Preparation method of water-borne PU adhesive for zero DMF immersion gloves

A water-based, glove technology, applied in the field of material preparation, can solve the problems of damaged skin and liver function, unfavorable health of workers, large water demand and energy consumption, etc. The effect of porosity

Inactive Publication Date: 2019-11-08
上海深禾聚合物材料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional production method of PU coated gloves, it is necessary to use dimethylformamide (DMF) solvent. DMF is N,N-dimethylformamide, which belongs to the second class of carcinogens and has high toxicity. It is harmful to the skin and liver. Function is damaged, flammable during use, such as DMF residues in gloves, which can be absorbed through the skin and respiratory tract after wearing, causing damage to liver function, affecting reproductive function, and adversely affecting the health of workers. Moreover, DMF The manufacturing process of the active solvent is complicated, and the water demand and energy consumption are very large, resulting in a waste of resources and not conducive to environmental protection. Therefore, the European Union has been committed to banning practical DMF, but there is no DMF-free gloves on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation method of zero DMF dipped gloves water-based PU glue, described water-based PU glue is made up of following weight ratio composition:

[0028] Water-based polyurethane dispersion 70%, anti-wear agent 2%, wax emulsion 1%, cell opener 0.5%, wetting agent 0.1%, adhesive 2%, foaming agent 1%, foam stabilizer 1%, association Type thickener 0.4%, deionized water 10%;

[0029] Its preparation steps include:

[0030] S1, take a certain amount of water-based polyurethane dispersion and place it in the mixing tank; the mixing tank is a stainless steel mixing tank with a smooth inner wall;

[0031] S2, an agitator is set outside the stainless steel mixing tank, the driving end of the agitator extends into the stainless steel mixing tank, and is stirred at a speed of 500-1100r / min;

[0032] S3, taking appropriate ratio of deionized water, foaming agent, foam stabilizer, adhesive and wetting agent into the water-based polyurethane dispersion, stirring for 5-13 minu...

Embodiment 2

[0040] The preparation method of zero DMF dipped gloves water-based PU glue, described water-based PU glue is made up of following weight ratio composition:

[0041] Water-based polyurethane dispersion 75%, anti-wear agent 3%, wax emulsion 3%, cell opener 2%, wetting agent 0.5%, adhesive 2.5%, foaming agent 2.5%, foam stabilizer 2.5%, association Type thickener 0.6%, deionized water 10%;

[0042] Its preparation steps include:

[0043] S1, take a certain amount of water-based polyurethane dispersion and place it in the mixing tank; the mixing tank is a stainless steel mixing tank with a smooth inner wall;

[0044] S2, an agitator is set outside the stainless steel mixing tank, the driving end of the agitator extends into the stainless steel mixing tank, and is stirred at a speed of 500-1100r / min;

[0045] S3, taking appropriate ratio of deionized water, foaming agent, foam stabilizer, adhesive and wetting agent into the water-based polyurethane dispersion, stirring for 5-13 ...

Embodiment 3

[0053] The preparation method of zero DMF dipped gloves water-based PU glue, described water-based PU glue is made up of following weight ratio composition:

[0054] Water-based polyurethane dispersion 80%, anti-wear agent 5%, wax emulsion 5%, cell opener 3%, wetting agent 1%, adhesive 3%, foaming agent 4%, foam stabilizer 4%, association Type thickener 0.8%, deionized water 20%;

[0055] Its preparation steps include:

[0056] S1, take a certain amount of water-based polyurethane dispersion and place it in the mixing tank; the mixing tank is a stainless steel mixing tank with a smooth inner wall;

[0057] S2, an agitator is set outside the stainless steel mixing tank, the driving end of the agitator extends into the stainless steel mixing tank, and is stirred at a speed of 500-1100r / min;

[0058] S3, taking appropriate ratio of deionized water, foaming agent, foam stabilizer, adhesive and wetting agent into the water-based polyurethane dispersion, stirring for 5-13 minutes;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a water-borne PU adhesive for zero DMF immersion gloves. The water-borne PU adhesive is prepared from the following components in percentage by weight:70-80% of water-borne polyurethane dispersion bodies, 2-5% of a wear-resistant agent, 1-5% of a wax emulsion, 0.5-3% of a pore opener, 0.1-1% of a wetting agent, 2-3% of an adhesive, 1-4% of a foamingagent, 1-4% of a foam stabilizer, 0.4-0.8% of a synthesis thickener, and 10-20% of deionized water. The preparation method includes the following steps that S1, a certain amount of the aqueous polyurethane dispersion bodies is taken and placed in a mixing tank; and S2, a mixer is arranged outside a stainless steel mixing cylinder, a drive end of the mixer extends into the stainless steel mixing cylinder, and mixes at a rotating speed of 500-1100 r / min. According to the preparation method, a PU adhesive does not use DFM, and is safe and environmental-friendly; by adding the wear-resistant agent, the pore opener, the wax emulsion, and the like, the softness and hand feeling of the gloves made by the PU adhesive are improved; and meanwhile, the hardness and wear resistance of the gloves areimproved, and the gloves are soft and wearable.

Description

technical field [0001] The invention relates to the technical field of material preparation, in particular to a preparation method of water-based PU glue for zero-DMF dipped gloves. Background technique [0002] PU coated gloves completely cover the palm part with specially treated polyurethane, which can provide good anti-skid performance and prevent hand sweat and particle pollution from the palm of the human body. Generally, the glove core is dipped and dried with PU glue on the glove mold. forming. In the traditional production method of PU coated gloves, it is necessary to use dimethylformamide (DMF) solvent. DMF is N,N-dimethylformamide, which belongs to the second class of carcinogens and has high toxicity. It is harmful to the skin and liver. Function is damaged, flammable during use, such as DMF residues in gloves, which can be absorbed through the skin and respiratory tract after wearing, causing damage to liver function, affecting reproductive function, and adver...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L9/02C08L91/06C08K5/3492C08J9/04C08G18/66C08G18/48C08G18/34C08G18/32C08G18/12
CPCC08G18/12C08G18/348C08G18/4854C08G18/6651C08G18/6659C08J9/0028C08J9/0061C08J9/04C08J2375/04C08J2409/02C08J2491/06C08K5/34922C08G18/3228
Inventor 吴志清
Owner 上海深禾聚合物材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products