Breathable cloth and manufacturing method thereof
A production method and fabric technology, applied in the field of materials, can solve the problems of affecting air circulation, uncomfortable clothes sticking to the body, physical discomfort, etc., and achieve the effect of simple production method, good ventilation effect and large porosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] A breathable cloth, comprising 50g of cotton, 12g of celery fiber, 15g of air-through non-woven fabric, 25g of silk, 12g of wood fiber and 15g of starch.
[0014] First, soak 50g of cotton and 12g of celery fiber in 5% hypochlorous acid for 2 hours.
[0015] Clean it after taking it out.
[0016] Then add pulverized to 100-mesh air-through non-woven fabric 15g, 25g of length 3mm and 12g of wood fibers of 6mm.
[0017] After mixing it was spun into threads with a diameter of 20 microns.
Embodiment 2
[0019] A breathable fabric, comprising 68g of cotton, 19g of celery fiber, 21g of air-through non-woven fabric, 36g of silk, 16g of wood fiber and 22g of starch.
[0020] First, soak 68g of cotton and 19g of celery fiber in 5% hypochlorous acid for 5 hours.
[0021] Clean it after taking it out.
[0022] Then add and be ground to the wood fiber 16g of 25-36g and 8 millimeters of 130 mesh hot-air non-woven fabrics 15-21g, length 5 millimeters.
[0023] After mixing it was spun into threads with a diameter of 25 microns.
Embodiment 3
[0025] A breathable cloth, comprising 51g of cotton, 13g of celery fiber, 16g of air-through non-woven fabric, 26g of silk, 13g of wood fiber and 16g of starch.
[0026] First, soak 51g of cotton and 13g of celery fiber in 5% hypochlorous acid for 2-5 hours.
[0027] Clean it after taking it out.
[0028] Then add the wood fiber 13g that is crushed to 120 mesh hot-air non-woven fabrics 16g, 26g of length 3-5 millimeters and 7 millimeters.
[0029] After mixing it was spun into threads with a diameter of 2 microns.
PUM
![No PUM](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com