Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for producing iron-metal-stone ceramics

A production method, iron gold stone technology, applied in the production field of iron gold stone ceramics, can solve the problems of weak strength and easy cracking of ceramic products

Inactive Publication Date: 2010-10-13
大连金州陶瓷艺术研究中心
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many unsolvable problems in ceramic products. The most typical problem is that the strength of ceramic products is relatively weak, and they are easy to break when they collide. Many excellent ancient ceramic handicrafts cannot be completely preserved; There is still room and need for improvement in the glaze color of products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for making ferrite ceramics, characterized in that: the method is carried out according to the following steps:

[0019] a. Get the raw materials mixed according to the following mass percentages:

[0020] Burnt stone powder 19%

[0021] Ash Clay 33%

[0022] Silica powder 4%

[0023] Fuzhou Bay Clay 18%

[0024] Melaleuca clay 11%

[0025] Iron Oxide 15%

[0026] b. Sieve the above-mentioned raw materials under a 60-mesh sieve, soak the sieved raw materials in sufficient water, let them stand for 22 hours and then stir them fully. After the sediment settles, decant the supernatant, Put the wet bottom mud on the gypsum board or brick, let the water in the bottom mud evaporate naturally, and when the water in the bottom mud evaporates to 10% (mass percentage) of the above raw materials, the mud refining and kneading will begin. mud process, and place the raw materials after the above treatment for 15 days.

[0027] c. The raw materials processed through t...

Embodiment 2

[0029] a. Take the raw materials mixed according to the following mass percentages:

[0030] Burnt stone powder 22%

[0031] Ash Clay 28%

[0032] Silica powder 6%

[0033] Fuzhou Bay Clay 24%

[0034] Laminated board clay 8%

[0035] Iron oxide 12%

[0036] b. Sieve the above raw materials under the 80-mesh sieve, and soak the sieved raw materials in sufficient water, let stand for 28 hours and then fully stir. After the sediment settles, decant the supernatant, Put the wet bottom mud on the gypsum board or brick, let the water in the bottom mud evaporate naturally, and when the water in the bottom mud evaporates to 15% (mass percentage) of the total amount of the above-mentioned raw materials, the mud refining and kneading will begin. mud process, and place the raw materials after the above treatment for 18 days.

[0037] c. The raw materials processed through the above steps are molded, dipped in glaze, and fired in a kiln to form a finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing iron-metal-stone ceramics, which is characterized by comprising the following steps: a. taking raw materials mixed according to certain mass percent; b. sieving the raw materials with 60-80 mesh screens, fully stirring the raw materials after the raw materials are soaked in water for 20-28h, decanting the supernatant after the sediment precipitates, evaporating the moisture in the sediment, carrying out sediment refining and wedging when the moisture in the sediment is evaporated until the content is 10-15% of the total amount of the raw materials and placing the treated raw materials for 15-18d; and c. molding the raw materials treated in the above steps, glazing the molded raw materials and firing the glazed raw materials in the kilns to produce finished products. The method can effectively improve the ceramic strength and enhance the brilliance of the ceramic glaze.

Description

technical field [0001] The invention relates to a method for making ceramics, in particular to a method for making ceramics that can enhance the strength of the ceramics and make the glaze color of the ceramics more vivid. Background technique [0002] As the birthplace of ceramic technology and the hometown of ceramic products, China's ceramic production technology has been developed for thousands of years, and many excellent ceramic production methods have been produced, as well as many excellent ceramic handicrafts that have been passed down through the ages. However, there are still many unsolvable problems in ceramic products. The most typical problem is that the strength of ceramic products is relatively weak, and they are easy to break when they collide. Many excellent ancient ceramic handicrafts cannot be completely preserved; There is still room and need for improvement in the glaze color of products. Contents of the invention [0003] The purpose of the present ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/00C04B33/14
Inventor 赵永峰
Owner 大连金州陶瓷艺术研究中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com