Experimental method and equipment for detecting wear of vulcanized rubber under high temperature and high humidity conditions

A vulcanized rubber, high temperature and high humidity technology, applied in the direction of testing wear resistance, measuring devices, instruments, etc., can solve the problem of not being able to detect the wear level of vulcanized rubber, and achieve the effect of optimizing the anti-moisture and heat wear performance

Inactive Publication Date: 2016-12-14
BAODING HUAYUE RUBBER BELTS
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides an experimental method and equipment for detecting the wear of vulcanized rubber under high temperature and high humidity conditions, so as to solve the problem in the prior art that the wear level of vulcanized rubber cannot be detected under high temperature and high humidity conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Experimental method and equipment for detecting wear of vulcanized rubber under high temperature and high humidity conditions
  • Experimental method and equipment for detecting wear of vulcanized rubber under high temperature and high humidity conditions
  • Experimental method and equipment for detecting wear of vulcanized rubber under high temperature and high humidity conditions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] Various exemplary embodiments of the present invention will now be described in detail with reference to the accompanying drawings. It should be noted that the relative arrangements of components and steps, numerical expressions and numerical values ​​set forth in these embodiments do not limit the scope of the present invention unless specifically stated otherwise.

[0038] At the same time, it should be understood that, for the convenience of description, the sizes of the various parts shown in the drawings are not drawn according to the actual proportional relationship.

[0039] The following description of at least one exemplary embodiment is merely illustrative in nature and in no way taken as limiting the invention, its application or uses.

[0040] Techniques, methods and devices known to those of ordinary skill in the relevant art may not be discussed in detail, but where appropriate, such techniques, methods and devices should be considered part of the descript...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention discloses an experimental method and equipment for detecting wear of vulcanized rubber under high temperature and high humidity conditions, the experimental method is as follows: putting a vulcanized rubber sample in the testing equipment, setting work parameters of the testing equipment; setting the experimental high temperature and high humidity environment conditions, and starting the equipment; reaching set experimental time, turning off the testing equipment, weighing residual mass of the vulcanized rubber sample, and calculating the wear quantity in unit time of the vulcanized rubber under the high temperature and high humidity environment conditions. The experimental method and equipment solve the problem that the wear level of the vulcanized rubber under the high temperature and high humidity conditions cannot be detected, according to product requirements, the high temperature and high humidity environment conditions can be set for vulcanized rubber samples for wear experiments, and the wear value is more closer to control standards of approved products; and according to the experimental results and the laws of the parameters, anti-humid anti-heat wear resistance of heat resistant rubber can be optimized to a larger degree.

Description

technical field [0001] The invention relates to the technical field of wear machines, in particular to an experimental method and equipment for detecting the wear of vulcanized rubber under high temperature and high humidity conditions. Background technique [0002] The wet heat abrasion tester is specially designed for testing the wear level of vulcanized rubber under the conditions of high temperature water and water vapor. Currently, the abrasion machines commonly used in the rubber industry in the world are Akron abrasion machines and roller abrasion machines. Abrasion test in dry air at normal temperature cannot be carried out on rubber with water or high temperature steam. As a result, although the wear amount of rubber in the general test has reached the index requirements, due to the change of the actual use environment conditions, the test results are greatly different from the actual use effect, which cannot truly reflect the use conditions and meet the service lif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N3/56G01N3/02
CPCG01N3/56G01N3/02G01N2203/0226G01N2203/0236
Inventor 李昭钦
Owner BAODING HUAYUE RUBBER BELTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap