Water-based high-solid antistatic coating and preparation method thereof

A high-solids, antistatic technology, applied in the field of coating science, can solve the problems of affecting the conductivity and physical properties of the coating, not easy to generate a homogeneous system, and insufficient fullness of the paint film, and achieve good hand and fullness. Antistatic properties, durable color and yellowing effect

Inactive Publication Date: 2016-08-17
广州益景春环保材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, more antistatic fillers such as conductive carbon black, graphite, metal and metal oxide powders are quite different from polymer structures, and poor dispersion makes it difficult to form a homogeneous system, which affects conductivity and coatings. physical properties
[0005] Due to the low solid content of ordinary water-based coatings, the fullness of the paint film is not enough, resulting in poor visual effects of furniture and other finished products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based high-solid antistatic coating and preparation method thereof
  • Water-based high-solid antistatic coating and preparation method thereof
  • Water-based high-solid antistatic coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1 water-based high solid antistatic coating

[0029] In this embodiment, a water-based high-solid antistatic coating comprises the raw material components in the following mass percentages as shown in Table 1:

[0030] The water-based high solid content antistatic coating material of table 1 embodiment 1

[0031]

[0032]

[0033]

[0034] The specific preparation steps of the water-based high-solid antistatic coating of the present embodiment are as follows:

[0035] First, add hydroxyl polyurethane resin and functional additives into the reactor at room temperature and stir for 15 minutes to fully emulsify, then add functional powder and conductive fillers to the reactor in sequence, stir at 1500rpm, and disperse at high speed to obtain a uniformly dispersed emulsion. The film-forming aid, pH regulator and water are added to the reactor to adjust the pH and viscosity of the system, and the water-based high-solid antistatic coating is obtained afte...

Embodiment 2

[0036] Embodiment 2 water-based high solid antistatic coating

[0037] This embodiment is a kind of water-based high-solid antistatic coating, and the raw material components comprising the following mass percentages are shown in Table 2:

[0038] The water-based high solid content antistatic coating raw material of table 2 embodiment 2

[0039]

[0040]

[0041] The specific preparation method of the water-based high-solid antistatic coating of this embodiment is the same as that of Embodiment 1.

Embodiment 3

[0042] Embodiment 3 water-based high solid antistatic coating

[0043] The present embodiment is a kind of water-based high-solid antistatic coating, and the raw material components comprising the following mass percentages are shown in Table 3:

[0044] The water-based high solid content antistatic coating material of table 3 embodiment 3

[0045]

[0046]

[0047]

[0048] The specific preparation method of the water-based high-solid antistatic coating of this embodiment is the same as that of Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based high-solid antistatic coating and a preparation method thereof. The coating comprises the following raw materials: hydroxyl polyurethane resin, conductive filler, functional powder, a functional additive, a coalescing agent, a pH modifier and the balance of water; the functional powder comprises carboxyl polyester resin with the acid value greater than 100, carboxyl polyester resin with the acid value of 25 to 100, and carboxyl polyester resin with the acid value smaller than 25, wherein the weight ratio of the three kinds of carboxyl polyester resin is (1-2):(1-2):(1-2). The water-based high-solid antistatic coating is characterized in that hydroxyl polyurethane water-base resin, water-based conductive filler and carboxyl polyester resin powder different in acid value gradient are compounded into a whole through cross-linking reaction, so that a compact film can be formed. The film formed by the coating has high solid content and good antistatic performance, has good chemical resistance, water resistance and excellent physical properties at the same time, and can be applied to the field of packaging and electromagnetic shielding of electronic products, furniture and the like.

Description

technical field [0001] The invention belongs to the field of paint science and technology, in particular to a water-based high-solid antistatic paint and a preparation method thereof. Background technique [0002] In recent years, a large number of electronic products have been damaged by static electricity every year, and the loss has reached more than 10 billion US dollars. As far as furniture is concerned, especially in the dry autumn and winter seasons, static electric shocks are prone to numbness, and furniture is also easily stained and dirty due to electrostatic adsorption. [0003] Oil-based paint products contain a large amount of benzene, toluene, xylene and their derivatives, which have high VOC emissions and directly endanger human health. Heavy pollution and serious damage to the environment. Oil-based paint is a highly flammable item, and there are great safety hazards in the process of storage and transportation. With the promulgation of relevant laws and r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/24C09D5/10C09D7/12
CPCC08K2201/001C08L2201/04C08L2205/025C08L2205/035C09D5/106C09D5/24C09D7/61C09D7/70C09D175/04C08L67/00C08K13/02C08K3/04C08K2003/0893C08K2003/085
Inventor 刘勇邓建华
Owner 广州益景春环保材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products