Drilling ink and application thereof

A technology for ink and drilling, which is applied in ink, applications, household appliances, etc., can solve the problems of easy generation of burrs or residues, and high production costs, so as to improve drilling efficiency and drilling accuracy, reduce production costs, and avoid The effect of debris wrapped around the knife

Pending Publication Date: 2021-06-25
SHENZHEN BAROY NEW MATERIAL TECH CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of drilling ink and its application, aiming to solve the technical problems such as easy generation of burrs or residues and high production cost in the drilling process of traditional printed circuit boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Drilling ink and application thereof
  • Drilling ink and application thereof
  • Drilling ink and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The embodiment of the present invention provides a preparation method of drilling ink, comprising the following steps:

[0051] S1. Provide modified acrylic resin, UV monomer, photoinitiator, color paste, filler, and auxiliary agent according to the above-mentioned drilling ink formula;

[0052] S2. Mix the modified acrylic resin, UV monomer, photoinitiator, color paste, filler and auxiliary agent to obtain the drilling ink.

[0053] Preferably, in the present invention, each component in S2 is added sequentially in the following order: photoinitiator, UV monomer, auxiliary agent, modified acrylic resin, filler, color paste; among the above components, each component should be added before adding Ensure that the aforementioned components are fully dispersed and evenly distributed. The dispersibility of the drilling ink obtained in this way is better, and it is easier to obtain a smooth and flat ink film when applied to the surface of the printed circuit board to be dri...

Embodiment 1

[0066] A kind of drilling ink, its preparation method comprises the steps:

[0067] (1) Stir and dissolve the photoinitiator in the UV monomer, and then evenly disperse the auxiliary agent in it;

[0068] (2) uniformly disperse the modified acrylic resin into the system obtained in step (1), and then add the filler to disperse evenly;

[0069] (3) Add color paste to the system obtained in step (2) and disperse evenly to obtain drilling ink.

[0070] The specific selection and content of each component in Example 1 are shown in Table 1. The resulting drilling ink was sampled for physical and chemical testing and performance testing for curing drilling applications, and the results are shown in Table 2.

[0071] Table 1 Embodiment 1 each component selection and content

[0072]

[0073]

[0074] The application and performance test result of the drilling ink of table 2 embodiment 1 gained

[0075] parameter Ink Consumption(g / m 2 )

Embodiment 2

[0077] A kind of drilling ink, its preparation method comprises the steps:

[0078] (1) Stir and dissolve the photoinitiator in the UV monomer, and then evenly disperse the auxiliary agent in it;

[0079] (2) uniformly disperse the modified acrylic resin into the system obtained in step (1), and then add the filler to disperse evenly;

[0080] (3) Add color paste to the system obtained in step (2) and disperse evenly to obtain drilling ink.

[0081]The specific selection and content of each component in Example 2 are shown in Table 3. The resulting drilling ink was sampled for physical and chemical testing and performance testing for curing drilling applications, and the results are shown in Table 4.

[0082] Each component selection and content of table 3 embodiment 2

[0083] Element Content (wt%) Trifunctional novolac epoxy acrylate UV1000 46.4 Difunctional epoxy acrylate 100 15 IBOA 8 TPGDA 11 DPHA 5 1173 0.5 907 0.1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
hardnessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of electronic materials, and particularly relates to drilling ink and application thereof. The drilling ink is prepared from the modified acrylic resin, a UV monomer, a photoinitiator, color paste, a filler and auxiliaries, an ink film formed after the drilling ink is cured has high hardness, the drilling ink can replace a traditional cover plate to be used for drilling in the drilling process of the printed circuit board, the ink film can be simply removed through laser and other methods after drilling is completed, and the drilling efficiency and the drilling precision can be remarkably improved. Meanwhile, due to the fact that traditional aluminum sheets, cold punching plates and the like are not used as cover plates, the production cost can be reduced, and the problems that chippings wind a cutter and the like can be solved.

Description

technical field [0001] The invention belongs to the technical field of electronic materials, and in particular relates to a drilling ink and an application thereof. Background technique [0002] In the printed circuit board (referred to as PCB) processing and manufacturing process, affected by many factors such as materials, structural design, circuit design, pressing process and equipment, the PCB board processed by the pressing process will have a certain degree of deformation, and it will be placed on a flat surface. There are different degrees of warping deformation on the marble platform. The warping deformation of the PCB board has a great influence on the drilling process. If the PCB board is thin (below 3.0mm), the drilling position of the PCB board can be changed by appropriately increasing the pressure of the pressure foot during drilling. The warping deformation makes the PCB board and the backing board close together, and the drilling will not produce excessive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/101C09D11/03
CPCC09D11/101C09D11/03
Inventor 梁辉郑建华
Owner SHENZHEN BAROY NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap