Scale and corrosion inhibitor

A technology of scale and corrosion inhibitor, weight percentage, applied in the field of scale and corrosion inhibitor, can solve the problems of single component, harm to human life, reduce heat transfer efficiency and so on

Inactive Publication Date: 2015-07-15
SHANDONG JIANZHU UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The use of circulating water in industry is beneficial to save the cost of enterprises and improve the benefits of enterprises. However, there will be two problems in the process of using circulating water. One is the evaporation of water, which causes the crystallization and precipitation of salts. The most common ones are Calcium carbonate, calcium silicate and other scales, the existence of scales greatly reduces the heat transfer efficiency, and the second is the electrochemical corrosion of circulating water on the equipment. Human life. At present, scale and corrosion inhibitors are added to circulating water to reduce the appearance of scale. However, the current scale and corrosion inhibitors on the market have a single component and the descaling effect is not good, especially for copper, brass pipes and wide pH. The treatment effect of circulating water is not good, which is the deficiency of existing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] A scale and corrosion inhibitor composed of the following components by weight percentage:

[0065] Amino Trimethylene Phosphonic Acid 25%

[0066] Hydroxyethylidene diphosphonic acid 2%

[0067] Sodium chloride 5%

[0068] Polyacrylic acid 3%

[0069] Hydrolyzed polymaleic acid 1%

[0070] Sodium ethylenediamine tetramethylene phosphonate 8%

[0071] The rest is water.

[0072] The pH of the raw water is 11, adding 30mg / L of scale and corrosion inhibitor, the copper test tube adhesion speed is 6.32mcm, the corrosion speed is 0.0003519mm / a, the brass test tube adhesion speed is 6.11mcm, and the corrosion The speed is 0.00006358mm / a.

Embodiment 2

[0074] Amino Trimethylene Phosphonic Acid 26.5%

[0075] Hydroxyethylidene diphosphonic acid 2.5%

[0076] Sodium chloride 5.6%

[0077] Polyacrylic acid 3.8%

[0078] Hydrolyzed polymaleic acid 1.2%

[0079] Sodium ethylene diamine tetramethylene phosphonate 8.5%

[0080] The rest is water.

[0081] The pH of the raw water is 11, and 30mg / L of scale and corrosion inhibitor is added. The adhesion speed of the copper test tube is 6.12mcm, the corrosion speed is 0.0003365mm / a, and the adhesion speed of the brass test tube is 6.02mcm. The speed is 0.00006183mm / a.

Embodiment 3

[0083] A scale and corrosion inhibitor composed of the following components by weight percentage:

[0084] Amino Trimethylene Phosphonic Acid 28.7%

[0085] Hydroxyethylidene diphosphonic acid 3.3%

[0086] Sodium chloride 6.7%

[0087] Polyacrylic acid 4.2%

[0088] Hydrolyzed polymaleic acid 1.6%

[0089] Sodium ethylenediamine tetramethylene phosphonate 9.2%

[0090] The rest is water.

[0091] The pH of the raw water is 11, 30mg / L of scale and corrosion inhibitor is added, and the adhesion speed of the copper test tube is 5.86mcm, the corrosion speed is 0.0002539mm / a, and the adhesion speed of the brass test tube is 5.77mcm, and the corrosion is monitored by detecting the heat exchanger. The speed is 0.00004957mm / a.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
speedaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of corrosion inhibitors, and concretely relates to a scale and corrosion inhibitor. The scale and corrosion inhibitor comprises 25-35wt% of aminotrimethylene phosphonic acid, 2-8wt% of 1-hydroxyethylidene-1,1-diphosphonic acid, 5-10wt% of sodium chloride, 3-8wt% of polyacrylic acid, 1-3wt% of hydrolytic polymaleic acid, 8-15wt% of sodium ethylenediamine tetramethylenephosphonate, and the balance water. The scale and corrosion inhibitor has a substantial effect on circulating water having a wide pH range of 3-11, has a substantial effect on copper tubes and brass tubes, allows the adherence speed and the corrosion speed of copper experiment tubes to be reduced 5.82mcm and 0.0002295mm / a respectively and the adherence speed and the corrosion speed of brass experiment tubes to be reduced to 5.55mcm and 0.00004458mm / a respectively.

Description

Technical field [0001] The invention relates to the technical field of corrosion inhibitors, more specifically a scale and corrosion inhibitor. Background technique [0002] The use of circulating water in industry is conducive to saving the cost of enterprises and improving the benefits of enterprises. However, there are two problems in the use of circulating water. One is that the evaporation of water causes the crystallization and precipitation of salts. The most common ones are Calcium carbonate, calcium silicate and other scales. The existence of scales greatly reduces the heat transfer efficiency. The second is the corrosive effect of the electrochemical corrosion of circulating water on the equipment. This corrosion is fatal, and the equipment is replaced in the light of it; Human life. Currently, scale and corrosion inhibitors are added to the circulating water to reduce the appearance of scale. However, the current scale and corrosion inhibitors on the market have a sing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C02F5/14C23F11/173
Inventor 郭晓斐牛林
Owner SHANDONG JIANZHU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap