A kind of sportswear fabric and preparation method thereof
A technology for sportswear and fabrics, applied in the field of textile fibers, can solve problems such as unfavorable moisture absorption and perspiration, achieve good UV resistance, save costs, and ensure the effect of finishing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] A preparation method for sportswear fabric, comprising the following steps:
[0040] A. Put the Coolplus fiber into 48°C water after simple cleaning and drying, add sodium hydroxide and dispersant to adjust the pH value of the solution to 9-10, and make an alkaline solution;
[0041] B. Add pearl powder with a particle size of 10-30 microns in the alkaline solution, and then perform ultrasonic treatment on the solution, the treatment condition is 40kHz, and the time is 20min, and then add nano-scale anion finishing agent and nano-scale antibacterial finishing agent In the neutral solution, while stirring, the temperature was raised to 95°C at a rate of 5°C / min, and kept for 12 minutes;
[0042]C. Put the treated Coolplus fiber into the washing machine, clean it and dry it;
[0043] D. Send the raw materials into the cotton blender, and mix the superfine polyester fiber, special-shaped polyester fiber and Coolplus fiber;
[0044] E. Send the mixed superfine polyester f...
Embodiment 2
[0060] A preparation method for sportswear fabric, comprising the following steps:
[0061] A. Put the Coolplus fiber into 45°C water after simple cleaning and drying, add sodium hydroxide and dispersant to adjust the pH value of the solution to 9-10, and make an alkaline solution;
[0062] B. Add pearl powder with a particle size of 10-30 microns in the alkaline solution, and then ultrasonically treat the solution. The treatment condition is 30kHz, and the time is 15min. Then add nano-scale negative ion finishing agent and nano-scale antibacterial finishing agent to alkali In the neutral solution, while stirring, the temperature was raised to 100°C at a rate of 3°C / min, and kept for 15 minutes;
[0063] C. Put the treated Coolplus fiber into the washing machine, clean it and dry it;
[0064] D. Send the raw materials into the cotton blender, and mix the superfine polyester fiber, special-shaped polyester fiber and Coolplus fiber;
[0065] E. Send the mixed superfine polyest...
Embodiment 3
[0081] A preparation method for sportswear fabric, comprising the following steps:
[0082] A. Put the Coolplus fiber into 45°C water after simple cleaning and drying, add sodium hydroxide and dispersant to adjust the pH value of the solution to 9-10, and make an alkaline solution;
[0083] B. Add pearl powder with a particle size of 10-30 microns in the alkaline solution, and then ultrasonically treat the solution. The treatment condition is 50kHz, and the time is 15min. Then add nano-scale negative ion finishing agent and nano-scale antibacterial finishing agent to alkali In the neutral solution, while stirring, the temperature was raised to 98°C at a rate of 10°C / min, and kept for 10 minutes;
[0084] C. Put the treated Coolplus fiber into the washing machine, clean it and dry it;
[0085] D. Send the raw materials into the cotton blender, and mix the superfine polyester fiber, special-shaped polyester fiber and Coolplus fiber;
[0086] E. Send the mixed superfine polyest...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com