Railway locomotive wheel rail solid lubricating block

A technology of solid lubrication and railway locomotives, applied in the field of wheel and rail lubricants, can solve the problems of non-compliance with environmental protection and energy saving, technological innovation, easy damage of grease and oil, blockage, insufficient lubrication of locomotive wheel rims, etc., and achieve easy promotion and mass production , extended service life, light weight effect

Active Publication Date: 2017-03-29
CHENGDU SHUZHONG RAILWAY TECH INVESTMENT CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the continuous development of special industries such as aerospace and military industry, people put forward higher requirements for the performance of lubricating materials, while traditional liquid lubricants require special supporting equipment, which have high cost and large consumption, and do not meet the requirements of environmental protection, energy saving, technical Innovation, the damage and blockage of the grease and oil Louis lead to insufficient lubrication of the locomotive wheel rim and different degrees of wear, which are difficult to meet the requirements. In order to obtain extreme work such as ultra-high temperature, ultra-low temperature, high pressure, high vacuum, high load and strong radiation Lubricating materials that can still function normally in the environment, solid lubricants have gradually become the first choice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Railway locomotive wheel rail solid lubricating block
  • Railway locomotive wheel rail solid lubricating block

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing a railway locomotive wheel and rail solid lubricating block, comprising the following steps:

[0029] S1: Install the mold and preheat to 90°C;

[0030] S2: Weigh the raw materials according to the following parts by weight: 18 parts of epoxy resin, 30 parts of molybdenum disulfide, 18 parts of halogen-free flame retardant, 5 parts of magnesium oxide, 15 parts of graphite, 7 parts of aluminum oxide, 7 parts of glass fiber, and The above-mentioned raw materials that weigh are placed in internal mixer and mix;

[0031] S3: Fill the mixed raw materials into the preheated mold to ensure that the raw materials fill the mold cavity;

[0032] S4: Carry out conventional molding operation. The molding operation parameters are: temperature 150°C, pressure 8MPa, time 5min. Exhaust gas twice during the molding operation, each exhaust time is 20s, and the exhaust interval time is 1min. The molding operation is completed Finally, keep it under molding tempera...

Embodiment 2

[0035] A method for preparing a railway locomotive wheel and rail solid lubricating block, comprising the following steps:

[0036] S1: Install the mold and preheat to 80°C;

[0037] S2: Weigh the raw materials according to the following proportions by weight: 15 parts of epoxy resin, 26 parts of molybdenum disulfide, 15 parts of halogen-free flame retardant, 3 parts of magnesium oxide, 12 parts of graphite, 5 parts of aluminum oxide, 5 parts of glass fiber, and The above-mentioned raw materials that weigh are placed in internal mixer and mix;

[0038] S3: Fill the mixed raw materials into the preheated mold to ensure that the raw materials fill the mold cavity;

[0039] S4: Carry out conventional molding operation. The molding operation parameters are: temperature 150°C, pressure 8MPa, time 5min. Exhaust gas twice during the molding operation, each exhaust time is 20s, and the exhaust interval time is 1min. The molding operation is completed Finally, keep it under molding t...

Embodiment 3

[0042] A method for preparing a railway locomotive wheel and rail solid lubricating block, comprising the following steps:

[0043] S1: Install the mold and preheat to 100°C;

[0044] S2: Weigh the raw materials according to the following parts by weight: 21 parts of epoxy resin, 34 parts of molybdenum disulfide, 21 parts of halogen-free flame retardant, 7 parts of magnesium oxide, 18 parts of graphite, 9 parts of aluminum oxide, 9 parts of glass fiber, and The above-mentioned raw materials that weigh are placed in internal mixer and mix;

[0045]S3: Fill the mixed raw materials into the preheated mold to ensure that the raw materials fill the mold cavity;

[0046] S4: Carry out conventional molding operation, the molding operation parameters in step S4 are: temperature 150°C, pressure 8MPa, time 5min, exhaust 3 times during the molding operation, each exhaust time is 20s, and the exhaust interval time is 1min , after the molding operation is completed, keep it under the mol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a railway locomotive wheel rail solid lubricating block and a preparation method thereof. The solid lubricating block comprises a lubricating rod (1), a boss (2) and a groove (3), wherein the boss (2) is arranged at one end of the lubricating rod (1), the groove (3) is formed in the other end of the lubricating rod (1), the four edge corners of the boss (2) are respectively in smooth transition, the side surface of the boss (2) is in chamfering connection with the plane of the lubricating rod (1), the four edge corners of the groove (3) are respectively in smooth transition, the side surface of the groove (3) is in chamfering connection with the plane of the lubricating rod (1), and one side surface of the lubricating rod (1) is provided with waves which are matched with a material delivery belt. The solid lubricating block has the advantages that the surface of the lubricating rod (1) is provided with the waves which are matched with the material delivery belt, and the groove is formed in one end of the lubricating rod, so the installation and replacement are convenient, and the easiness in falling is avoided; the connecting plane of the groove and the lubricating rod and the connecting plane of the boss and the lubricating rod respectively adopt the chamfering connection, and the edge corners of the groove and the boss are respectively in smooth transition, so the installation is convenient, the friction between the lubricating block and equipment is reduced, and the abrasion of equipment is decreased.

Description

technical field [0001] The invention relates to a wheel-rail lubricant, in particular to a railway locomotive wheel-rail solid lubricating block. Background technique [0002] With the large number of internal combustion and electric locomotives on the road and the development of railways in the direction of speed increase and heavy load, the side wear of curved steel rails on my country's busy main railway lines is on the rise, and the problem of wheel and rail wear is becoming more and more prominent; during the "Ninth Five-Year Plan" period of Jinan Railway Bureau A total of 185km of rails with curved wear exceeding the limit were replaced, accounting for 43.5% of the total number of damaged rails replaced. The shortest service life of small-radius curved carbon rails on busy trunk lines is only 10 months, and the total weight of passing through is 70Mt km / km, which is the normal service life of rails. The service life of rare earth rails on the R=600m curve of Jinpu Line i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B61K3/00C10M169/04C10N50/08
CPCB61K3/00C10M169/048C10N2050/08
Inventor 喻泽玖徐正庚史雪蕾罗江
Owner CHENGDU SHUZHONG RAILWAY TECH INVESTMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products