A kind of low temperature sintered flexible magnetic sheet and preparation method thereof

A flexible magnetic sheet, low-temperature sintering technology, applied in the direction of magnetic objects, magnetic materials, inorganic materials, etc., to solve the adhesion of upper and lower magnetic sheets, improve production efficiency and performance of magnetic sheets, and reduce sintering temperature.

Active Publication Date: 2022-01-25
TDG HLDG CO LTD
View PDF20 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent with the notification number CN110156449B discloses a method for improving the reliability of ferrite materials, but it does not involve low-temperature sintering, and there is no requirement for the power loss performance of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low temperature sintered flexible magnetic sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In this embodiment, a low-temperature sintered flexible magnetic sheet is prepared according to the following method:

[0027] 1) Mixing of raw materials: mix the raw materials in proportion to Fe 2 o 3 : 69.5 wt%, ZnO: 7.00wt% and the balance of MnO are used for batching and sanding, mixed evenly and then dried;

[0028] 2) Pre-burning: Put the dried powder into the firing bowl and put it into the pre-burning furnace and heat it to 850°C at a heating rate of 5°C / min for two hours;

[0029] 3) High-energy ball milling: After vibrating the pre-burned powder, add the auxiliary component CaCO 3 :500ppm, Nb 2 o 5 :200, CuO:1000ppm, Co 2 o 3 : 3000ppm, B 2 o 3 -ZnO-Li 2 O series glass: 1000ppm, then ball milling 2h in a high-energy ball mill to obtain D50 is 150-250nm, and D90 is nano-scale magnetic powder of 250-450nm;

[0030] 4) Pulping: Put the nano-scale magnetic powder prepared in step 3) with xylene, ethanol, and safflower oil in a certain proportion and mix...

Embodiment 2

[0035] In this embodiment, a low-temperature sintered flexible magnetic sheet is prepared according to the following method:

[0036] 1) Mixing of raw materials: mix the raw materials in proportion to Fe 2 o 3 : 69.5 wt%, ZnO: 7.00wt% and the remainder MnO to carry out batching and carry out sanding, dry after mixing evenly;

[0037] 2) Pre-burning: Put the dried powder into the firing bowl and put it into the pre-burning furnace and heat it to 850°C at a heating rate of 5°C / Min for two hours for pre-burning;

[0038] 3) High-energy ball milling: After vibrating the pre-burned powder, add the auxiliary component CaCO 3 :500ppm, Nb 2 o 5 :200, CuO:1000ppm, Co 2 o 3 : 3000ppm, Bi 2 o 3 -B 2 o 3 -SiO 2 System glass: 500ppm, then ball milling 2h in a high-energy ball mill to obtain D50 is 150-250nm, and D90 is nano-scale magnetic powder of 250-450nm;

[0039] 4) Pulping: Put the nano-scale magnetic powder prepared in step 3) with xylene, ethanol, and safflower oil in a c...

Embodiment 3

[0044] In this embodiment, a low-temperature sintered flexible magnetic sheet is prepared according to the following method:

[0045] 1) Mixing of raw materials: mix the raw materials in proportion to Fe 2 o 3 : 69.5 wt%, ZnO: 7.00wt% and the remainder MnO to carry out batching and carry out sanding, dry after mixing evenly;

[0046] 2) Pre-burning: Put the dried powder into the firing bowl and put it into the pre-burning furnace and heat it to 850°C at a heating rate of 5°C / Min for two hours for pre-burning;

[0047] 3) High-energy ball milling: After vibrating the pre-burned powder, add the auxiliary component CaCO 3 :500ppm, Nb 2 o 5 :200, CuO:1000ppm, Co 2 o 3 : 3000ppm, Bi 2 o 3 -B 2 o 3 -SiO 2 System glass: 500ppm, then obtain D50 and be 400-500nm by ball milling 1h in high-energy ball mill, D90 is the nanoscale magnetic powder of 500-700nm;

[0048] 4) Pulping: Put the nano-scale magnetic powder prepared in step 3) with xylene, ethanol, and safflower oil in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a low-temperature sintered flexible magnetic sheet and a preparation method thereof. Nano-scale ferrite magnetic powder is mainly obtained through a high-energy ball mill, and glass powder is doped in it, and finally sintered at a lower temperature to obtain a dense structure. product. Due to the high particle size uniformity of the powder used, the consistency of the electromagnetic properties of the samples is also high. Moreover, sintering at low temperature not only avoids the problem of adhesion between the upper and lower layers of the magnetic sheet during sintering, but also reduces energy consumption and production costs. The main steps of the invention are raw material mixing, 2) pre-calcination, 3) high-energy ball milling, 4) pulping, 5) casting, 6) sintering, and 7) coating splits. Finally, a magnetic sheet with low loss, high Bs and strong toughness is obtained.

Description

technical field [0001] The invention relates to the technical field of magnetic materials, in particular to a soft magnetic flexible material and a preparation process thereof. Background technique [0002] With the rise of wireless charging technology in recent years, magnetic shielding materials in wireless charging devices have received increasing attention. In the wireless charging system, the magnetic shielding material can enhance the coil induction magnetic field, improve the coil coupling coefficient, and then improve the charging efficiency; at the same time, it can shield the attenuation interference of the metal conductor to the coil magnetic field, prevent the eddy current loss from causing the battery to heat up, and realize the wireless charging system and terminal equipment. EMC function. At present, there are four kinds of widely used wireless charging magnetic shielding materials: manganese-zinc ferrite thin magnetic sheet, nickel-zinc ferrite thin magnetic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/26H01F1/34
CPCC04B35/265H01F1/344C04B2235/3284C04B2235/3279C04B2235/3262C04B2235/36C04B2235/6025C04B2235/3208C04B2235/3251C04B2235/3281C04B2235/6565C04B2235/3275C04B2235/3203C04B2235/3409C04B2235/6562C04B2235/6567
Inventor 李赟邢冰冰张强原王鸿健张志新黄艳锋盖鹏祥李伟健
Owner TDG HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap