Trimethylolpropane ester-based plasticizer composition for polyvinyl chloride resin

A technology of trimethylolpropane ester and trimethylolpropane, which is applied in the field of trimethylolpropane ester-based plasticizer compositions, and can solve the problems of poor physical properties and weak chemical bonds of trimethylolpropane ester

Inactive Publication Date: 2003-04-02
LG CHEM LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As mentioned above, trimethylolpropane esters have poor physical properties because one-component esters have too many weak bonds to function as plasticizers, even in the absence of compatibility with PVC resins Also (US Patent No. 3939201)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Next, the present invention will be described in more detail by the following examples and comparative examples. However, the following examples are only for the understanding of the present invention, and the present invention is not limited by the following examples. Embodiment 1 (preparation of plasticizer composition containing trimethylolpropane ester)

[0028] 268.36 grams of trimethylolpropane, 576.84 grams of 2-ethylhexanoic acid, 366.39 grams of benzoic acid, 50 grams of xylene as an entrainer substance, and 2.83 grams of tetraisopropyl titanate as a catalyst were added to a 2 In a 4-neck round bottom flask equipped with a stirrer and a condenser, the reaction was carried out for 10 hours by raising the temperature of the mixture to 220°C.

[0029] After the reaction, use a vacuum pump to evacuate the flask to 2mmHg at 200°C, remove unreacted acid, and neutralize the contents of the flask with 5% by weight of sodium hydroxide, wash and dry, and then add absorb...

Embodiment 2

[0042] Trimethylolpropane esters and samples were prepared by the same method as in Example 1, except that the raw materials and quantities are shown in Table 1 below, and the results of measuring the esters for physical properties are shown in Table 2 below.

[0043] The composition ratio of the ester mixture is 25.65% by weight of trimethylolpropane tri-2-ethylhexanoate, 44.72% by weight of 2,2-bis-2-ethylhexanoylmethoxybutyl benzoate, 24.05% by weight of 2,2-bis-benzoylmethoxybutyl 2-ethylhexanoate, 3.47% by weight trimethylolpropane tribenzoate, and 2.11% by weight other ingredients.

Embodiment 3

[0045] Trimethylolpropane esters and samples were prepared by the same method as in Example 1, except that the raw materials and quantities are shown in Table 1 below, and the results of measuring the esters for physical properties are shown in Table 2 below.

[0046] The composition ratio of the ester mixture is 34.51% by weight trimethylolpropane tri-2-ethylhexanoate, 44.56% by weight 2,2-bis 2-ethylhexanoyl methoxybutyl benzoate, 17.52% by weight 2,2-bis-benzoylmethoxybutyl 2-ethylhexanoate, 1.38% by weight of trimethylolpropane tribenzoate, and 2.03% by weight of other ingredients.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a trimethylolpropane ester-based plasticizer composition for polyvinyl chloride resin, more particularly a plasticizer composition comprising trimethylolpropane ester capable of using as plasticizer of polyvinyl chloride resin. The present invention can prepare polyvinyl chloride resin having superior tensile strength, elongation, migration, and sheet heating loss etc. by using the plasticizer composition.

Description

field of invention [0001] The present invention relates to a trimethylolpropane ester-based plasticizer composition, more particularly a trimethylolpropane ester-based plasticizer composition used as a plasticizer in the preparation of polyvinyl chloride resin. Background technique [0002] Polyvinyl chloride (PVC) is a general resin, properly mixed with some additives, such as stabilizers, fillers, pigments and plasticizers, it can obtain various physical processing properties. Polyvinyl chloride, which has various physical processing properties, is widely used as a raw material for various items such as wallpaper, gloves, and toys, and is also used for pipes, wire insulation materials, and artificial leather. In order to impart various physical properties to polyvinyl chloride resin, such as processability, flexibility, electrical insulation, etc., plasticizers are necessary additives for the preparation of polyvinyl chloride. [0003] Typi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K5/057C08K5/09C08K5/103C08L27/06
CPCC08K5/103C08L27/06
Inventor 李启锡李揆一金显圭
Owner LG CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap