Method of reducing tin defects in glass product

A product and defect technology, applied in the field of reducing tin defects in glass products, can solve the problem of dripping onto the upper surface of the glass ribbon or condensing into tin droplets and then dripping onto the upper surface of the glass ribbon, and the tin liquid surface cannot be covered by the glass ribbon , affect the glass quality and other issues, to improve the internal space environment, reduce the exposed area, reduce the effect of tin evaporation

Pending Publication Date: 2021-01-05
CHINA LUOYANG FLOAT GLASS GROUP
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because float glass manufacturers need to adjust product specifications frequently according to market demand, this requires a large distance between the glass ribbon in the tin bath and the edge of the tin bath, resulting in a large area of ​​tin liquid surface that cannot be covered by the glass ribbon. We refer to the tin liquid surface in the tin bath not covered by the glass tape as the exposed tin liquid surface in the tin bath, and the exposed tin liquid surface in the tin bath will continuously evaporate the tin liquid, forming a large amount of tin in the tin bath. Steam, tin vapor is oxidized and drips onto the upper surface of the glass ribbon or condenses into tin droplets and then drips onto the upper surface of the glass ribbon, resulting in tin defects and affecting glass quality, etc.
[0003] The inventor found through searching that those skilled in the art have not yet proposed a method to solve the above technical problems. Therefore, how to propose a method for reducing tin defects in glass products has become a long-term technical appeal for those skilled in the art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of reducing tin defects in glass product
  • Method of reducing tin defects in glass product
  • Method of reducing tin defects in glass product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The present invention can be explained in more detail by the following examples, and the present invention is not limited to the following examples;

[0028] First of all, it should be noted that the terms "upper", "lower", "front", "rear", "left", "right", "top", "bottom", "inside", etc. The orientation or positional relationship indicated by "outside" is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of description and simplification of description, rather than indicating or implying that the device or element referred to must have a specific orientation, use a specific configuration and operation, and therefore should not be construed as limiting the invention.

[0029] combined with Figure 1~3 A method for reducing tin defects in glass products, said method specifically comprising the steps of:

[0030] The first step is to adjust the liquid tin covering device according to the specifications of the glas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for reducing tin defects in a glass product, relates to the technical field of glass production, and aims to assemble an exposed tin liquid level graphite cover plate(4) matched with a tin liquid tank (7) according to the shape and size of the surface area of exposed tin liquid (6) in the tin liquid tank (7), cover the exposed tin liquid level in the tin liquid tank and reduce the exposed area of the tin liquid in the tin liquid tank to the greatest extent. The method has the advantages that the operation steps are simple, the use effect is good, and the method is suitable for large-scale popularization and application. The tin evaporation is effectively reduced, the internal space environment of the tin liquid tank is improved, and the quality of the glass tape is improved.

Description

technical field [0001] The invention relates to the technical field of glass production, in particular to a method for reducing tin defects in glass products. Background technique [0002] It is known that with the development of the glass production and processing industry, especially the increase in the amount of electronic glass, the quality requirements of the original glass are getting higher and higher. Taking float glass as an example, the main reason affecting the quality of float glass is currently One of these is tin defects. Because float glass manufacturers need to adjust product specifications frequently according to market demand, this requires a large distance between the glass ribbon in the tin bath and the edge of the tin bath, resulting in a large area of ​​tin liquid surface that cannot be covered by the glass ribbon. We refer to the tin liquid surface in the tin bath not covered by the glass tape as the exposed tin liquid surface in the tin bath, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B18/16C03B18/02
CPCC03B18/02C03B18/16Y02P40/57
Inventor 谢军郭卫杨慧杰董明张艳娟郭利波郭钧理
Owner CHINA LUOYANG FLOAT GLASS GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com