Method for producing electromagnetic stove ceramic cooking utensil with magnetic resonant heating film

A technology for cooking utensils and a manufacturing method, which is applied in the field of induction cooker ceramic cooking utensils, can solve the problems of damage to nutrients, inability to achieve the original taste, damage, etc. Effect

Inactive Publication Date: 2007-01-24
陈国彬
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional cooking utensils for induction cookers are basically metal products made of iron or stainless steel. Although metal products conduct heat quickly, they quickly decompose nutrients in food, thereby destroying some nutrients and failing to achieve the original purpose. It is authentic, and metal utensils have poor thermal insulation performance. Some trace metals may cause harm to the human body after long-term use. Therefore, ceramic cooking utensils used in induction cookers have become the first choice for home kitchens and catering industries. The obvious advantage of convenience is entering mass consumption, so how to apply ceramic cooking utensils to induction cookers has become an urgent requirement for the catering industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] 1. Prepare materials

[0008] ①Silver 1kg, ink 0.3kg, add appropriate steel balls. Mixed with steel balls and milled for 4 hours,

[0009] 800-mesh sieve to form low-temperature material for later use.

[0010] ② 1kg of low-temperature colorant (760-800°C) and 0.3kg of ink are evenly mixed and ball-milled for 4 hours, and passed through a 800-mesh sieve to form a low-temperature material for later use.

[0011] ③ printing paper and printing oil.

[0012] 2. Membrane production:

[0013] The root diameter of the product is required to be ¢150 mm. Place the printing paper under a 160-mesh screen and print twice with the prepared silver material. After the silver film is printed, use a low-temperature material to print the protective layer. After drying, print the cover oil again.

[0014] 3. Film sticking and decaling process: immerse the printed finished film in water for 4 minutes, the film and the printing paper are separated by themselves, and then stick the film...

Embodiment 2

[0016] 1. The preparation of materials is the same as in 1 in Example 1.

[0017] 2. According to the size of the product and the required bottom diameter of 180 mm, place the printing paper under a 200-mesh screen, print 3 times with the prepared silver material, and then print the protective layer. After the film is dry, print the cover oil.

[0018] 3. Same as 3 in Embodiment 1, the ceramic vessel can be used normally on a 1600W induction cooker.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses making process of electromagnetic oven ceramic cooking utensil with magnetic resonant heating film, and ceramic cooking utensil features its heating layer, which is one magnetic resonant heating film to block magnetic force lines to form magnetic force eddy flow. The magnetic resonant heating film is 0.02-0.15mm thick and has one antioxidant protecting layer of 0.02-0.15mm thickness. The present invention makes it possible to use ceramic cooking utensil on electromagnetic oven.

Description

technical field [0001] The invention relates to a method for manufacturing a ceramic cooking vessel, in particular to a method for manufacturing an induction cooker ceramic cooking vessel with a magnetic resonance heating film. Background technique [0002] Traditional cooking utensils for induction cookers are basically metal products made of iron or stainless steel. Although metal products conduct heat quickly, they quickly decompose nutrients in food, thereby destroying some nutrients and failing to achieve the original purpose. It is authentic, and the insulation performance of metal utensils is poor. Long-term use of some trace metals may cause harm to the human body. Therefore, ceramic cooking utensils used in induction cookers have become the first choice for home kitchens and catering industries. The obvious advantage of convenience is entering mass consumption, so how to apply ceramic cooking utensils to induction cookers has become an urgent requirement of the cate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/80A47J27/00
Inventor 陈国彬
Owner 陈国彬
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products