1,4,5,8-naphthalenetetracarboxylic imide derivative bifluorescent material and method of preparing the same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of naphthalene tetracarboxylic acid diimide and dual fluorescence, which is applied in the fields of luminescent materials, chemical instruments and methods, organic chemistry, etc., can solve the problem of low quantum yield and achieve the effect of high thermal stability
Inactive Publication Date: 2012-10-03
ANHUI UNIVERSITY
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the quantum yield of this kind of dual fluorescent materials is very low, so how to prepare naphthalene diamide fluorescent materials with higher fluorescence quantum yield through molecular design and tailoring is a challenge for researchers.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0044] Taking R as 4,6-dimethylpyrimidine as an example, non-limiting examples are described as follows:
[0045] 1. Refining of raw materials of naphthalene tetracarboxylic dianhydride: heating and dissolving the purchased industrial-grade naphthalene tetracarboxylic dianhydride raw material with KOH aqueous solution, and then recrystallizing with ethanol to obtain crystalline potassium salt of naphthalene tetracarboxylic acid, which is dissolved in an appropriate amount of water Use hydrochloric acid to adjust the pH of the solution to <3, and a large amount of white precipitates are produced. The precipitates are separated, and the precipitates are vacuum-dried to obtain relatively pure yellow naphthalene tetracarboxylic dianhydride powder.
[0046] 2. Preparation of intermediate (1):
[0047] Get 2.00g (7.46mmol) of refined naphthalene tetracarboxylic dianhydride in a three-necked flask, add 20mL DMF, 13mg (0.07mmol) zinc acetate, in N 2 When heated to ≥100° C. under prot...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a 1,4,5,8-naphthalenetetracarboxylic acid diimide derivative bifluorescence material which has a chemical name of N-(2-ethylhexyl)-N-R- naphthalenetetracarboxylic formyl diimide compound and has a chemical formula; in the formula, R is selected from an a structural formula. A preparation method of the bifluorescence material takes naphthalene tetracarboxylic acid dianhydride of industrial product as raw materials which are first imidized with 2-ethyl-hexylamine to obtain an intermediate (1) N-(2-ethylhexyl)-naphthalene-1,8-dimethyl benzene anhydride-4,5-dicarboximide, and then the intermediate (1) is respectively imidized with 4-amino-1,2,4-triazole or 2-aminopyridine or 2-amino-4,6-dimethylpyrimidine to obtain a target product, and the imidization is that the raw materials are reacted for at least 5 hours at 140-160 DEG C under the protection of nitrogen in organic solvent and in the presence of catalyst zinc acetate.
Description
1. Technical field [0001] The present invention relates to an organic dual fluorescent material and a preparation method thereof, in particular to a class of organic dual fluorescent material with electrochemiluminescent properties and a preparation method thereof, specifically a naphthalene diimide dual fluorescent material and its preparation method. Preparation. 2. Background technology [0002] Naphthalene diamide derivatives are used in photosynthesis (R.F.Kelley, M.J.Tauber and M.R.Wasielewski, J.Am.Chem.Soc., 2006, 128, 4779), solar cells (M.Tasior, D.T.Gryko, M.Cembor, J.S.Jaworski, New J.Chem., 2007, 31, 247), field Effect transistors (Y.Ofir, A.Zelichenok and S.Yitzchaik, J.Mater.Chem., 2006, 16, 2142), gas storage (K.L.Mulfort and J.T.Huppand, J.Am.Chem.Soc., 2007, 129, 9604), biosensors (H.S.Cao, V.Chang, R.Hernandez and M.D.Heagy, J.Org.Chem., 2005, 70, 4929), anticancer drugs (Y.Chu, S.Sorey, D.W.Hoffman and B.L. Iverson, J.Am.Chem.Soc., 2007, 129, 1304) and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.