Method for improving electric conductivity of carbon nano tube network

A carbon nanotube and electrical conductivity technology, which is applied in the field of improving the electrical conductivity of carbon nanotube networks, can solve problems such as affecting the electrical conductivity of carbon nanotube fibers, and achieve the effects of improving electrical conductivity and performance.

Inactive Publication Date: 2012-01-04
SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This also affects the conductivity of the carbon nanotube fibers themselves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving electric conductivity of carbon nano tube network
  • Method for improving electric conductivity of carbon nano tube network
  • Method for improving electric conductivity of carbon nano tube network

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Specifically, proceed through the following steps:

[0023] 1) Carbon nanotube sample preparation: carbon nanotube powder was put into ethanol solvent to prepare a suspension, and the water area was sonicated for 3 hours. The substrate is a flat, cleaned quartz plate of 20mm×20mm×1mm. The substrate is placed on a heating stage with a temperature of 150°C, covered with a 0.3mm thick mask to control the shape and size of the sample, and placed for 10 minute. Use a pneumatic airbrush to spray the prepared carbon nanotube suspension onto the heated substrate in the form of a spray with the assistance of nitrogen, and control the spraying time so that the transmittance of the resulting carbon nanotube network at 550nm visible light is 88%. %. Replace the substrate with a conductive silicon wafer, repeat the above preparation process, so that the carbon nanotube network on the silicon wafer is the same as that on the quartz substrate, observe the sample on the silicon wafer...

Embodiment 2

[0029] Specifically, proceed through the following steps:

[0030] 1) Carbon nanotube sample preparation: carbon nanotube powder was put into ethanol solvent to prepare a suspension, and the water area was sonicated for 3 hours. The substrate is a flat, cleaned quartz plate of 20mm×20mm×1mm. The substrate is placed on a heating stage with a temperature of 150°C, covered with a 0.3mm thick mask to control the shape and size of the sample, and placed for 10 minute. Use a pneumatic airbrush to spray the prepared carbon nanotube suspension onto the heated substrate in the form of a spray with the assistance of nitrogen, and control the spraying time so that the transmittance of the resulting carbon nanotube network at 550nm visible light is 63%. %.

[0031] 2) Place the sample on the quartz substrate in a vacuum (vacuum degree 10 -4 Pa) was heated to 800K, kept for at least 30 minutes, and then naturally cooled to room temperature in vacuum. The conductivity of the network was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving electric conductivity of a carbon nano tube network, which comprises the following steps of: (1) uniformly distributing carbon nano tubes on the surface of a substrate to form a sample; (2) placing the distributed carbon nano tube sample in a target chamber of an ion beam irradiation device, and heating the sample; (3) after the carbon nano tube sample is heated to a thermodynamic temperature of between 700 and 1,000 DEG C, irradiating the sample by using ion beams; and (4) after the irradiation is finished, stopping heating, and cooling the sample to room temperature, and taking the sample out of the target chamber. Compared with the prior art, the method can effectively improve the electric conductivity of the carbon nano tube network underthe condition of avoiding chemical pollution, can be compatible with the conventional semiconductor process, and can be used for promoting the performance of carbon nano tube related devices and usedfor manufacturing flexible transparent conductive films of the carbon nano tubes.

Description

technical field [0001] The invention relates to a method for improving the conductivity of the carbon nanotube network. Background technique [0002] Since their discovery in 1991, carbon nanotubes have attracted great attention due to their excellent properties in electricity, heat, and mechanics. One of the application forms of carbon nanotubes is that multiple carbon nanotubes are aggregated into a network or film, which is generally soft, transparent and conductive. Although metallic carbon nanotubes themselves have good electrical conductivity, when they overlap to form a network, since adjacent carbon nanotubes only interact with each other by Van der Waals force, the contact resistance between the tubes is caused. Larger, which limits the conductivity of macroscopic carbon nanotube films. [0003] The currently reported methods to improve the conductivity of carbon nanotube films are mainly to disperse the carbon nanotubes with surfactants (such as sodium lauryl sul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/02
Inventor 周广颖闫隆
Owner SHANGHAI INST OF APPLIED PHYSICS - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com