Joint mixture for ceramic tiles and preparation method thereof

A technology of caulking agent and tiles, which is applied in the field of building decoration materials, can solve the problems of large amount of raw material addition, general weathering resistance, and poor adhesion of formulas, and achieve low unit cost, shortened construction period, and strong adhesion. Effect

Inactive Publication Date: 2021-05-07
王忠良
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] To sum up, the disadvantages of the existing joint filling materials are: the amount of raw materials added in the formula is relatively large, the cost is high, waste raw materials are not fully utilized as raw materials, the formula has poor adhesion, and it is easy to fall off after a long time. Generally, the unit cost is higher when the amount is large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A caulking agent for ceramic tiles and a preparation method thereof, comprising the following parts by weight: 30 parts of cement, 10 parts of diatomaceous earth, 5 parts of sumac seed kernel oil, 30 parts of waste mash, 10 parts of black liquor, and 10 parts of white water part, preservative (sorbic acid) 1.0 part.

[0045] Described a kind of preparation method of ceramic tile grout, comprises the following steps:

[0046] (1) After mixing the waste mash, black liquor and white water, filter through a 120-mesh filter screen to obtain a filtrate for later use;

[0047] (2) The mixed solution obtained in the above step 1) is heated to 90°C with stirring, evaporation and concentration, and when the mass percentage concentration is 55%, the concentration is stopped and the temperature is kept at 50°C for later use;

[0048] (3) Put the cement and diatomite into the oven, mix and stir for 20 minutes at a speed of 100 r / min at a high temperature of 250 °C, take out, and co...

Embodiment 2

[0051] A caulking agent for ceramic tiles and a preparation method thereof, comprising the following parts by weight: 20 parts of cement, 5 parts of diatomaceous earth, 1 part of sumac seed kernel oil, 20 parts of waste mash, 5 parts of black liquor, and 5 parts of white water parts, preservatives (sorbic acid, potassium sorbate, Kaison, mass ratio 1:1:3) 0.5 parts.

[0052] Described a kind of preparation method of ceramic tile grout, comprises the following steps:

[0053] (1) After mixing the waste mash, black liquor and white water, filter through an 80-mesh filter screen to obtain a filtrate for later use;

[0054] (2) The mixed solution obtained in the above step 1) was heated to 80°C, stirred, evaporated and concentrated, and when the mass percentage concentration was 45%, the concentration was stopped and the temperature was kept at 40°C for later use;

[0055] (3) Put the cement and diatomite into the oven, mix and stir for 15 minutes at a speed of 150r / min at a high...

Embodiment 3

[0058] A caulking agent for ceramic tiles and a preparation method thereof, comprising the following parts by weight: 25 parts of cement, 8 parts of diatomaceous earth, 3 parts of sumac seed kernel oil, 25 parts of waste mash, 6 parts of black liquor, and 6 parts of white water. 0.8 servings of preservatives (Caisson).

[0059] Described a kind of preparation method of ceramic tile grout, comprises the following steps:

[0060] (1) After mixing the waste mash, black liquor and white water, filter through a 100-mesh filter screen to obtain a filtrate for later use;

[0061] (2) heating the mixed solution obtained in the above step 1) to 85°C, stirring, evaporating and concentrating, stopping the concentration when the mass percentage concentration is 50% and keeping the temperature at 45°C for later use;

[0062] (3) Put cement and diatomite into an oven, mix and stir for 16 minutes at a speed of 150 r / min at a high temperature of 230 °C, take out, and cool down to obtain a he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a joint mixture for ceramic tiles and a preparation method thereof. The joint mixture is prepared from the following components in parts by weight: 30-50 parts of cement, 5-10 parts of diatomite, 1-5 parts of lacquer tree seed kernel oil, 20-30 parts of waste mash, 5-10 parts of black liquor and 5-10 parts of white water. The invention further discloses the preparation method of the joint mixture for the ceramic tiles. According to the raw material for the joint mixture, wastes of sugar mills, paper mills and paint mills are fully utilized, so that the wastes are recycled and reasonably utilized, and the environmental load is reduced; in addition, the joint mixture is wide in raw material source, scientific in proportion, good in air permeability, simple in production process, low in cost, high in production efficiency, good in use effect and suitable for industrial mass production. The joint mixture disclosed by the invention can be applied to the fields of ceramic tile joint filling, wall surface repairing, ground leaking stoppage and the like.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a caulking agent for ceramic tiles and a preparation method thereof. Background technique [0002] Tile is one of the durable building decoration materials and belongs to the traditional building decoration materials. The ceramic tile has a smooth surface, light weight, and can be used for large-scale decoration. Its texture is hard, wear-resistant, pressure-resistant, scrub-resistant, and has low water absorption, no discoloration, small deformation, safe and non-toxic, and does not pollute the environment. Construction and maintenance It is convenient and can meet the functional requirements of any space for wall or floor materials. It is one of the most commonly used wall or floor decoration materials in home decoration. And it has rich colors, many patterns and patterns, and is highly decorative. With the continuous improvement of production technology,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/27C04B111/20
CPCC04B28/00C04B2111/27C04B2111/20C04B2111/00663C04B18/241C04B18/24C04B14/08C04B22/0046C04B24/04C04B24/008
Inventor 王忠良
Owner 王忠良
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com