PPy are 0.5wt% and 0.2wt%, 0.4wt%, 0.6wt%, 0.8wt%, 1.0wt%. Then, high-purity nitrogen gas was passed thereinto for 30 minutes to remove dissolved oxygen therein. Finally, use a 300W xenon lamp to irradiate with full light for 30 minutes, filter the obtained sample, wash it several times with deionized water and absolute ethanol, and dry it in an air atmosphere at 60°C for 12 hours to obtain TiO 2 -Pd-PPy composite photocatalyst.

[0041] Replace the pyrrole monomer with methanol, adjust the pH of the reaction solution to 3.0 with 1.0mol / L sodium hydroxide, and follow the same steps as above to obtain the comparative sample TiO 2 -0.5Pd....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a TiO2-Pd-PPy compound photocatalyst and a preparation method and application thereof. The TiO2-Pd-PPy compound photocatalyst is prepared by the steps: ultrasonically dispersing TiO2 in water, adding PdCl2 and a pyrrole monomer into the water, removing dissolved oxygen, and irradiating with a xenon lamp for photooxidation reduction. A one-step simultaneous photooxidation reduction deposition method adopted in the invention can realize precise positioning and loading of the Pd and PPy. In the compound photocatalyst prepared according to the preparation method, the deposition positions of the Pd and PPy are just the photocatalytic reaction active spots of photo-generated electrons and holes, and can effectively promote separation of photon-generated carriers. The prepared TiO2-Pd-PPy compound photocatalyst shows preferable photocatalysis activity, wherein under full gloss, the hydrogen production efficiency of a TiO2-0.5Pd-0.6PPy photocatalyst through photocatalystic decomposition of water can reach 602mumol / h.

Description

technical field [0001] The invention relates to a novel photocatalytic material, in particular to a TiO 2 -Pd-PPy composite photocatalyst and its preparation method and application. Background technique [0002] As a carbon-free fuel, hydrogen energy is considered an ideal energy source because it can replace fossil fuels to reduce carbon emissions. Since 1972, Fijishima and Honda reported on the n-type semiconductor TiO 2 Photoinduced splitting of water on a single crystal electrode to generate H 2 and O 2 , photocatalytic technology has become one of the effective strategies to directly convert solar energy into hydrogen energy. So far, thousands of photocatalysts have been applied in photocatalytic water splitting for hydrogen production. Among them, titanium dioxide (TiO 2 ) is the earliest and most studied photocatalyst, however, its wide bandgap (-3.2eV) and low quantum efficiency severely limit the practical application of titania. Therefore, it will be of grea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/38B01J37/34B01J37/12B01J37/16C01B3/04
CPCC01B3/042B01J31/38B01J37/12B01J37/16B01J37/344C01B2203/1064B01J35/39Y02E60/36
Inventor 张倩倩李鑫黄柏标王朋王泽岩张晓阳秦晓燕刘媛媛
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com