A kind of sound insulation material and preparation method thereof

A technology of sound insulation materials and foam ceramics, which is applied in the field of materials, can solve the problems of complex preparation process, flammability, and high VOC concentration, and achieve the effect of simple construction process, improved physical properties, and good reproducibility

Active Publication Date: 2021-12-31
广州凝博科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it has the disadvantages of complicated preparation process, high VOC concentration and flammability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sound insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A sound insulation material, made of the following components in parts by weight: 60 parts of high damping silicone rubber, 4 parts of hydroxyl silicone oil, 12 parts of silica airgel, 1 part of dicumyl peroxide, PP resin 60 parts, 18 parts of turpentine, 20 parts of white carbon black, 23 parts of foam ceramic powder, 2 parts of barium sulfate, 0.4 parts of sodium stearate, 0.3 parts of active zinc oxide, 6 parts of diatomaceous earth, 3 parts of zinc borate, high ethylene 5 parts of base silicone oil, 0.2 parts of silane coupling agent, 3 parts of vulcanizing agent, and 1.4 parts of accelerator.

[0032] A method for preparing a sound-insulating material, comprising the steps of:

[0033] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0034] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl silicone oil, alu...

Embodiment 2

[0044] A sound insulation material, made of the following components in parts by weight: 65 parts of high damping silicone rubber, 4.5 parts of hydroxyl silicone oil, 15 parts of silica airgel, 1.2 parts of dicumyl peroxide, PP resin 65 parts, 19 parts of turpentine, 22 parts of white carbon black, 25 parts of foam ceramic powder, 2.5 parts of barium sulfate, 0.5 parts of sodium stearate, 0.35 parts of active zinc oxide, 7 parts of diatomaceous earth, 4 parts of zinc borate, high ethylene 6 parts of base silicone oil, 0.25 parts of aluminate coupling agent, 3.5 parts of vulcanizing agent, and 1.5 parts of accelerator.

[0045] A method for preparing a sound-insulating material, comprising the steps of:

[0046] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0047] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl s...

Embodiment 3

[0057] A sound insulation material, made of the following components in parts by weight: 70 parts of high damping silicone rubber, 5 parts of hydroxyl silicone oil, 18 parts of silica airgel, 1.4 parts of dicumyl peroxide, PP resin 70 parts, 21 parts of turpentine, 24 parts of white carbon black, 29 parts of foam ceramic powder, 3 parts of barium sulfate, 0.7 parts of sodium stearate, 0.45 parts of active zinc oxide, 8 parts of diatomaceous earth, 5 parts of zinc borate, high ethylene 7 parts of base silicone oil, 0.35 parts of aluminate coupling agent, 4 parts of vulcanizing agent, and 1.7 parts of accelerator.

[0058] A method for preparing a sound-insulating material, comprising the steps of:

[0059] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0060] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl silicon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sound insulation material, which is made of the following components in parts by weight: 60-80 parts of high damping silicone rubber, 4-6 parts of hydroxyl silicone oil, 12-25 parts of silicon dioxide airgel, Dicumyl oxide 1~2 parts, PP resin 60~80 parts, turpentine 18~25 parts, white carbon black 20~30 parts, foam ceramic powder 23~38 parts, barium sulfate 2~4 parts, sodium stearate 0.4~0.9 parts, 0.3~0.5 parts of activated zinc oxide, 6~10 parts of diatomaceous earth, 3~7 parts of zinc borate, 5~8 parts of high vinyl silicone oil, 0.2~0.4 parts of aluminate coupling agent, vulcanizing agent 3~5 parts, accelerator 1.4~1.9 parts. Also disclosed is a preparation method of the sound insulation material. The sound insulation material provided by the invention has the characteristics of light weight, good mechanical performance, fire resistance and flame retardancy, and the ability to effectively absorb low-frequency sound waves. The preparation method is simple, the cost is low, and it can be produced in batches.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a sound-insulating material and a preparation method thereof. Background technique [0002] Noise pollution has become a global environmental problem and has seriously affected people's production and life. The demand for sound-absorbing materials in modern society is increasing, and the performance requirements for sound-absorbing materials are also getting higher and higher. Existing sound-absorbing materials have good sound-absorbing performance in the high-frequency band of noise, but poor sound-absorbing performance in the low-frequency band. How to improve the sound-absorbing performance of sound-absorbing materials in the low-frequency range has become a difficult point in the field of sound-absorbing materials research. [0003] Existing decorative materials have waterproof, fireproof, anti-aging, poor impact resistance, high energy consumption of materials, are not e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04C08L23/12C08L83/07C08K7/26C08K3/36C08K3/30C08K3/22C08K3/38C08K5/098C08K5/10
CPCC08L23/12C08L83/04C08K2003/3045C08K2003/2296C08K2003/387C08L2205/035C08L2205/025C08L2201/02C08K7/26C08K3/36C08K3/30C08K3/22C08K3/38C08K5/098C08K5/10
Inventor 海苗苗李明珠
Owner 广州凝博科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com