Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of sintering method and equipment of optical fiber preform rod

A technology of optical fiber preform and sintering equipment, which is applied in glass manufacturing equipment, manufacturing tools, etc., and can solve the problems of inability to adjust temperature in real time and effectively control it

Active Publication Date: 2015-12-23
ZHONGTIAN TECH ADVANCED MATERIALS CO LTD +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention can overcome the problem that the current technology cannot adjust the temperature in the sintering process in real time and effectively control the transparency of the preform, and proposes a method based on PID control technology to adjust the temperature in the sintering process in real time and effectively control the transparency of the preform The method and its equipment can effectively prevent the rod body from being opaque after sintering due to improper setting of the sintering temperature of the sintering furnace.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sintering method and equipment of optical fiber preform rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0105] Set the temperature required for each stage on the temperature control cabinet 13, then install the powder preform 7 above the quartz suspender 4, send it into the furnace, and sinter according to the sintering method of the preform described above. A laser beam with a wavelength of 850nm and a power of 5.0mw is emitted from the laser transmitter 15, and the signal acquisition unit in the laser control cabinet 24 collects the laser power P' at the receiving end every 5s, and calculates the power difference ΔP =5mw-P'. Here, the upper limit value ΔPmax of ΔP is set to 4.5mw, and the lower limit value ΔPmin of ΔP is set to 3.5mw.

[0106] When the lower tail handle of the preform reaches the horizontal position of the laser, the laser senses the preform and enters the working state. When the ΔP value exceeds ΔPmax, the laser control cabinet sends a signal to the temperature control cabinet 13, requiring it to lower the furnace temperature by 10°C; when the ΔP value is lo...

Embodiment 2

[0108] Set the temperature required for each stage on the temperature control cabinet 13, then install the powder preform 7 above the quartz suspender 4, send it into the furnace, and sinter according to the sintering method of the preform described above. A laser beam with a wavelength of 850nm and a power of 5.0mw is emitted from the laser transmitter 15, and the signal acquisition unit in the laser control cabinet 24 collects the laser power P' at the receiving end every 5s, and calculates the power difference ΔP =5mw-P'. Here, the upper limit value ΔPmax of ΔP is set to 4.2mw, and the lower limit value ΔPmin of ΔP is set to 3.8mw.

[0109] When the lower tail handle of the preform reaches the horizontal position of the laser, the laser senses the preform and enters the working state. When the ΔP value exceeds ΔPmax, the laser control cabinet sends a signal to the temperature control cabinet 13, requiring it to lower the furnace temperature by 5°C; when the ΔP value is low...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a sintering method of optical fiber preform and equipment thereof. The invention relates to the field of optical fiber perform sintering, and particularly relates to a method and equipment which utilize a laser feedback control system for adjusting the temperature of a sintering furnace in a sintering process in real time so as to realize the closed-loop control over the sintering process. The equipment comprises a tower body, a motor I, a chuck, a quartz derrick, a guide rail, a gas suction port, powder perform, a quartz chamber, a washing tower, a furnace body, a heat insulation material, a heating body, a temperature control cabinet, a quartz furnace core pipe, a laser transmitter, a laser receiver, a Cl2 gas holder, a He gas holder, an N2 gas holder, a Cl2 mass flow controller, a He mass flow controller, an N2 mass flow controller, an MFC (Microfunction Circuit) flow control cabinet, a laser control cabinet, an air exhaust and supply controller, a motor control cabinet, a motor II, a thermocouple, a lead screw and a control computer.

Description

technical field [0001] A method and equipment for sintering an optical fiber preform according to the present invention relate to the field of sintering an optical fiber preform, specifically, a laser feedback control system is used to adjust the temperature of the sintering furnace in real time during the sintering process, so as to realize the control of the sintering process. A method and device for closed-loop control. The method can be used to adjust the temperature of the sintering furnace in real time during the sintering process, so as to effectively control the transparency of the preform and prevent the preform from being opaque after sintering due to improper setting of the sintering temperature of the sintering furnace. Background technique [0002] At present, during the process of sintering the preform in the sintering furnace, its temperature is mainly controlled by a temperature controller. The temperature controller pre-sets several stages and assigns a con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B37/012
Inventor 陶伟沈一春吴椿烽
Owner ZHONGTIAN TECH ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com