Oil-resistant, cold-resistant double-density shoe rubber outsole and preparation method thereof

A double-density, rubber technology, applied in shoe rubber and its preparation, cold-resistant double-density shoe rubber outsole and its preparation, and oil-resistant fields, can solve the problems of poor processing technology and high content of nitrile rubber, and achieve easy control of the process , good cold resistance and long scorch safety period

Active Publication Date: 2018-04-06
JIHUA 3514 LEATHER & FOOTWARE
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this application, the content of nitrile rubber is too high, and the processing technology is poor. The main direction of protection is oil resistance and antistatic, not oil and cold resistance. For non-antistatic rubber materials, it is absolutely unnecessary to use carbon black with good conductivity, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-resistant, cold-resistant double-density shoe rubber outsole and preparation method thereof
  • Oil-resistant, cold-resistant double-density shoe rubber outsole and preparation method thereof
  • Oil-resistant, cold-resistant double-density shoe rubber outsole and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] Example 1 An oil-resistant and cold-resistant double-density shoe rubber outsole and its preparation method

[0070] This embodiment provides an oil-resistant and cold-resistant double-density rubber outsole for shoes and boots and its preparation method. The specific preparation process is carried out in sequence as follows:

[0071] (11) Rubber mastication

[0072] Put 31kg of natural rubber (model SCR-10) into an open mill or an internal mixer for masticating, and after the plasticity reaches 0.45-0.50, natural rubber A1 with satisfactory plasticity is obtained;

[0073] (12) Compounding and refining

[0074] Put 27kg of butadiene rubber (model BR9000) and 43 kg of nitrile rubber (model JSR N240S) into the open mixer or internal mixer together with A1 and knead until the rubber cross-section is uniform , after being flat and smooth, C1 is obtained;

[0075] (13) Compound mixing

[0076] C1 and middle material [4kg zinc oxide, 2kg stearic acid, anti-aging agent (0...

Embodiment 2-5

[0083] Example 2-5 Oil-resistant, cold-resistant double-density shoe rubber outsole and preparation method thereof

[0084] This example is an oil-resistant and cold-resistant double-density rubber outsole for shoes and boots. Its preparation method is similar to that of Example 1, except that the ingredients of the product and the process parameters in the preparation process are different. See the table below for details.

[0085] Table 1 Formula and process parameters of oil-resistant and cold-resistant double-density rubber outsole for shoes and boots

[0086]

[0087] Explanation: The engine oil in Example 2-5 is added in two times, and the timing of addition is referred to in Example 1. The weight ratio of the two times is 2:1, that is, 2 / 3 of the total amount is added for the first time, and the rest is added for the second time. quantity.

[0088] The preparation method of the above embodiment is simple, the process is easy to control, and the processing performanc...

Embodiment 6-9

[0089] Example 6-9 Oil-resistant and cold-resistant double-density shoe rubber outsole and its preparation method

[0090] This embodiment is respectively a kind of oil-resistant, cold-resistant double-density rubber outsole for shoes and boots, and its ingredient composition is shown in Table 2.

[0091] Table 2 The formula and process parameters of oil-resistant and cold-resistant double-density rubber outsole for shoes and boots

[0092]

[0093] The preparation method of the oil-resistant and cold-resistant double-density shoe rubber outsole provided in Examples 6-9 is carried out in sequence according to the following steps:

[0094] (I) Rubber mastication

[0095] Put the natural rubber into an open mill or an internal mixer for masticating, and after the plasticity reaches 0.45-0.50, natural rubber a with satisfactory plasticity is obtained;

[0096] (Ⅱ) Compound mixing

[0097] Put the nitrile rubber and butadiene rubber into the open mill or internal mixer toget...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oil-resistant and cold-resistant double-density rubber outsole for shoes and boots. The compatibility of raw materials is reasonable, and natural rubber, butadiene rubber and nitrile rubber are used as main materials, supplemented by other auxiliary agents, and the ingredients are processed in consideration of rubber materials. and physical and chemical properties, the oil resistance and cold resistance of the rubber material are good; The steps of manufacturing and the like are carried out in sequence, the method is simple, the process is easy to control, and the outsole of the prepared shoe has moderate hardness, good durability and cold resistance. The invention is suitable for preparing oil-resistant and cold-resistant rubber outsoles, rubber hoses, sealing rings and other rubber articles for shoes and boots.

Description

technical field [0001] The invention belongs to the field of rubber manufacturing, and relates to shoe rubber and a preparation method thereof, in particular to an oil-resistant and cold-resistant double-density shoe rubber outsole and a preparation method thereof. Background technique [0002] When working or training in cold regions and environments exposed to non-polar solvents, officers and soldiers need to wear cold-resistant and oil-resistant shoes. Due to their special functions, these shoes are very different from ordinary rubber shoes in the preparation process. Big difference. Rubber has cold resistance, which requires the main part of the rubber to have a soft molecular chain, which is not easy to be crystallized and hardened by the low temperature environment. At present, oil-resistant and cold-resistant rubber materials are mainly made of nitrile rubber, supplemented by a certain proportion of other rubber types. Nitrile rubber contains -CN groups and has stron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/02C08L9/00C08L45/02C08L91/00C08K13/02C08K3/22C08K5/09C08K3/04C08K5/18A43B13/04B29C43/58
Inventor 李贝贝焦占磊赵宏伟
Owner JIHUA 3514 LEATHER & FOOTWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com