Rubber composition and preparation method thereof

A technology of rubber composition and masterbatch, which is applied in the field of rubber, can solve the problems such as not easy to disperse, and achieve the effect of good wear, high tensile strength and balance

Pending Publication Date: 2022-08-09
QINGDAO DOUBLESTAR TIRE IND CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the existing technology, the technical problem to be solved by the present invention is to overcome the problem that the existing natural rubber system uses white carbon black as a reinforcing material that is not easy to disperse, and propose a method that can reduce hysteresis energy loss and reduce rubber compound Heat generation, significantly improving the controllability of the rubber compound, improving the processability of the rubber compound and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] This embodiment provides a hydroxy POSS / natural rubber composition for regulating the physicochemical properties of the sizing material and a preparation method thereof.

[0051] The formula is specifically:

[0052] In parts by weight, it includes the following components: 100 parts of natural rubber, 2 parts of D-POSS, 5 parts of silane coupling agent, 40 parts of high wear-resistant carbon black (HAF) N330, 8 parts of zinc oxide, 2.5 parts of stearic acid parts, 2.5 parts of antioxidant, 3 parts of S, and 1 part of accelerator; among them, granule glue 1# is used, the molecular weight is 300,000-350,000, the low viscosity system is used, the Mooney viscosity is 68 degrees, and 1,4- The isoprene unit accounts for 90% of the mass of the rubber segment of the pellet rubber.

[0053] The preparation method includes the following steps:

[0054] The first stage of mixing: the rotor speed is 45rpm, and the upper bolt pressure is 6.0MPa. First, the hydroxyl POSS and silan...

Embodiment 2

[0058] This embodiment provides a hydroxy POSS / natural rubber composition for regulating the physicochemical properties of the sizing material and a preparation method thereof.

[0059] The formula is specifically:

[0060] In parts by weight, it includes the following components: 100 parts of natural rubber, 2.2 parts of D-POSS, 5 parts of silane coupling agent, 40 parts of high wear-resistant carbon black (HAF) N330, 8 parts of zinc oxide, 2.5 parts of stearic acid parts, 2.5 parts of antioxidant, 3 parts of S, and 1 part of accelerator.

[0061] The preparation method is the same as in Example 1.

Embodiment 3

[0063] This embodiment provides a hydroxy POSS / natural rubber composition for regulating the physicochemical properties of the sizing material and a preparation method thereof.

[0064] The formula is specifically:

[0065] In parts by weight, it includes the following components: 100 parts of natural rubber, 3 parts of D-POSS, 5 parts of silane coupling agent, 40 parts of high wear-resistant carbon black (HAF) N330, 8 parts of zinc oxide, 2.5 parts of stearic acid parts, 2.5 parts of antioxidant, 3 parts of S, and 1 part of accelerator.

[0066] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Mooney viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a rubber composition and a preparation method thereof, and belongs to the technical field of rubber. The modified natural rubber comprises the following components in parts by weight: 100 parts of natural rubber, 1-3 parts of hydroxyl POSS (Polyhedral Oligomeric Silsesquioxane) and 5-10 parts of a silane coupling agent, the hydroxyl POSS is any one of octahydroxy butylation-POSS, trans-cyclohexanediol heptyl-POSS, trisilanol-isooctyl-POSS and trisilanol phenyl-POSS, and the hydroxyl POSS is any one of octahydroxy butylation-POSS, trans-cyclohexanediol heptyl-POSS, trisilanol-isooctyl-POSS and trisilanol phenyl-POSS. The silane coupling agent is liquid Si-69, and the main structure of the silane coupling agent is bis-[gamma-(triethoxysilyl) propyl] tetrasulfide. The invention is applied to the aspect of rubber materials, solves the problem that the existing natural rubber system takes white carbon black as a reinforcing material and is not easy to disperse, and can reduce the hysteresis energy loss, reduce the heat generation of the rubber materials, obviously improve the controllability of the rubber materials and improve the processability of the rubber materials.

Description

technical field [0001] The invention belongs to the technical field of rubber, and in particular relates to a rubber composition and a preparation method thereof. Background technique [0002] Since the tire itself is temperature sensitive and is a poor conductor of heat, during use, a large amount of heat generated by dynamic heat generation accumulates inside the material, resulting in an increase in temperature. Therefore, on the one hand, the oxidation of the rubber will be accelerated, the molecular chain will be broken, and softening will occur; on the other hand, the temperature may also lead to further branching and cross-linking of the rubber, which will reduce the strength of the rubber, harden the surface, crack and lose elasticity, and deteriorate the product. performance, thereby shortening product life and increasing safety risks. [0003] Existing tires are often made of natural rubber and butadiene rubber as the main materials, and silica as the reinforcing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L83/04C08K5/548C08K3/04C08K3/06C08K3/22C08K5/09
CPCC08L7/00C08K2003/2296C08L83/04C08K5/548C08K3/04C08K3/06C08K3/22C08K5/09Y02T10/86
Inventor 王鹏君张进生王洋李慧张晨罗宝玉高绪风丛守清刘连波方永清
Owner QINGDAO DOUBLESTAR TIRE IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap