Anti-foaming two-component coating capable of being thickly coated as well as preparation method and construction method of anti-foaming two-component coating

A two-component coating, anti-foaming technology, applied in polyester coatings, coatings, devices for coating liquid on the surface, etc., can solve problems such as bubbles, time and manpower consumption, and adverse effects of topcoat spraying, etc. Achieve excellent performance, high economic value and market prospects, and solve the difficulties of rapid production and shortened construction period

Pending Publication Date: 2022-07-15
上海君子兰新材料股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional painting method is to spray multiple primers on the wood surface. However, after each primer is sprayed, it needs to wait for a period of time to dry completely before polishing, and then proceed to the next painting process. Such a painting process requires consumes a lot of time and manpower
[0003] But, along with the progress of technology, researchers have all done more improvement and optimization in aspects such as the formulation and performance of two-component coatings, Chinese invention patent CN111040601A discloses a kind of water-based skin feeling two-component wood coating, in In the published patent, it is prepared by water-based polyurethane, defoamer, wetting agent, matting powder, and isocyanate. However, after the two-component coating prepared in the published patent is after-coated at one time, bubbles, Detrimental effect on subsequent topcoat application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-foaming two-component coating capable of being thickly coated as well as preparation method and construction method of anti-foaming two-component coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] A two-component paint capable of thick coating and anti-foaming, the preparation raw materials include a first component and a second component;

[0073] The raw materials for the preparation of the first component, in terms of weight percentage, include: 40% resin material, 20% first filler, 30% second filler, 5% auxiliary agent, and solvent makes up the balance;

[0074] The raw materials for the preparation of the second component, in terms of weight percentages, include: 30% solvent, 0.5% dehydrating agent, and solidifying agent supplementary balance to 100%;

[0075] The resin material is hydroxy alkyd resin, and the brand name is XC9855 of Xiance Company;

[0076] The first filler is titanium dioxide, the median particle size is 0.3 μm, model NTR-606A, purchased from Ningbo Xinfu Titanium Dioxide Co., Ltd.;

[0077] Described second filler is talcum powder, particle diameter is 1250 meshes, purchased from Guangzhou Shenpeng Chemical Co., Ltd.;

[0078] Described...

Embodiment 2

[0093] A two-component paint capable of thick coating and anti-foaming, the preparation raw materials include a first component and a second component;

[0094] The raw materials for the preparation of the first component, in terms of weight percentage, include: 40% resin material, 15% first filler, 35% second filler, 5% auxiliary agent, and solvent makes up the balance;

[0095] The raw materials for the preparation of the second component, in terms of weight percentages, include: 30% solvent, 0.5% dehydrating agent, and solidifying agent supplementary balance to 100%;

[0096] The resin material is hydroxy alkyd resin, and the trade name is Fangxin Company FX-6107;

[0097] The first filler is titanium dioxide, which is CR-828 purchased from Kemeiji Company;

[0098] Described second filler is talcum powder, particle diameter is 1250 meshes, purchased from Guangzhou Shenpeng Chemical Co., Ltd.;

[0099] Described auxiliary agent includes dispersant, defoamer, leveling agen...

Embodiment 3

[0114] A two-component paint capable of thick coating and anti-foaming, the preparation raw materials include a first component and a second component;

[0115] The raw materials for the preparation of the first component, by weight percentage, include: 35% of resin material, 20% of first filler, 35% of second filler, 5% of auxiliary agent, and solvent to make up the balance;

[0116] The raw materials for the preparation of the second component, in terms of weight percentages, include: 30% solvent, 0.5% dehydrating agent, and solidifying agent supplementary balance to 100%;

[0117] The resin material is hydroxy alkyd resin, and the trade name is Changxing Company 33014-X-65;

[0118] The first filler is titanium dioxide, which is BLR-895 purchased from Lomon Company;

[0119] Described second filler is talcum powder, particle diameter is 1250 meshes, purchased from Guangzhou Shenpeng Chemical Co., Ltd.;

[0120] Described auxiliary agent includes dispersant, defoamer, leve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of C09D coatings, and particularly relates to a thick-coating anti-foaming two-component coating as well as a preparation method and a construction method thereof. The invention relates to an anti-foaming double-component coating capable of being thickly coated. The preparation raw materials comprise a first component and a second component, the weight ratio of the first component to the second component is 1: (0.3-0.5); the anti-foaming double-component coating capable of being thickly coated, which is prepared by the preparation method disclosed by the invention, is mainly applied to decorative materials for furniture and home decoration, is an odorless environment-friendly coating and has convenient and rapid construction performance; according to the anti-foaming double-component coating capable of being thickly coated, the specific alkyd resin and the second filler added into the system are compounded, so that an excellent compounding synergistic effect is generated, a very remarkable contribution is provided for the anti-foaming property of the coating, the effect of post-coating can be realized in the use process of the coating, and the anti-foaming performance of the coating is improved. And internal defects are avoided, so that the performance of the paint film is prevented from being influenced.

Description

technical field [0001] The invention belongs to the technical field of CO9D coatings, and more particularly relates to thick-coating and anti-foaming two-component coatings and a preparation method and construction method thereof. Background technique [0002] With the development of my country's social economy and people's increasing demand for wood furniture, with the increase in the use of wood furniture, the traditional method of painting the surface of furniture is increasingly unable to meet people's needs. The traditional coating method is to spray multiple primers on the surface of the wood. However, after each primer is sprayed, it needs to wait for a period of drying before grinding, and then proceed to the next coating process. Such a coating process requires Consume a lot of time and manpower. [0003] However, with the advancement of technology, researchers have made more improvements and optimizations in the formulation and performance of two-component coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D7/61B05D7/24B05D1/02
CPCC09D167/08C09D7/61B05D7/24B05D1/02C08K2003/2241C08K3/22C08K3/34
Inventor 王海军汪启发易文强向安邓文根
Owner 上海君子兰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com