Anti-corrosion structure of edge plate of oil storage tank and its construction method

A technology of edge plates and storage tanks, which is applied to the anti-corrosion structure of oil depot storage tank edge plates and its construction, can solve the problems of lack of performance characteristics, etc., achieve isolation of external water vapor and other corrosives, good external water vapor and other corrosives, and increase thickness Effect

Active Publication Date: 2018-08-03
CENT PLASTICS TIANJIN
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To sum up, relying on traditional construction methods or using a single anti-corrosion material lacks targeted performance characteristics, it is impossible to achieve effective corrosion control and protection for the tank edge plate area, which is an important and difficult point in anti-corrosion engineering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-corrosion structure of edge plate of oil storage tank and its construction method
  • Anti-corrosion structure of edge plate of oil storage tank and its construction method
  • Anti-corrosion structure of edge plate of oil storage tank and its construction method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] like figure 1 The shown anti-corrosion structure for the edge plate of an oil depot storage tank includes an anti-corrosion primer layer 4, a flexible slope-seeking layer 3 arranged on the outside of the anti-corrosion primer layer 4, and a first slope-seeking layer arranged on the outside of the flexible slope-seeking layer 3. The anti-corrosion oil tape layer 5 and the second anti-corrosion oil tape layer 6 covering the outside of the first anti-corrosion oil tape layer 5, and the anti-corrosion primer layer 4 includes a storage tank for covering at least part of the outer side of the tank wall plate 10 Wall plate anti-corrosion section 4-1, edge plate surface anti-corrosion section 4-2 used to cover the upper surface of edge plate 2, edge plate outer side anti-corrosion section 4-3 used to cover the outer side of edge plate 2, used to cover storage The anti-corrosion section 4-4 on the upper surface of the tank foundation 1 and the anti-corrosion section 4-5 on the o...

Embodiment 2

[0088] like Image 6 As shown, the difference between this embodiment and Embodiment 1 is only that: the outer side of the first anti-corrosion oil tape layer 5 is also coated with an anti-corrosion primer for bonding with the second anti-corrosion oil tape layer 6 to strengthen Layer 13.

[0089]In this embodiment, when the construction temperature is -20°C to 15°C, the anti-corrosion primer reinforcement layer 13 is added in order to enhance the bonding strength of the first anti-corrosion oil tape layer 5 and the second anti-corrosion oil tape layer 6 . The anti-corrosion primer reinforcement layer 13 can effectively improve the bonding strength of the first anti-corrosion oil tape layer 5 and the second anti-corrosion oil tape layer 6 .

[0090] In the present embodiment, the anti-corrosion primer reinforcement layer 13 is made of petrolatum anti-corrosion primer, and the petrolatum anti-corrosion primer adopts the model STAC oil-based petrolatum primer produced by Centra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an oil depot storage tank margin plate anticorrosion structure. The oil depot storage tank margin plate anticorrosion structure includes an anticorrosion priming paint layer, a flexible slope finding layer arranged outside the anticorrosion priming paint layer, a first anticorrosion oil band layer arranged outside the flexible slope finding layer, and a second anticorrosion oil band layer covering the first anticorrosion oil band layer. The anticorrosion structure can effectively isolate corrosives such as water in a large range, has a certain anticorrosion thickness, and then can achieve an effective anticorrosion effect on an oil depot storage tank margin plate. The invention further discloses a construction method for the oil depot storage tank margin plate anticorrosion structure. The construction method includes the following steps: a first step, construction of the anticorrosion priming paint layer; a second step, construction of the flexible slope finding layer; a third step, construction of the first anticorrosion oil band layer; a fourth step, construction of the second anticorrosion oil band layer; and a fifth step, construction of a protection device. The construction method can rapidly and effectively achieve construction work of the oil depot storage tank margin plate anticorrosion structure.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion of storage tanks in oil depots, and in particular relates to an anti-corrosion structure for edge plates of storage tanks in oil depots and a construction method thereof. Background technique [0002] The storage tank of the oil depot is the most important facility and equipment in the oil depot, and it is also the biggest accident source in the oil depot. Therefore, it has always been listed as the most important safety protection object of the oil depot. Among the combined components of the oil depot storage tank, the tank bottom plate is the most important of all components, because the accident caused by the problem of the oil tank bottom plate is the most destructive. At the edge plate of the tank bottom plate, there are substrate surfaces composed of metal substrates, welds, building materials and other materials, which are easily corroded. Temporary measures can be taken to repair a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B65D90/06
CPCB65D90/06
Inventor 王彦民李玲杰赵常英任晓伟赵建恒姜佩东蒋文誉郭燕诚谭兴刘亮韩书宁郭浩
Owner CENT PLASTICS TIANJIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap