Crack-resistant abrasion-resistant hydraulic concrete and preparation method thereof

A hydraulic concrete and anti-scouring technology, which is applied in the field of hydraulic concrete to improve the performance of concrete mixtures and anti-scour performance, the effect of readily available and cheap raw materials, and low production costs

Inactive Publication Date: 2011-04-13
广西壮族自治区水利科学研究院
View PDF3 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problems of cracks caused by plastic shrinkage, drying shrinkage and self-volume deformation while improving the anti-abrasion strength of hydraulic concrete, and to provide a kind of anti-crack and anti-abrasion hydraulic concrete and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crack-resistant abrasion-resistant hydraulic concrete and preparation method thereof
  • Crack-resistant abrasion-resistant hydraulic concrete and preparation method thereof
  • Crack-resistant abrasion-resistant hydraulic concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The technical solution of the present invention is trially applied to anti-scouring concrete of a water conservancy project in Guilin, Guangxi, with design grade of compressive strength C40 and anti-scouring strength ≥ 12.0h / kg / m 2 , 28d drying shrinkage value≤350×10 -6 , 28d self-generated volume deformation value ≤ 140×10 -6 , requiring no cracks after concrete pouring. The preparation method is as follows:

[0033] (1) Dry mix the cement, silica fume powder and polypropylene fiber evenly, then put the mixture and 1 / 2 water into the mixer, and stir for 35-40 seconds;

[0034] (2) Put sand, small stones, medium stones and large stones into the mixer on the basis of the completion of step (1), and stir for 45 to 50 seconds;

[0035] (3) On the basis of the completion of step (2), add internal curing agent, water reducing agent, air-entraining agent and the remaining 1 / 2 water into the mixer, and stir for 85-90 seconds;

[0036] (4) Install the concrete that has been...

Embodiment 2

[0043] The technical solution of the present invention is trially applied to anti-scouring concrete of a water conservancy project in Chuanjiang, Guilin, Guangxi. The design grade of compressive strength is C40, and the anti-scouring strength is ≥ 14.0h / kg / m 2 , 28d dry shrinkage value ≤ 300 × 10-6, 28d self-generated volume deformation value ≤ 120 × 10-6, requiring no cracks after concrete pouring. The preparation method is as follows:

[0044] (1) Dry mix the cement, silica fume and polypropylene fiber evenly, then put the mixture and 1 / 2 water into the mixer, and stir for 30-35 seconds;

[0045] (2) Put sand, small stones, medium stones and large stones into the mixer on the basis of the completion of step (1), and stir for 40 to 45 seconds;

[0046] (3) On the basis of the completion of step (2), add internal curing agent, water reducing agent, air-entraining agent and the remaining 1 / 2 water into the mixer, and stir for 80-85 seconds;

[0047] (4) Install the concrete t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses crack-resistant abrasion-resistant hydraulic concrete and a preparation method thereof. The hydraulic concrete comprises materials of cement, sand, stones, a polypropylene fiber, a water reducing agent, an air entraining agent and water, and is characterized in that: an internal curing agent and silica fume powder are added; by adopting the internal curing agent as a super absorbent resin, internal maintenance of the concrete is enhanced, the concrete shrinkage is reduced, the abrasion resistance of the concrete is improved, and the crack resistance of the concrete is improved; by adopting the silica fume powder, the concrete mixture performance and abrasion resistance are improved, the comprehensive utilization of industrial wastes and resource and energy conservation are realized, and the environment is protected; and taking concrete at C40 strength grade as an example, the abrasion resistance is 23.52h / kg / m<2>, the early plastic shrinkage crack resistance reaches the first grade, cracks are not formed on the surface of the concrete, an air shrinkage value within 28 days is 162*10<-6>, and the autogenous volume deformation within 28 days is 20*10<-6>. The technical scheme is simple in technical operation, readily available in raw materials, lower in production cost and better in economic and social benefits.

Description

Technical field: [0001] The invention belongs to the technical field of hydraulic concrete, and relates to an anti-cracking and anti-scouring hydraulic concrete and a preparation method thereof. Background technique: [0002] With the implementation of the western development strategy and the development strategy of power transmission from west to east, my country needs to build a number of large-scale high-water-head power stations. The flow velocity of the discharge structures reaches 40-50m / s, and when the water flow is entrained with suspended or displaced substances, the erosion and cavitation erosion suffered by the buildings will be even more serious. Therefore, higher requirements are put forward for the crack resistance and abrasion resistance of hydraulic concrete. Although the current hydraulic anti-scour concrete configuration technology can solve the anti-scour strength of hydraulic concrete, the cracks caused by the early plastic shrinkage, later drying shrink...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00
CPCC04B28/02Y02W30/91C04B14/02C04B14/06C04B16/0633C04B18/146C04B20/0076C04B40/0028C04B2103/302C04B2103/304C04B24/16
Inventor 陈建国郭晋川凌贤宗彭华娟周立新
Owner 广西壮族自治区水利科学研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com