A kind of preparation method of ecological type high-efficiency composite flocculant

A composite flocculant and ecological technology, applied in the direction of flocculation/sedimentation water/sewage treatment, etc., can solve the problems of unrealistic large-scale industrialization, complex production process of flocculation materials, high production cost, etc., and achieve the elimination of aluminum salt toxicity , good flocculation effect and good ecological security

Inactive Publication Date: 2011-12-21
NANKAI UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing methods and production processes for screening, cultivating, fermenting and extracting flocculation substances by microorganisms and bacteria are complicated and the production cost is too high. At present, most of them are still in the laboratory stage, and it is not realistic to implement large-scale industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of ecological type high-efficiency composite flocculant
  • A kind of preparation method of ecological type high-efficiency composite flocculant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of an ecological composite high-efficiency composite flocculant, the steps are as follows:

[0031] 1) Take 1 gram of sodium carboxymethyl cellulose and add 25 mL of water to fully stir and mix to form a sodium carboxymethyl cellulose solution;

[0032] 2) Take 5 grams of polyaluminum chloride, containing 0.667 grams of aluminum, and add 100 mL of water to form a polyaluminum salt solution;

[0033] 3) Slowly add the polyaluminum salt solution to the sodium carboxymethyl cellulose solution under the condition of magnetic stirring at 300 rpm and 70°C, stir for 30 minutes to obtain a mixed solution, and then put the mixed solution into a 40°C water bath Under the condition of composite reaction for 3 hours, a light yellow emulsion was obtained, which is the product flocculant A.

Embodiment 2

[0035] A preparation method of an ecological composite high-efficiency composite flocculant, the steps are as follows:

[0036] 1) Take 1 gram of sodium carboxymethyl cellulose and add 25 mL of water to fully stir and mix to form a sodium carboxymethyl cellulose solution;

[0037] 2) Take 5 grams of polyaluminum chloride, containing 0.667 grams of aluminum, and add 100 mL of water to form a polyaluminum salt solution;

[0038]3) Under the conditions of magnetic stirring at 300 rpm and heating at 80°C, slowly add the sodium carboxymethyl cellulose solution to the polyaluminum salt solution, stir for 15 minutes to obtain a mixed solution, and then place the mixed solution at 50°C The complex reaction was carried out for 5 hours in a water bath to obtain a light yellow emulsion, which is the product flocculant B.

Embodiment 3

[0040] A preparation method of an ecological composite high-efficiency composite flocculant, the steps are as follows:

[0041] 1) Take 4 grams of sodium carboxymethyl cellulose and add 100 mL of water to fully stir and mix to form a sodium carboxymethyl cellulose solution;

[0042] 2) Take 2 grams of polyaluminum chloride, containing 0.267 grams of aluminum, and add 40 mL of water to form a polyaluminum salt solution;

[0043] 3) Under the conditions of magnetic stirring at 200 rpm and heating at 70°C, slowly add the sodium carboxymethyl cellulose solution to the polyaluminum salt solution, and stir for 15 minutes to obtain a mixed solution; then place the mixed solution at 50°C The composite reaction was carried out for 3 hours under the condition of water bath, and a light yellow emulsion was obtained, which is the product flocculant C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for an ecological high-efficient complex flocculating agent. By the preparation method, the complex flocculating agent consisting of sodium carboxymethyl cellulose and inorganic aluminum salt is prepared by using the inorganic aluminum salt as a matrix basic material. The method comprises the following steps of: 1) mixing the sodium carboxymethyl cellulose with water and stirring to obtain transparent sticky sodium carboxymethyl cellulose solution; 2) mixing the inorganic aluminum salt with water to obtain polymeric aluminum salt solution; and 3) mixing the sodium carboxymethyl cellulose solution with the polymeric aluminum salt solution, stirring, and performing a complex reaction to obtain the light yellow emulsible complex flocculating agent. The preparation method has the advantages of: good flocculation effect, no secondary pollution and high ecological safety; the preparation method is simple, has mild reaction conditions, and is easy to extend to realize industrialized production; the preparation method is high in economic performance and low in cost, has wide synthetic raw material sources and meets the requirements on recycling economy and pollution-free production; and the preparation method has a wide applicable range, is suitable for various kinds of industrial wastewater and life wastewater, and even water supply industrial water, and the using range can be further extended by regulating formula proportions.

Description

technical field [0001] The invention relates to the fields of sewage treatment and water supply, in particular to a preparation method of an ecological composite high-efficiency composite flocculant used for industrial waste water or domestic sewage treatment and drinking water purification. Background technique [0002] At present, flocculants widely used in sewage treatment can be divided into inorganic flocculants, organic flocculants, microbial flocculants and composite flocculants. Among them, inorganic flocculants are cheap and have good flocculation effects, represented by aluminum salts, iron salts and their polymers; the density and strength of alum flowers formed by iron salts are relatively large, and the water purification effect is remarkable, and the effect is little affected by water temperature. It has a wide range of applications and has a good treatment effect on some raw water. However, the iron salt flocculant is not only strongly corrosive, but also requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/52C02F1/56
Inventor 杨晓霞周启星华涛王玉哲
Owner NANKAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com