Bismuth/europium-ion-codoped zirconate fluorescent material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A fluorescent material, europium ion technology, applied in the field of ceramic phosphors, can solve the problems of low color rendering, complexity, and narrow visible light emission color gamut, and achieve the effect of wide emission color gamut and high-efficiency response characteristics
Inactive Publication Date: 2014-12-31
KUNMING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to solve the problems of the existing LED lighting phosphors, such as narrow visible light luminous color gamut, low color rendering, the need for compounding of various phosphors, high cost and complicated preparation methods, etc., using Bi and Eu ions as active ions to prepare Bismuth, europium ion co-doped zirconate white phosphor material with high-efficiency response to ultraviolet light excitation
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] (1) According to the molar ratio of Ba:Zr:Eu:Bi=1:1:0.025:0.05, weigh BaCO 3 , ZrO 2 、 Bi 2 o 3 and Eu 2 o 3 , and mix evenly;
[0015] (2) Put the mixture obtained in step (1) in a corundum crucible, pre-calcined in the air at 1300°C for 3 hours, after natural cooling, in a reducing atmosphere H 2 +N 2 Calcined at 1300°C for 3 hours, and after grinding, the zirconate fluorescent material BaZrO co-doped with bismuth and europium ions was obtained. 3 : 0.025Eu: 0.05Bi.
Embodiment 2
[0017] (1) According to the molar ratio of Mg: Zr: Eu: Bi = 1: 1: 0.01: 0.01, weigh MgCO 3 , ZrO 2 、 Bi 2 o 3 and Eu 2 o 3 , and mix evenly, wherein, M is any one of Mg, Ca, Sr, Ba;
[0018] (2) Put the mixture obtained in step (1) in a corundum crucible, pre-calcined in the air at 1300 ° C for 4 hours, after natural cooling, in a reducing atmosphere H 2 +N 2 Calcined at 1200°C for 5h, and after grinding, the zirconate fluorescent material MgZrO co-doped with bismuth and europium ions was obtained. 3 : 0.01Eu: 0.01Bi.
Embodiment 3
[0020] (1) According to the molar ratio of Ca: Zr: Eu: Bi = 1: 1: 0.03: 0.08, weigh CaCO 3 , ZrO 2 、 Bi 2 o 3 and Eu 2 o 3 , and mix evenly;
[0021] (2) Put the mixture obtained in step (1) in a corundum crucible, pre-calcined in air at 1300°C for 1 hour, after natural cooling, in a reducing atmosphere H 2 +N 2 Calcined at 1000°C for 1h, and after grinding, a zirconate fluorescent material CaZrO co-doped with bismuth and europium ions was obtained. 3 : 0.03Eu: 0.08Bi.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a bismuth / europium-ion-codoped zirconate fluorescent material and a preparation method thereof. The MZrO3:Eu:Bi mol ratio in the material is 1:(0.01-0.1):(0.01-0.1), wherein M is any one of Mg, Ca, Sr and Ba. The preparation method comprises the following steps: weighing MCO3, ZrO2, Bi2O3 and Eu2O3 according to the M:Zr:Eu:Bi mol ratio of 1:1:(0.01-0.1):(0.01-0.1), evenly mixing, precalcining the mixture in the air at 1300 DEG C for 1-4 hours, naturally cooling, calcining at 1000-1300 DEG C in a reducing atmosphere for 1-5 hours, and grinding to obtain the bismuth / europium-ion-codoped zirconate fluorescent material. The fluorescent powder has 470nm wideband emission peak from Bi<3+> and red feature emission of Eu<3+> under the excitation of 340nm ultraviolet light; and the fluorescent powder has wide light-emitting color range under the excitation of ultraviolet light, does not need multiple fluorescent powder ratios, and can not have the problem of color temperature drift.
Description
technical field [0001] The invention belongs to the technical field of display and illumination phosphors, and in particular relates to a ceramic phosphor with display and illumination functions under the excitation of ultraviolet light. Background technique [0002] White LED is a new type of solid-state lighting energy. It is considered to be a new energy that may replace traditional lighting sources in the 21st century due to its advantages of energy saving, long service life, low energy consumption, no pollution, and high efficiency. At present, there are two main ways to obtain white light LEDs: one is the multi-chip combination type, which combines LEDs that emit red, green, and blue light respectively, and mixes the three kinds of light to form white light emission. The white light of this scheme has the advantages of high brightness, good stability and color rendering; however, the cost is high, the driving circuit is complicated, and there is no large-scale producti...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more