A kind of flame retardant rubber composition and its application

A flame-retardant rubber and composition technology, applied in the field of rubber preparation, can solve problems such as tire fire, life and property safety hazards, and human harm, and achieve the effects of reducing the percentage content, improving flame-retardant performance, and improving flame-retardant performance

Active Publication Date: 2017-07-21
GUANGZHOU FENGLI RUBBER TIRE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Pneumatic rubber tires are generally composed of rubber and skeleton materials, but rubber is a material that is extremely flammable in the air. For vehicles that have been operating at high temperatures and close to fire sources for a long time, tires are prone to fire. Phenomena, leaving great hidden dangers to life and property safety
The traditional solution is to use the high-efficiency flame retardant decabromodiphenyl ether in the formula as a flame retardant in the tire formula, but because the EU believes that decabromodiphenyl ether is harmful to the human body, it prohibits the use of decabromodiphenyl ether in tires, As a result, the tire industry has gradually banned the use of decabromodiphenyl ether in tire formulations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of flame retardant rubber composition and its application
  • A kind of flame retardant rubber composition and its application
  • A kind of flame retardant rubber composition and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] By weight: 40kg of natural rubber, 60kg of butadiene rubber, 50kg of carbon black, 3kg of zinc oxide, 2kg of stearic acid, 1kg of p-phenylenediamine antioxidant, 1kg of quinoline antioxidant, 1kg of paraffin wax, sulfenamide accelerator 1kg, sulfur 1kg, decabromodiphenylethane 30kg, antimony trioxide 10kg, red phosphorus 3kg.

[0047] The above-mentioned composition material is processed by a 3-stage mixing process, and the 3-stage mixing is carried out in an F370 type internal mixer, and the rotor speed is 10-60r / min; after the 3-stage mixing, the tablet is discharged from the mill; : Add 40kg of natural rubber, 60kg of butadiene rubber, 50kg of carbon black, 3kg of zinc oxide, 2kg of stearic acid, 1kg of p-phenylenediamine antioxidant, 1kg of quinoline antioxidant, 1kg of paraffin, 30kg of decabromodiphenylethane in one stage , antimony trioxide 10kg, red phosphorus 3kg, debinding temperature 165°C; the second stage is the rubber compound re-milling process; the third...

Embodiment 2

[0050] By weight: natural rubber 45kg, butadiene rubber 55kg, high wear-resistant carbon black 55kg, zinc oxide 5kg, stearic acid 4kg, p-phenylenediamine antioxidant 3kg, quinoline antioxidant 2kg, paraffin 3kg, decabromodi 25kg of phenylethane, 8kg of antimony trioxide, and 5kg of red phosphorus.

[0051]The above-mentioned composition material is processed by a 3-stage mixing process, and the 3-stage mixing is carried out in an F370 type internal mixer, and the rotor speed is 10-60r / min; after the 3-stage mixing, the tablet is discharged from the mill; : Add 40kg of natural rubber, 60kg of butadiene rubber, 50kg of carbon black, 3kg of zinc oxide, 2kg of stearic acid, 1kg of p-phenylenediamine antioxidant, 1kg of quinoline antioxidant, 1kg of paraffin, 30kg of decabromodiphenylethane in one stage , 10kg of antimony trioxide, 3kg of red phosphorus, debinding temperature 165°C; the second stage is the process of mixing rubber; the third stage adds 2kg of sulfur and 2kg of sulf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
crystallization temperatureaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame retardant rubber composition and application thereof. The flame retardant rubber composition does not contain decabromodiphenyl ether, is superior in flame retardancy, and is prepared from natural rubber, 2,2',3,3',4,4',5,5',6,6'-decabromobibenzyl, antimonous oxide, red phosphorus and an assistant. Through the synergistic effect of 2,2',3,3',4,4',5,5',6,6'-decabromobibenzyl, antimonous oxide and red phosphorus, the flame retardancy of a tire sizing material in a formula is greatly improved, so that the prepared rubber does not burn easily and self-extinguishes in case of open fire; the invention further provides the application of the flame retardant rubber composition in the field of tire preparation.

Description

technical field [0001] The invention relates to the field of rubber preparation, in particular to a flame-retardant rubber composition and its application. Background technique [0002] The development of the automotive industry has benefited from substantial advances in the technology of the individual components themselves. As an important part of automobiles, tires have a direct impact on the progress of the automobile industry. [0003] Tires are often used under complex and harsh conditions, and they are subjected to various deformations, loads, forces, and high and low temperature effects during driving, so they must have high load-bearing performance, traction performance, and cushioning performance. [0004] Half of the world's rubber consumption is used for tire production, which shows the ability of tires to consume rubber. However, rubber is flammable. In the complex environment of tires, the flame retardancy of rubber is particularly important. [0005] Pneuma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/00C08K13/02C08K3/04C08K3/22C08K5/09C08K5/18C08K3/02C08K5/03B60C1/00
CPCB60C1/00C08L7/00C08L9/00C08L2201/02C08L2205/03C08L91/06C08K13/02C08K3/04C08K2003/2296C08K5/09C08K5/18C08K2003/026C08K5/03C08K3/2279
Inventor 李键
Owner GUANGZHOU FENGLI RUBBER TIRE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More