A kind of method for preparing silicon dioxide/titanium dioxide composite film containing dendritic pore structure on substrate

A technology of silicon dioxide and titanium dioxide, applied in the direction of coating, etc., can solve the problems of super-hydrophilic effect failure and other problems, and achieve the effects of good wear resistance, non-failure, and good dirt resistance

Active Publication Date: 2021-11-30
FUJIAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, on the one hand, there are still very few research reports on the function of superhydrophilicity and water storage. It is an innovative work to prepare a structure with regular pores to achieve the performance of absorbing water, transporting water and storing water; Regarding the durability of the super-hydrophilic coating, since the surface of the hydrophilic oxide contains a large number of hydroxyl groups that have the characteristics of absorbing water, it shows super-hydrophilic anti-fog properties macroscopically, but as time goes on, its surface The hydroxyl content of the coating gradually decreases, and the super-hydrophilic effect will gradually fail. Therefore, the development of a high-efficiency and long-lasting super-hydrophilic coating has become a frontier topic in current development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing silicon dioxide/titanium dioxide composite film containing dendritic pore structure on substrate
  • A kind of method for preparing silicon dioxide/titanium dioxide composite film containing dendritic pore structure on substrate
  • A kind of method for preparing silicon dioxide/titanium dioxide composite film containing dendritic pore structure on substrate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Surface polishing: the ordinary float glass with length 50mm×width 30mm×height 1mm is first soaked in acetone for 10-60 minutes, then ultrasonically washed with ethanol solution for 5-60 minutes, and then cleaned with deionized water to obtain a clean surface. substrate.

[0040] (2) Preparation of sol mixture:

[0041] Preparation of titanium dioxide sol: Pour 120mL of absolute ethanol into a dry beaker, then slowly drop 30mL of butyl titanate into the beaker at a rate of 0.2mL per minute, and stir at a speed of 800r / s for 10 minutes; Then slowly add 2 mL of acetylacetone dropwise at a rate of 0.2 mL per minute, and continue to stir vigorously at a rate of 800 r / s for 10 min; add catalyst nitric acid dropwise at a rate of 0.2 mL per minute to adjust the pH to 2-3 In between, stir for 1 h to obtain titanium dioxide sol.

[0042] Preparation of silica sol: add 4mL tetraethyl orthosilicate, 4mL, and 4m deionized water into a beaker and stir; add 2mL of ammonia water...

Embodiment 2

[0046] (1) Ordinary float glass with a length of 50 mm × width 30 mm × height 1 mm is first soaked in acetone for 10-60 min, then ultrasonically washed with ethanol solution for 5-60 min, and then cleaned with deionized water to obtain a substrate with a clean surface.

[0047] (2) Preparation of sol mixture

[0048] Preparation of titanium dioxide sol: Pour 120mL of absolute ethanol into a dry beaker, then slowly drop 30mL of butyl titanate into the beaker at a rate of 0.2mL per minute, and stir at a speed of 800r / s for 10 minutes; Then slowly add 2 mL of acetylacetone dropwise at a rate of 0.2 mL per minute, and continue to stir vigorously at a rate of 800 r / s for 10 min; add catalyst nitric acid dropwise at a rate of 0.2 mL per minute to adjust the pH to 2-3 In between, stir for 1 h to obtain titanium dioxide sol.

[0049] Preparation of silica sol: add 4mL tetraethyl orthosilicate, 4mL, and 4m deionized water into a beaker and stir; add 2mL of ammonia water (concentration...

Embodiment 3

[0053] (1) Surface polishing: the ordinary float glass with length 50mm×width 30mm×height 1mm is first soaked in acetone for 10-60 minutes, then ultrasonically washed with ethanol solution for 5-60 minutes, and then cleaned with deionized water to obtain a clean surface. substrate.

[0054] (2) Preparation of sol mixture:

[0055] Preparation of titanium dioxide sol: Pour 120mL of absolute ethanol into a dry beaker, then slowly drop 30mL of butyl titanate into the beaker at a rate of 0.2mL per minute, and stir at a speed of 800r / s for 10 minutes; Then slowly add 2 mL of acetylacetone dropwise at a rate of 0.2 mL per minute, and continue to stir vigorously at a rate of 800 r / s for 10 min; add catalyst nitric acid dropwise at a rate of 0.2 mL per minute to adjust the pH to 2-3 In between, stir for 1 h to obtain titanium dioxide sol.

[0056] Preparation of silica sol: add 4mL tetraethyl orthosilicate, 4mL, and 4m deionized water into a beaker and stir; add 2mL of ammonia water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a low-temperature sol-gel method for preparing a functional oxide SiO on a substrate 2 / TiO 2 The invention relates to a method for regulating the pore structure of a composite film, which belongs to the field of preparation of nano functional materials. Preparation of SiO from Ethyl Orthosilicate 2 Sol, using butyl titanate as raw material to prepare TiO 2 sol, the above two sols are mixed in a certain proportion, and the prepared SiO 2 / TiO 2 The composite film is rich in regular dendritic structure, and by regulating the polymer and SiO 2 Sol and TiO 2 The cross-linking reaction between sols can effectively control the pore structure. The coating structure of the present invention is uniquely designed, presenting a dendritic and regularly distributed pore structure; the pore structure is beneficial to the characteristics of water transmission and water storage, and has a super-hydrophilic effect with good durability, and is a self-cleaning function with excellent performance film material.

Description

technical field [0001] The invention relates to a method for preparing SiO with dendritic hole structure on a substrate 2 / TiO 2 The method of composite thin film, especially relates to a kind of low-temperature sol-gel method to prepare a kind of functional oxide SiO on the substrate 2 / TiO 2 The invention relates to a method for regulating the pore structure of a composite film, which belongs to the field of preparation of nano functional materials. Background technique [0002] Self-cleaning glass (Self-cleaning glass) refers to the special physical or chemical treatment of ordinary glass, which produces unique physical and chemical properties on the surface, so that the glass can achieve cleaning effect without traditional manual scrubbing methods. Glass. Anti-fogging glass refers to the special treatment of ordinary glass to make the surface super-hydrophilic, so that the tiny water droplets formed due to atomization can be quickly flattened, so that it has self-cle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/00
CPCC03C17/002C03C17/006C03C2218/11C03C2218/32
Inventor 吴玉萍王乾廷孙炜王逸斌陈钟辉林本祥雷鸣
Owner FUJIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap