Non-sintered brick based on flue gas desulfurization byproduct and preparation method thereof

A desulfurization by-product, sintering-free technology, applied in the field of building materials, can solve problems such as unsatisfactory effects, achieve significant economic and social benefits, meet energy conservation and emission reduction, and simplify the production process.

Inactive Publication Date: 2011-02-16
WUHAN KAIDI ELECTRIC POWER CO LTD
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Those skilled in the art have also been trying to replace solid clay bricks with industrial waste as raw materials, but the results obtained so far are not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-sintered brick based on flue gas desulfurization byproduct and preparation method thereof
  • Non-sintered brick based on flue gas desulfurization byproduct and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A non-sintered brick, which uses flue gas desulfurization ash as the main material, supplemented by cement, fly ash, gypsum and sand, is obtained by pressing and curing after adding water, mixing and stirring evenly. Among them: the desulfurization ash is the powder obtained by drying and sieving the desulfurization by-products produced by the semi-dry flue gas desulfurization process of the circulating fluidized bed. The remaining rate is about 3.48%. The calcium oxide content in the desulfurization ash is 55%, the sulfur oxide content is 28%, and the silicon and aluminum oxide content is 6%. The cement is selected from the national standard GB175-2007 with a strength grade of 32.5. The fly ash is grade II ash in the national standard GB / T1596-2005. The gypsum is selected from the first-grade dihydrate gypsum in the national standard GB5483-85. The sand is river sand that has been dried and sieved, and its water content is about 0.75%, and its particle size is all be...

Embodiment 2

[0032] Another kind of non-sintered brick, which uses flue gas desulfurization ash as the main material, supplemented by cement, fly ash, gypsum and sand, is obtained by pressing and curing after mixing with water and stirring evenly. Among them: the desulfurization ash is the powder obtained by drying and sieving the desulfurization by-products produced by the reflux circulating fluidized bed semi-dry flue gas desulfurization process. The moisture content is about 0.64%, and the 0.074mm square hole The excess sieve rate is about 4.76%, the calcium oxide content in the desulfurization ash in the desulfurization ash is 60%, the sulfur oxide content is 26%, and the silicon and aluminum oxide content is 5.8%. The cement is selected from the cement with a strength grade of 42.5 in the national standard GB175-2007. The fly ash is grade II ash in the national standard GB / T1596-2005. The gypsum is selected from the first-grade dihydrate gypsum in the national standard GB5483-85. Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a non-sintered brick based on a flue gas desulfurization byproduct and a preparation method thereof. The brick is prepared by the following steps: desulfurated ash produced by desulfuration treatment on flue gas generated in a coal fired power plant is taken as a main material, cement, fly ash, gypsum and sand are taken as auxiliary materials, water is added into the main material and the auxiliary materials, the mixture is evenly stirred and then is subject to compression moulding to obtain the brick, wherein the solid raw materials contain the following components by weight percent: 30-35% of the desulfurated ash, 10-15% of the cement, 5-10% of the fly ash, 3-5% of the gypsum and 40-50% of the sand; and the adding amount of the water accounts for 10-12% of the total weight of the solid raw materials. Because the brick takes the desulfurated ash as the raw material instead of solid clay, and natural resources are not used or used as little as possible, which avoids the damage on land resources owing to taking clay and reduces secondary pollution of the desulfurated ash. The preparation method comprises the steps of taking raw materials, mixing the raw materials, carrying out compression moulding and carrying out later-period consevation. The brick is not subject to high temperature sintering treatment, thus energy consumption is greatly reduced, and the protection and the improvement on ecological environment can be achieved more easily. Tests indicate that the non-sintered brick has strength grade greater than or equal to MU 10 grade, and can fully replace the traditional solid clay brick.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a non-sintered brick based on by-products of flue gas desulfurization and a preparation method thereof. Background technique [0002] With the rapid development of my country's national economy, the sharp increase of industrial solid waste that has not been utilized as secondary resources not only occupies a large amount of land resources and causes many secondary pollution problems, but also is a waste of resources. Increasing demands for environmental protection and economic policies to achieve sustainable development are not in harmony. The resource utilization of industrial solid waste has increasingly become a research hotspot for scientific researchers. [0003] Flue gas desulfurization (FGD) is the most widely used method in the world to control SO 2 emission technology. According to the form of desulfurization agent and desulfurization ash, it can be divided into wet, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/02C04B18/062Y02W30/91C04B14/06C04B18/08C04B22/143C04B40/0032C04B40/0071
Inventor 薛永杰韩旭魏世发王志龙张岩丰
Owner WUHAN KAIDI ELECTRIC POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products