Colorful SMC material applied to bathroom products and preparation method thereof

A sanitary product and colorful technology, applied in the field of colorful SMC materials and its preparation, can solve the problems of surface gloss and color loss, low production efficiency, complicated procedures, etc., achieve high surface gloss, improve production efficiency, and good mechanical strength Effect

Inactive Publication Date: 2020-11-17
广东百汇达新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the traditional colorful bathroom SMC products adopt the method of secondary spraying or product surface stickers, the procedure is complicated, the surface gloss and color are easy to fade with time, the production efficiency is low and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A colorful SMC material used in sanitary products, which consists of the following components by weight percentage: continuous phase resin paste 69.6%; dispersed phase toning base paint 3%; 25% magnesium oxide (RA-150) thickening Agent 1.4%; 25mm OWENSP204-4800 alkali-free glass fiber 26%.

[0050]The raw materials of the continuous phase resin paste are as follows (by weight): 65 parts of unsaturated resin HS-1520, 35 parts of low-profile additive HS-9817, 1.2 parts of curing agent TBPB, 0.75 parts of polymerization inhibitor, 4.5 parts of zinc stearate, 1.5 parts of BYK W-9010 wetting and dispersing agent p-benzoquinone, 1 part of BYK W-9076 wetting and dispersing agent, 160 parts of aluminum hydroxide, 50 parts of calcined kaolin, 10 parts of titanium dioxide.

[0051] The raw materials of the dispersed phase toning base paint are as follows (by weight): 16.5 parts of ethyl cellulose, 10 parts of mesoflagellate, 60 parts of α-methylstyrene, 14.5 parts of formamide, 1...

Embodiment 2

[0060] A colorful SMC material used in sanitary products, composed of the following components by weight percentage: 65.9% of continuous phase resin paste; 2.5% of dispersed phase toning base paint; 25% by weight of magnesium oxide (RA-150) Thickener 1.6%; 25mmOWENS P204-4800 alkali-free glass fiber 30%.

[0061] The raw materials of the continuous phase resin paste are as follows (by weight): 45 parts of unsaturated resin HS-1520, 15 parts of unsaturated resin LY-S28803, 30 parts of low-profile additive HS-9817, 10 parts of low-profile additive HS-9812, 1 1 part of curing agent TBPB, 0.5 part of polymerization inhibitor p-benzoquinone, 4 parts of zinc stearate, 2 parts of wetting and dispersing agent BYK W-9010, 1 part of wetting and dispersing agent BYK W-9076, 180 parts of aluminum hydroxide, 50 parts 1 part of calcined kaolin, 10 parts of titanium dioxide.

[0062] The raw materials of the dispersed phase toning base paint are as follows (by weight): 17.6 parts of ethyl c...

Embodiment 3

[0071] A colorful SMC material used in sanitary products, composed of the following components by weight percentage: 70.5% continuous phase resin paste; 3% dispersed phase tinting base paint; 25% magnesium oxide (RA-150) thickening Agent 1.5%; 25mm OWENSP204-4800 alkali-free glass fiber 25%.

[0072] The raw materials of the continuous phase resin paste are as follows (by weight): 65 parts of unsaturated resin HS-1520, 35 parts of low-profile additive HS-9817, 1.2 parts of curing agent TBPB, 0.7 parts of polymerization inhibitor 2,6-di-tert-butyl p-cresol, 4.5 parts of zinc stearate, 1 part of BYKW-9010 wetting and dispersing agent, 1 part of BYK W-9076 wetting and dispersing agent, 150 parts of aluminum hydroxide, 50 parts of calcined kaolin, 10 parts of titanium dioxide.

[0073] The raw materials of the dispersed phase toning base paint are as follows (by weight): 15.5 parts of ethyl cellulose, 8 parts of iron red, 60 parts of α-methylstyrene, 12 parts of formamide, 1.3 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colorful SMC material applied to bathroom products, which comprises the following components in percentage by weight: 65.9-73% of continuous-phase resin paste, 1-3% of dispersed-phase color matching base paint, 1-1.6% of a thickener and 25-30% of alkali-free glass fibers, and the sum of the weight percentages of the components is 100%. The invention also provides a preparation method of the colorful SMC material. The colorful SMC material disclosed by the invention has the advantages of good surface gloss, various colors, good product color stability, good mechanicalstrength and simple production process.

Description

technical field [0001] The invention belongs to the field of chemical composite materials, and in particular relates to a colorful SMC material used in sanitary products and a preparation method thereof. Background technique [0002] Thermosetting resin glass fiber reinforced composite material, Sheet Molding Compound (SMC for short), is a kind of glass fiber reinforced composite material. It is based on unsaturated polyester resin, low shrinkage additives, thickeners, initiators, mold release agents, fillers, colorants, etc. mixed into a resin paste, and then impregnated with chopped glass fiber roving or glass chopped mat, and on both sides The "sandwich" molding compound formed by wrapping polyethylene or polypropylene film can be used after a certain period of aging. The SMC molding process is currently mainly molded, solidified and demolded under heating and pressure conditions to obtain a closed-film molding composite material technology for the desired product. Comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08L67/00C08L33/12C08L1/28C08K13/04C08K7/14C08K3/22C08K3/34C08J5/04
CPCC08J5/043C08J2367/06C08J2467/00C08J2433/12C08J2401/28C08K13/04C08K7/14C08K2003/2224C08K3/346C08K2003/2241
Inventor 彭新龙周立新陆志华江林鹤梁卓恩
Owner 广东百汇达新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com