Bamboo fibre and ramie hemp blended yarn and production method thereof
A technology of ramie fiber and production method, which is applied in the field of bamboo fiber and ramie fiber blended yarn and its production, can solve the problems of pure ramie products such as difficulty in weaving, itchy wearing performance, and whitening of dyeing, so as to achieve improved hand feeling and appearance, and bright dyeing , Strong effect of dehumidification
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] make 14 s yarn.
[0015] Bamboo fiber and ramie fiber (short fiber) are selected at a ratio of 55:45, which are evenly stacked in the plucking machine, and rolled into rolls after being grasped, mixed, opened, and impurity removed, and the weight of the roll is controlled at 495±5 g / m; the roll is carded into strips, the speed of the carding licker-in roller is controlled at 750-900 rpm (900 rpm in this embodiment), the draft ratio is 107 times, and the carding sliver weighs 28.5 ± 0.5 g / min 5 meters; the sliver after carding is further evenly stretched on the drawing frame and combined into mature sliver, and the drawing draft ratio is controlled at 7.5-8.5 times (the present embodiment is 7.8 times), and the drawing process conditions are as follows: : 9×12(mm), front roller speed: 2000 rpm.
[0016] Spinning is that cooked sliver is spun into roving, and the spinning roving process condition is that the draft ratio of roving is controlled at 6.5-8.5 times (the pres...
Embodiment 2
[0025] make 32 s yarn.
[0026] Select bamboo fiber strips and ramie fiber strips (medium-length fibers), the ratio of which is 90:10, mix bamboo fiber strips and ramie strips on a carding machine, and evenly draft mature strips, and control the draft ratio of the combs at 7.5-9.5 times (the present embodiment is 8.5 times). The technological conditions are needle plate striking times: 852 times / minute, needle plate specification: 7-13 needles / hour, back tension: 1.013, front tension: 1.014.
[0027] Spinning is that cooked sliver is spun into roving, and the process condition of spinning head roving is that the draft ratio of roving is controlled at 6.5-8.5 times (the present embodiment is 8.5 times), spindle speed: 300 rpm, front roller speed: 185 rpm / min, the twist coefficient is 19; the process condition of spinning the second roving is that the draft ratio of the roving is controlled at 6.5-8.5 times (the present embodiment is 8.2 times), the spindle speed: 450 rev / min...
Embodiment 3
[0035] make 7 s yarn.
[0036] Bamboo fiber and ramie fiber (short fiber) are selected at a ratio of 25:75, and they are evenly stacked in the plucking machine, and rolled into rolls after grasping, mixing, opening, and impurity removal, and the weight of the roll is controlled at 495±5 g / m; the roll is carded into strips, the speed of the carding licker-in roller is controlled at 750-900 rpm (900 rpm in this embodiment), the draft ratio is 107 times, and the carding sliver weighs 28.5 ± 0.5 g / min 5 meters; the sliver after carding is further evenly straightened on the drawing frame and combined into mature sliver, and the drawing draft ratio is controlled at 7.5-8.5 times (the present embodiment is 8 times), and the drawing process conditions are as follows: roller gauge : 9×12(mm), front roller speed: 2000 rpm.
[0037] Spinning is that cooked sliver is made into yarn through air spinning, and its process conditions are: opening roller speed 5500-7500 rev / min (this embodim...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com