Enhanced power information cable conduit and preparation method thereof

An electric power information and enhanced technology, applied in the field of plastic pipes, can solve the problems of tensile strength, toughness reduction, poor impact resistance of plastic pipes, etc., and achieve the effect of enhancing mechanical properties

Inactive Publication Date: 2017-05-31
四川鑫森管业有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The UPVC pipes in the prior art are tested according to the GB / T5836.1-92 standard for drop hammer impact test. After years of testing, it is found that the one-pass rate is only less than 50%, and many products even break after 10 impacts. Therefore, the resistance of plastic pipes Poor impact
Doing so can indeed increase the softening temperature, but it will greatly reduce other properties of the pipe, especially the impact resistance, tensile strength and toughness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced power information cable conduit and preparation method thereof
  • Enhanced power information cable conduit and preparation method thereof
  • Enhanced power information cable conduit and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Preparation of premix: 100 parts of CPVC, 1 part of 330ACR, 2 parts of 334ACR, 5 parts of calcium carbonate, 1 part of calcium / zinc composite stabilizer, 0.1 part of β-diketone, 0.1 part of hydrotalcite, 0.5 part of silicon micropowder , 1 part of polyethylene wax, 0.21 part of orange red, and 0.18 part of macromolecular yellow are measured and put into a planetary mixer with a temperature of 70 ° C and a rotation speed of 105 rpm, and the premix is ​​fully stirred for 8 minutes; (2) CPVC pipe Preparation of special material: Put the premixed material prepared in step (1) into the hopper of a twin-screw extruder with a temperature of 120°C and a screw speed of 110 rpm, and melt extrusion and air-cooled grinding to pelletize the prepared Special material for CPVC pipe;

[0044] (3) Forming preparation of CPVC pipe material: send the special material for CPVC pipe material prepared in step (2) into the hopper of a single-screw extruder with a temperature of 120°C and ...

Embodiment 2

[0046] (1) Preparation of premix: 100 parts of CPVC, 1 part of PVC, 2 parts of 330ACR, 2 parts of 323B ACR, 1 part of butadiene modified ACR, 10 parts of calcium carbonate, 3 parts of calcium / zinc composite stabilizer, β-di 0.2 parts of ketone, 0.2 parts of hydrotalcite, 1 part of silicon micropowder, 1.5 parts of stearic acid, 0.06 parts of phthalocyanine green, 0.05 parts of macromolecular yellow, and 0.08 parts of titanium dioxide are measured and put into the planet with a temperature of 70 ° C and a rotation speed of 110 rpm In the mixer, the premix was fully stirred for 8.5 minutes;

[0047] (2) Preparation of special materials for CPVC pipes: Put the premix prepared in step (1) into the hopper of a twin-screw extruder with a temperature of 130°C and a screw speed of 110rpm, and melt and extrude and air-cool the surface Pelletizing to produce special materials for CPVC pipes;

[0048] (3) Forming preparation of CPVC pipe material: send the special material for CPVC pipe...

Embodiment 3

[0050] (1) Preparation of premix: 100 parts of CPVC, 10 parts of PVC, 2 parts of 330ACR, 3 parts of 323B ACR, 15 parts of calcium carbonate, 4 parts of calcium / zinc composite stabilizer, 0.3 part of β-diketone, 0.3 part of hydrotalcite , 2 parts of silicon micropowder, 1.0 part of PE wax, 0.04 part of phthalocyanine blue, and 0.12 part of titanium dioxide were measured and put into a planetary mixer with a temperature of 70 ° C and a rotation speed of 115 rpm, and were fully stirred for 9 minutes to prepare a premix;

[0051] (2) Preparation of special material for CPVC pipes: Put the premixed material prepared in step (1) into the hopper of a twin-screw extruder with a temperature of 140°C and a screw speed of 110rpm, melt extrusion and air-cooled grinding Pelletizing to produce special materials for CPVC pipes;

[0052] (3) Molding preparation of CPVC pipe material: send the special material for PVC pipe material prepared in step (2) into the hopper of a single-screw extrude...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
tensile yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enhanced power information cable conduit and a preparation method thereof. The components of cable conduit materials mainly include CPVC, PVC, ACR, calcium carbonate, calcium / zinc composite stabilizer, β-diketone, hydrotalcite, silicone spherical micropowder and processing aids. Its preparation method: put each component into a planetary mixer, and make a premix after thorough stirring; send the prepared premix into a twin-screw extruder, melt extrusion and air-cooled grinding surface cutting The special material for CPVC pipes is obtained; the special material for CPVC pipes is fed into a single-screw extruder to extrude a tube blank in a molten state, and the tube blank is formed, cooled, drawn, cut and stacked to obtain enhanced power information Cable conduit. The invention utilizes the dispersion strengthening technology, and the rigid particle organosilicon spherical micropowder is used as the second phase, and the fine dispersed particles are evenly distributed in the CPVC phase to produce a strengthening effect and improve the comprehensive performance of the pipe.

Description

technical field [0001] The invention relates to the technical field of plastic pipes, in particular to a cable guide for laying wires and cables and a preparation method thereof. Background technique [0002] With the rapid development of electric power industry and information industry, power information cables have been widely promoted in urban construction and renovation, making cable laying and threading conduits more and more widely used. There are many types of cable laying conduits, such as traditional plastic pipes, cast iron pipes, galvanized steel pipes, cement pipes, etc. Plastic cable laying conduit, because of its advantages of energy saving, ecological protection, and convenient construction, has a wide range of applications and has become the main force of the urban construction pipe network in the new century. In particular, the widespread use of new environmentally friendly plastic pipes has set off a revolution to replace traditional pipes. [0003] Plasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/24C08L27/06C08L33/04C08L83/04C08L23/06C08K13/02C08K5/07C08K3/26B29C47/92B29B9/06B29C48/92
CPCC08L27/24B29B9/06B29C48/92C08L2203/18C08L2203/20C08L2201/08C08L2205/025C08L2205/035C08L2205/02B29C49/78C08L33/04C08L83/04C08L23/06C08K13/02C08K2003/265C08K5/07C08K3/26C08L27/06
Inventor 侯世荣董定旭谢佳董静萍
Owner 四川鑫森管业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap