Light non-fired hollow building blocks produced from ceramic waste residue and manufacturing method thereof
A technology of ceramic waste slag and hollow block is applied in the manufacture of the light-weight unburned hollow block, and the field of the lightweight unburned hollow block can solve the problems of affecting people's health, producing haze weather, air pollution and the like, Achieve good heat resistance and long-term stability, improve durability index, and reduce pollution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0039] The waste porcelain mud produced in the process of ceramic production is dehydrated into solid waste and damaged blanks, damaged waste products that have not been calcined and glazed, semi-finished products that have been calcined and glazed, waste products with damage or cracks, construction waste ceramics and sanitation The mixture of waste ceramic residues is crushed, sorted, pulverized, and magnetically separated to remove waste metals, and then dried, wheel-milled and sorted to make a powder with a particle size of less than -10mm;
[0040] A kind of volcanic ash-like mixed material formed by burning coal at high temperature to generate electricity is a kind of solid waste discharged from coal-fired power plants. The fineness is generally below 45um and then dried and screened to make fly ash powder.
[0041] The fine powder and leftover waste produced by the granite processing plant in the process of producing and cutting granite are crushed, sorted, pulverized, an...
Embodiment 2
[0044] Get the ceramic waste slag powder 55kg of embodiment 1, fly ash 20kg, granite waste slag powder 25kg, Portland cement 20kg, particle diameter is the unslaked lime powder 12kg of-0.2mm, gypsum powder 6kg, polycarboxylate high-efficiency 1.0kg of water reducing agent, 1.2kg of sodium carbonate, 0.6kg of calcium formate, 0.5kg of sodium sulfate and 18kg of water. The above raw materials are mixed with a twin-shaft mixing mixer until they are moist, and then extruded by mechanical vibration. Manufactured under a pressure of 28Mpa The molded ceramic waste lightweight hollow block has a specification of 390mm×140mm×190mm. It is cured at natural temperature, and then is naturally dried and cured at room temperature for 28 days by water spraying method to make the ceramic waste light-weight non-fired hollow block product. The average value of the tested compressive strength is: 6.8Mpa, and the minimum value of a single block is: 5.2Mpa, which is a qualified product.
Embodiment 3
[0046] Get embodiment 1 ceramic waste slag powder 60kg, fly ash 25kg, granite waste slag powder 23kg, Portland cement 22kg, particle diameter is the unslaked lime powder 13kg of-0.2mm, gypsum powder 6.5kg, polycarboxylate high-efficiency 1.5kg of water reducing agent, 1.5kg of sodium carbonate, 0.8kg of calcium formate, 0.6kg of sodium sulfate and 20kg of water, the above raw materials are mixed with a twin-shaft mixing mixer until they are wet, and then extruded by mechanical vibration, and manufactured under a pressure of 26Mpa The molded ceramic waste lightweight solid partition wall bricks, the specification is: 230mm×110mm×45mm, are cured at natural temperature, and then naturally dried and cured at room temperature for 28 days by water spraying method to make ceramic waste light-weight non-burning brick products. The average value of the tested compressive strength is: 9.8Mpa; the minimum value of a single block is: 8.0Mpa, and the flexural strength is: 5.0Mpa, which is a...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap