A kind of conductive, barrier polyethylene composition and its preparation method and application

A composition and polyethylene technology, which is applied in the field of conductive and barrier polyethylene compositions, can solve the problems of high composition cost, narrow material processing window, and limited material application range, so as to increase the processing window and excellently prevent static electricity , low cost effect

Active Publication Date: 2015-12-16
KINGFA SCI & TECH CO LTD +1
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this patent, polyamide is used as the matrix resin, and polyethylene resin is dispersed in the polyamide resin. Since the melt strength of polyamide is low and is greatly affected by temperature and shear strength, the material processing window is narrow. Therefore, the scope of application of the material is limited
In addition, carbon nanotubes are added to the composition, and the resulting composition is expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of conductive, barrier polyethylene composition and its preparation method and application
  • A kind of conductive, barrier polyethylene composition and its preparation method and application
  • A kind of conductive, barrier polyethylene composition and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The present invention will be further described below through specific embodiments. The following examples are preferred implementation forms of the present invention, but the implementation manners of the present invention are not limited by the following examples.

[0035] In the composition formula of the example shown in Table 1: the selected polyethylene is HDPEMS201B of Tatol Company; due to the different melting points and viscosities of polyamides of different types and grades, the melting points selected in this example are 180°C, 220°C, Polyamides with viscosities of 2.1dL / g, 2.4dL / g, 3.4dL / g, 3.8dL / g, and 4.2dL / g at 240°C and 290°C respectively; the compatibilizer is maleic anhydride grafted polyethylene, of which The mass part of grafted maleic anhydride is 0.25 parts, and the grade is Dow’s GR320; the grade of carbon black is Ketjenblack EC300JD, the grade of carbon black I is Ketjenblack EC600JD, and the grade of carbon black II is CONDUCTEX7067; the grade ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a conductive barrier polyethylene composition, its preparation method and application. The composition comprises: (A) 50-90 parts by mass of base resin, which contains (A1) 70-97 mass% of polyethylene resin and (A2) 3-30 mass% of polyamide resin dispersed in the polyethylene resin (A1) in a multilayer overlapping lamellar structure; (B) 0.1-10 parts by mass of a polyolefin grafted copolymer; and (C) 5-25 parts by mass of carbon black. The composition provided in the invention takes polyethylene as the main base resin, fusion and kneading methods are employed to make the polyamide resin form the multilayer overlapping lamellar structure in the polyethylene resin. With excellent barrier property and conductivity, the polyethylene composition is low in cost, increases the material processing window, broadens the application field of materials, and can be used for preparing containers accommodating fuels and organic solvents, and conveying pipelines, etc.

Description

technical field [0001] The invention relates to a conductive and barrier polyethylene composition, in particular to a conductive and barrier polyethylene composition and its preparation method and application. Background technique [0002] Polyethylene is a non-polar high polymer, low in price, easy to process, has a certain rigidity and toughness, can prevent the penetration of water, is a good packaging material, but the disadvantage is that it cannot prevent the penetration of gas and organic liquids, thus limiting its use. In the packaging industry and other applications requiring high barrier properties. At present, there are three main technologies for improving the barrier properties of polyethylene materials: surface treatment technology, multi-layer co-extrusion technology, and blending barrier technology. Surface treatment technology is to fluorinate or sulfonate the surface of plastic products, or surface coating, etc. The application of this technology is limite...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L77/00C08L77/02C08L77/06C08L51/06C08K3/04
Inventor 张超蔡彤旻宁凯军姜苏俊宁方林王鹏宋晓辉易庆锋
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com