Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Seal

一种密封片、胶粘片的技术，应用在压敏薄膜/薄片、薄膜/薄片状的粘合剂、粘合剂类型等方向，能够解决难以完全防止水汽渗入间隙等问题

Active Publication Date: 2018-04-10
NITTO DENKO CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the floor panels are fixed to the main body frame by bolting, it is difficult to completely prevent moisture from penetrating into the gap between the bolts and the screw holes formed for bolting the floor panels even when the bolts are screwed into the screw holes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seal
  • Seal
  • Seal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0214] A thermosetting room temperature liquid resin (manufactured by Kaneka Corporation, trade name "ACX022") composed of terminal allylated polyoxypropylene having an allyl group bonded to both ends of polypropylene glycol having an average molecular weight of about 28000 was used. ", 100 parts by weight) were mixed with a tackifying resin (pentaerythritol rosin, 20 parts by weight), and the mixture was heated to 100° C. and stirred for 30 minutes. It was confirmed that the mixture was transparent and the tackifier resin was dissolved in the thermosetting normal temperature liquid resin. Thereto was added a solution of platinum / 1,3-divinyltetramethyldisiloxane complex in 2-propanol (complex concentration 3%, manufactured by N.E.CHEMCAT Corporation, trade name "3% A curing catalyst (0.05 parts by weight) consisting of Pt-VTS-IPA solution"), a hydrogen siloxane compound having an average of 5 hydrosilyl groups in one molecule (manufactured by Zhongyuan Chemical Co., Ltd., trad...

Embodiment 2

[0219] A sealing sheet was obtained in the same manner as in Example 1 except that a 25 μm thick polyethylene terephthalate film (relaxation rate 21.8%, tensile strength 185 N / 10mm) was used instead of the 20 μm thick polypropylene film .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
coating massaaaaaaaaaa
sizeaaaaaaaaaa
fineness modulusaaaaaaaaaa
Login to View More

Abstract

The present invention provides a sealing sheet mainly composed of an adhesive sheet comprising a core film and adhesive layers formed on both surfaces of the core film, the core film having a thickness of less than A water vapor transmission rate of 7.5 g / 100sq.in and a relaxation rate of not less than 10%, the water vapor transmission rate measured by a method according to JIS Z 0208, and the relaxation rate measured by a bending-stress relaxation rate measurement test have to. The sealing sheet of the present invention has excellent water vapor permeation resistance and excellent level difference absorbency.

Description

technical field [0001] The present invention relates to a sealing sheet having excellent water vapor permeation resistance and excellent level difference absorbency. Background technique [0002] For example, since electronic components, power wiring, etc. are disposed under the floor panels of the aircraft, it is necessary to insulate the floor panels from moisture and moisture so that the moisture does not seep below the floor panels. However, since the floor panel is fixed to the main body frame by bolting, it is difficult to completely prevent moisture from penetrating into the gap between the bolt and the screw hole formed for bolting the floor panel even when the bolt is screwed into the screw hole. To this end, sealing sheets are adhered to the floor panels to seal the floor panels from water and moisture. [0003] In addition, antennas for facilitating communication between the craft and remote parties are provided on the outer surfaces (external panels) of the body...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/24C09J7/30C09J11/00C09J171/00C09J7/38C09J7/22
CPCB32B7/12B32B27/08C09J2423/106C09J2427/006C09J2467/006C09J2471/00B32B7/06B32B27/32B32B27/36B32B2307/3065B32B2307/7244B32B2307/748B32B2605/08B32B2605/10B32B2605/18C09J7/22Y10T428/2848C09J2301/124C09J2301/302C09J2301/312C09J7/38
Inventor 甲谷龙一牟田茂树铃木理利广濑彻哉井口伸儿
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com