Water purifying material prepared from waste straw and preparation method thereof

A waste straw and water purification technology, applied in chemical instruments and methods, water pollutants, and other chemical processes, can solve the problems of few reports in the field of water treatment, and achieve the effect of simple preparation process

Inactive Publication Date: 2016-07-06
SUZHOU SHENGPULA NEW MATERIAL SCI & TECH
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the research is on the use of biomass degradation for p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] S1: Put 50 parts of waste straw into a pulverizer and pulverize it to a size of 2mm×2mm, then add 5 parts of cellulase to it, and react at a temperature of 25°C for 5h;

[0019] S2: Add 18 parts of linalool and 10 parts of dimethyl sulfide to the reactant in step S1, and stir at a rate of 350 r / min for 20 min at room temperature to obtain a mixed solution A;

[0020] S3: Add 6 parts of selenium dioxide, 10 parts of fine silicic acid, 3 parts of zinc ferrite and 13 parts of ferric ammonium citrate into the mixed solution A described in step S2, and react at a temperature of 60° C. for 10 minutes;

[0021] S4: Add 1 part of acetylferrocene and 15 parts of glycerol phosphate to step S3, pressurize and react at a temperature of 50°C for 15 minutes; then press, dry, and shape to obtain the water purification using waste straw Material.

Embodiment 2

[0028] S1: Put 80 parts of waste straw into a pulverizer and pulverize it to a size of 2mm×2mm, then add 10 parts of cellulase to it, and react at a temperature of 50°C for 8h;

[0029] S2: Add 25 parts of linalool and 15 parts of dimethyl sulfide to the reactant in step S1, and stir at a rate of 450 r / min for 30 min at room temperature to obtain a mixed solution A;

[0030] S3: Add 12 parts of selenium dioxide, 20 parts of fine silicic acid, 9 parts of zinc ferrite and 18 parts of ferric ammonium citrate into the mixed solution A described in step S2, and react at a temperature of 80° C. for 16 minutes;

[0031] S4: Add 6 parts of acetylferrocene and 25 parts of glycerol phosphate to step S3, pressurize and react at a temperature of 80°C for 20 minutes; then press, dry and shape to obtain the water purification using waste straw Material.

Embodiment 3

[0038] S1: Put 60 parts of waste straw into a grinder and pulverize it to a size of 2mm×2mm, then add 6 parts of cellulase to it, and react at a temperature of 30°C for 6h;

[0039] S2: Add 20 parts of linalool and 12 parts of dimethyl sulfide to the reactant in step S1, and stir at a rate of 400 r / min for 25 minutes at room temperature to obtain a mixed solution A;

[0040] S3: Add 8 parts of selenium dioxide, 15 parts of fine silicic acid, 5 parts of zinc ferrite and 14 parts of ferric ammonium citrate into the mixed solution A described in step S2, and react at a temperature of 70° C. for 12 minutes;

[0041] S4: Add 2 parts of acetyl ferrocene and 18 parts of glycerol phosphate to step S3, pressurize and react at a temperature of 60°C for 15 minutes; then press, dry, and shape to obtain the water purification using waste straw Material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water purifying material prepared from waste straw.The water purifying material is prepared from, by weight, 50-80 parts of waste straw, 5-10 parts of cellulose, 6-12 parts of selenium dioxide, 10-20 parts of superfine silicic acid, 3-9 parts of zinc ferrite, 10-15 parts of dimethyl sulfide, 13-18 parts of ammonium ferric citrate, 1-6 parts of acetylferrocene, 15-25 parts of glycerophosphate and 18-25 parts of linalool.By using the purifying material, metal impurities in water can be effectively degraded and removed, and an effective way is provided for recycling waste straw.

Description

technical field [0001] The invention belongs to the field of water treatment materials, and in particular relates to a water purification material utilizing waste straw and a preparation method thereof. Background technique [0002] my country is a large agricultural country, so there are a lot of crop straws produced every year, but the utilization rate of straws is seriously insufficient. At present, the common practice for straw is still simple and rude in-situ burning. The incineration of straw not only causes serious environmental pollution and fire hazards, but also a large waste of resources. As the country advocates five-in-one, sustainable development of circular economy and ecological economy, how to make better use of straw resources and turn waste into treasure has become a research hotspot. At present, most of the research is on the use of biomass degradation for power generation, but there are few reports on the field of water treatment. Contents of the inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/24B01J20/30C02F1/28C02F101/20C02F101/22
CPCB01J20/24B01J20/0244B01J20/0251B01J20/0262B01J20/22B01J2220/46B01J2220/4825C02F1/286C02F2101/20C02F2101/22
Inventor 费金华
Owner SUZHOU SHENGPULA NEW MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com