Preparation method of phenolic resin with cross-linked amino structure and application thereof
A technology of phenolic resin and cross-linked amine groups, which is applied in the field of preparation of highly selective adsorption resins, can solve the problems of limiting the reaction efficiency of amine functional groups, limited content of amine functional groups, complex resin synthesis steps, etc., and achieves production costs Low, low extraction efficiency, good use strength effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A kind of preparation method with the phenolic resin of cross-linked amino structure, the steps are as follows:
[0022] 1) Dissolve 20 g of phenol, 7.66 g of paraformaldehyde and 0.26 g of sodium hydroxide in 17.66 g of ethylene glycol in a 500 mL three-necked flask equipped with electric stirring, temperature control device, and reflux condenser, and heat to 90 ℃, keep warm for 2.5 h, then add 3.83 g paraformaldehyde and 3.83 g ethylenediamine into the reaction bottle, keep warm for 30 min, adjust the pH to 1.0 with a hydrochloric acid solution with a mass percent concentration of 36%, and obtain the reaction phase;
[0023] 2) Prepare a turbine oil containing Tween 80 mass percent with a concentration of 1% in a beaker as the dispersed phase;
[0024] 3) Mix the above-mentioned dispersed phase with the reaction phase for polymerization reaction, the mass ratio of the reaction phase and the dispersed phase is 1:2, stir the mixed solution and adjust the stirring speed ...
Embodiment 2
[0031] A kind of preparation method with the phenolic resin of cross-linked amino structure, the steps are as follows:
[0032] 1) Dissolve 30 g of phenol, 11.48 g of paraformaldehyde and 0.39 g of sodium hydroxide in 60.63 g of ethylene glycol in a 1000 mL three-neck flask equipped with electric stirring, temperature control device, and reflux condenser, and heat to 85 ℃, keep warm for 3 h, then add 9.57 g of paraformaldehyde and 9.57 g of ethylenediamine into the reaction flask, react at 80 °C for 30 min, adjust the pH to 1.5 with a hydrochloric acid solution with a mass percent concentration of 36%, and obtain the reaction phase;
[0033] 2) Prepare a turbine oil containing Tween 80 mass percent with a concentration of 1% in a beaker as the dispersed phase;
[0034] 3) Mix the above-mentioned dispersed phase with the reaction phase for polymerization reaction. The mass ratio of the reaction phase and the dispersed phase is 1:3. Stir the mixed solution and adjust the stirrin...
Embodiment 3
[0041] A kind of preparation method with the phenolic resin of cross-linked amino structure, the steps are as follows:
[0042] 1) Dissolve 30 g of phenol, 11.48 g of paraformaldehyde and 0.39 g of sodium hydroxide in 102.45 g of ethylene glycol in a 1000 mL three-necked flask equipped with electric stirring, temperature control device, and reflux condenser, and heat to 95°C Insulate for 2 hours, then add 9.57g of paraformaldehyde and 16.44g of diethylenetriamine into the reaction flask, react at 80°C for 30 minutes, adjust the pH to 1.5 with a hydrochloric acid solution with a concentration of 36% by mass, and obtain the reaction phase;
[0043] 2) Prepare a turbine oil containing Tween 80 mass percent with a concentration of 1% in a beaker as the dispersed phase;
[0044] 3) Mix the above-mentioned dispersed phase with the reaction phase for polymerization reaction, the mass ratio of the reaction phase and the dispersed phase is 1:2, stir the mixed solution and adjust the st...
PUM
Property | Measurement | Unit |
---|---|---|
purity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com