Meteorologic balloon and production method thereof

A weather balloon and production method technology, applied in the direction of instruments and the like, can solve the problems of poor cold resistance, cold resistance and low temperature elongation of balloons, and achieve the effects of good film forming effect, large elongation performance, and improved uniformity.

Active Publication Date: 2009-12-02
CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] E. Balloons have poor cold resistance
The sounding balloon is used to expand at a low temperature and low pressure of -80 degrees, which requires good cold resistance and high elongation. In the prior art, the formula balloon has poor cold resistance and low temperature elongation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A weather balloon with a mass of 1600g, a body length of 3.05cm, a handle width of 10cm, and a handle length of 14cm. The thickness of the handle of the weather balloon is 0.2mm. The top, handle and waist of the ball The thickness difference between the two is controlled within 0.03mm.

[0037] The production method of the weather balloon mentioned above, its raw materials are composed of solid raw materials, oily raw materials, and colloidal raw materials. The composition and weight ratio of the solid raw materials are: 0.10 parts of potassium hydroxide, 0-0.15 parts of casein, and O0. .10 parts, 1.0 part sulfur, 1.00 part N-phenyl-2-naphthylamine, 1.00 part N-phenyl-N'-isopropyl-p-phenylenediamine, ethyl-phenyl-dithiocarbamic acid The weight ratio of zinc 1.50 parts, zinc oxide 0.20 parts, dioctyl sebacate is 5.00 parts, the addition amount of centrifugal concentrated natural rubber latex is 100 parts, and the addition amount of chloroprene polymer is 20 parts.

[0038]Th...

Embodiment 2

[0040] A weather balloon with a mass of 1700g, a body length of 3.55cm, a handle width of 11cm, and a handle length of 16cm. The thickness of the handle of the weather balloon is 0.2mm. The thickness difference is controlled within 0.03mm.

[0041] The production method of the weather balloon mentioned above, its raw materials are composed of solid raw materials, oily raw materials, and colloidal raw materials. The composition and weight ratio of the solid raw materials are: 0.30 parts of potassium hydroxide, 0.15 parts of casein, and 0.10 parts of O. , 3 parts of sulfur, 2 parts of N-phenyl-2-naphthylamine, 2 parts of N-phenyl-N'-isopropyl-p-phenylenediamine, 3 parts of ethyl-phenyl-dithiocarbamate zinc The weight ratio of 5 parts of zinc oxide to dioctyl sebacate is 5.00 to 10.0 parts, the addition amount of centrifugal concentrated natural rubber latex is 100 parts, and the addition amount of chloroprene polymer is 5 parts.

[0042] The raw material preparation method is as fol...

Embodiment 3

[0044] A weather balloon with a mass of 1650g, a body length of 3.05cm, a handle width of 10cm, and a handle length of 12cm. The thickness of the handle of the weather balloon is 0.2mm. The thickness difference is controlled within 0.03mm.

[0045] The production method of the weather balloon mentioned above, its raw materials are composed of solid raw materials, oily raw materials, and gelatinous raw materials. The composition and weight ratio of the solid raw materials are: 0.15 parts of potassium hydroxide, 0.10 parts of casein, and 0.10 parts of plain O. , Sulfur 2.00 parts, N-phenyl-2-naphthylamine 1.5 parts, N-phenyl-N'-isopropyl-p-phenylenediamine 1.50 parts, ethyl-phenyl-dithiocarbamate zinc 2.00 parts The weight ratio of 3 parts of zinc oxide to dioctyl sebacate is 5.00 to 10.0 parts, the addition amount of centrifugal concentrated natural rubber latex is 100 parts, and the polymer of chloroprene is 30 parts.

[0046] The raw material preparation method is as follows: fir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a meteorologic balloon and a production method thereof. The raw materials consist of a solid raw material, an oily raw material and a gluey raw material; the solid raw material comprises the following components by weight: 0 to 0.30 portion of potassium hydroxide, 0 to 0.15 portion of casein, 0 to 0.10 portion of peregal O, 1.00 to 3 portions of sulfur, 1.00 to 2 portions of N-phenyl-2-naphthylamine, 1.00 to 2 portions of N-phenyl-N'-isopropyl-ursol, 1.50 to 3 portions of ethyl-phenyl-zinc dithiocarbamate, 0.20 to 5 portions of zinc oxide, and 5 to 30 portions of chloroprene polymer; the oily raw material is dioctyl sebacate, and the weight rate of the dioctyl sebacate is 5.00 to 10.0 portions; and the gluey raw material is centrifugally-concentrated natural latex, and the adding amount of the centrifugal concentrated natural latex is 100 portions. The weight of the meteorologic balloon is 1,600 to 1,700 grams, the length of the balloon body is 3.05 to 3.55 meters, the width of the ball handle is 10 to 11 centimeters, and the length of the ball handle is 12 to 16 centimeters. The meteorologic balloon can adapt to the requirement of probing high-altitude meteorological elements of more than 35,000 meters, has the advantages of good aging resistance, high blastoff height, long balloon service time and the like, and can effectively overcome the morning-evening difference.

Description

Technical field [0001] The invention relates to a vehicle for detecting air weather and a production method thereof, in particular to a weather balloon and a production method thereof. Background technique [0002] Meteorological balloon is a vehicle commonly used to detect meteorological elements in the air. It is not only used by the meteorological department to detect meteorological elements and provide meteorological guarantee conditions, but also is an indispensable means of meteorological testing when troops perform national defense scientific research and military missions such as space, aviation, navigation, and combat. In recent years, due to rapid industrial development, large changes in the geographical environment, and global climate warming, many changes have taken place in meteorological elements in various places. Weather balloons should adapt to the constantly changing and complex meteorological elements in the atmosphere. With the development of science and techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01W1/08
Inventor 肖迪娥张望
Owner CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com