A method for preparing carbon nanotube-modified palladium-loaded electrodes by electrophoresis-pulse deposition

A carbon nanotube, pulse deposition technology, applied in electrodes, electrophoretic plating, electrolytic coatings, etc., can solve the problem of high cost, and achieve the effect of improving efficiency, uniform dispersion and good dispersibility

Active Publication Date: 2016-08-10
BEIJING UNIV OF TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a catalyst, palladium (Pd) greatly improves the degradation rate of chlorinated organic compounds, but as a noble metal, the cost is high, so it is a meaningful research to improve the utilization rate of Pd and prepare efficient catalytic electrodes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing carbon nanotube-modified palladium-loaded electrodes by electrophoresis-pulse deposition
  • A method for preparing carbon nanotube-modified palladium-loaded electrodes by electrophoresis-pulse deposition
  • A method for preparing carbon nanotube-modified palladium-loaded electrodes by electrophoresis-pulse deposition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Put CNTs in mixed acid Ultrasonic at medium temperature for 4 hours, reflux at 60°C for 2 hours, filter and wash until neutral, dry and set aside;

[0027] (2) Dip the titanium (Ti) mesh in 40% NaOH solution at 80°C for 2 hours to remove surface oil stains, wash it with distilled water until neutral, then immerse it in 15% oxalic acid solution to remove surface oxides, at 98°C Keep it for 2 hours, rinse it with distilled water, and dry it with nitrogen for later use;

[0028] (3) prepare the Py solution of 0.04mmol / L, wherein the concentration of SDS is 1mmol / L, H 2 SO 4 The concentration is 0.05mol / L. The Ti mesh treated in step (2) is used as the anode, the Pt sheet is used as the cathode, and the Py solution is used as the plating solution. The current is adjusted to 3mA and the time is 5min. The PPy film is deposited on the surface of the Ti mesh by electrochemical method to obtain a PPy / Ti electrode. figure 1 It can be seen that a layer of PPy film is unif...

Embodiment 2

[0034] (1) Put CNTs in mixed acid Ultrasonic at medium temperature for 4 hours, reflux at 60°C for 2 hours, filter and wash until neutral, dry and set aside;

[0035] (2) Dip the titanium (Ti) mesh in 40% NaOH solution at 80°C for 2 hours to remove surface oil stains, wash it with distilled water until neutral, then immerse it in 15% oxalic acid solution to remove surface oxides, at 98°C Keep it for 2 hours, rinse it with distilled water, and dry it with nitrogen for later use;

[0036] (3) prepare the Py solution of 0.04mmol / L, wherein the concentration of SDS is 1mmol / L, H 2 SO 4 The concentration is 0.05mol / L. The Ti mesh treated in step (2) is used as the anode, the Pt sheet is used as the cathode, and the Py solution is used as the plating solution. The current is adjusted to 3mA and the time is 5min. The PPy film is deposited on the surface of the Ti mesh by electrochemical method to obtain a PPy / Ti electrode. figure 1 It can be seen that a layer of PPy film is unif...

Embodiment 3

[0044] (1) Put CNTs in mixed acid Ultrasonic at medium temperature for 4 hours, reflux at 60°C for 2 hours, filter and wash until neutral, dry and set aside;

[0045] (2) Dip the titanium (Ti) mesh in 40% NaOH solution at 80°C for 2 hours to remove surface oil stains, wash it with distilled water until neutral, then immerse it in 15% oxalic acid solution to remove surface oxides, at 98°C Keep it for 2 hours, rinse it with distilled water, and dry it with nitrogen for later use;

[0046] (3) prepare the Py solution of 0.04mmol / L, wherein the concentration of SDS is 1mmol / L, H 2 SO 4 The concentration is 0.05mol / L. The Ti mesh treated in step (2) is used as the anode, the Pt sheet is used as the cathode, and the Py solution is used as the plating solution. The current is adjusted to 3mA and the time is 5min. The PPy film is deposited on the surface of the Ti mesh by electrochemical method to obtain a PPy / Ti electrode. figure 1 It can be seen that a layer of PPy film is unif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for preparing carbon nanotube-modified palladium-loaded electrodes by electrophoresis-pulse deposition, which belongs to the technical field of electrochemical water treatment, uses polypyrrole as a cocatalyst, and carbon nanotubes as a catalyst carrier to improve the dispersion and utilization of the catalyst. As a catalyst deposition technology, electroplating refines the crystallization of the coating and enhances the catalytic performance of the electrode. The invention uses the titanium net as the matrix, and after polymerizing a layer of polypyrrole film on the surface, adopts an electrophoresis method to modify the oxidized carbon nanotube to the surface of the matrix to form a layer of uniform carbon nanotube carrier film. The palladium catalyst was deposited by pulse electroplating. Compared with the Pdped / Ti electrode prepared under the same conditions and the Pdded / Ti electrode prepared by DC electroplating, the catalytic performance of the Pd / CNTs / PPy / Ti electrode was higher.

Description

technical field [0001] The invention belongs to the technical field of electrochemical water treatment, uses titanium mesh as a substrate, electrophoresis deposits and modifies carbon nanotubes, deposits palladium catalysts by pulse electroplating, and prepares Pd / CNTs / PPy / Ti composite electrodes, which can be used for water phase electrodes of chlorinated organics. Catalytic reduction dechlorination. Background technique [0002] Chlorinated organic compounds belong to the category of typical persistent organic pollutants, which are highly toxic and difficult to degrade. Electrocatalytic hydrodechlorination technology is an economical and effective green technology for degrading chlorinated organic compounds, with mild experimental conditions, low operating costs and few toxic by-products. As a catalyst, palladium (Pd) greatly improves the degradation rate of chlorinated organic compounds, but as a noble metal, the cost is high, so it is a meaningful research to improve th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/04C25B3/04C25D9/02C25D13/02C25D5/18C25D3/50C25B3/25
Inventor 孙治荣杜冉刘丹
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap