A rolling method for reducing the hardness and bending degree of 42crmo hot-rolled state

A bending and hardness technology, applied in the field of rolling to reduce the hardness and bending of 42CrMo hot-rolled state, can solve the problems of production organization and downstream users, easy to form cracks, fractures, large bending degree of hot-rolled state, etc., to achieve The effect of shortening the production cycle, improving the hardness of the hot-rolled state, and improving the bending degree

Active Publication Date: 2020-04-21
NANJING IRON & STEEL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the production process of this steel type, there are problems of large bending degree and high hardness in the hot-rolled state, which lead to the problem of difficult blanking
And it is easy to form cracks, fractures and other defects during cold shearing, shrinking rods, drawing and other processing
Although it meets the requirements of "GB / T 702-2017 Hot Rolled Steel Bar Size, Shape, Weight and Allowable Deviation", it still causes great troubles to production organizations and downstream users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A rolling method for reducing the hardness and bending degree of 42crmo hot-rolled state
  • A rolling method for reducing the hardness and bending degree of 42crmo hot-rolled state
  • A rolling method for reducing the hardness and bending degree of 42crmo hot-rolled state

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Below, the present invention will be described in further detail in conjunction with the accompanying drawings.

[0016] A rolling method that reduces 42CrMo hot-rolled state hardness and curvature, comprises the steps:

[0017] (1) Heating: The purpose of this step is to heat the billet to the temperature range of the austenite single-phase solid solution structure, and have enough time to homogenize and dissolve carbides, thereby improving the shaping of the steel, reducing deformation resistance, and improving the internal structure. and performance for easy rolling. The specific requirement is to carry out step-by-step heating on the blank, and the step-by-step heating includes a non-heating section, a preheating section, a heating section, a heating section, a soaking section, and a soaking section; The temperature of the heating section is 600-850°C, the heating rate is 0.180-0.254°C / s, the temperature of the preheating section is 800-1020°C, the heating rate is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Brinell hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rolling method capable of reducing hot-rolled hardness and curvature of 42CrMo. The rolling method comprises the following steps of: (1) performing step type heating on blank; (2) rolling the blank; and (3), cooling the rolled steel. A metallographic microstructure of 42CrMo rolled by the method is ferrite, pearlite and bainite, and prevents a central area of the steel from generating a great deal of the needle-like martensite structure which is in blocky distribution, is high in strength and hardness, and is relatively poor in plasticity. The rolling method effectively improves the hot-rolled hardness of steel to be 240-300HB, and also solves the problem that curvature is worsened as a result of hardness reduction, so that the hot-rolled curvature of the steel is97.34% or higher within 0.4%. Hot-rolled direct delivery use is met, the hardness does not need to reduce by follow-up annealing, and the curvature does not need to improve by straightening. The production period is shortened, and production consumption is reduced.

Description

technical field [0001] The invention relates to a steel rolling process, in particular to a rolling method for reducing the hardness and curvature of 42CrMo in a hot-rolled state. Background technique [0002] 42CrMo is a common steel used in mechanical engineering and has a wide range of uses. It is mainly used in the manufacture of bolts, gears, gear shafts, shafts, and other equipment parts. In the production process of this steel type, there are problems of large bending degree and high hardness in the hot-rolled state, resulting in difficulty in blanking. And it is easy to form defects such as cracking and fracture during cold shearing, rod shrinkage, drawing and other processing. Although it meets the requirements of "GB / T 702-2017 Hot Rolled Steel Bar Size, Shape, Weight and Allowable Deviation", it still causes great troubles to production organizations and downstream users. Contents of the invention [0003] Purpose of the invention: In order to overcome the def...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B37/74C21D8/00
CPCB21B37/74C21D8/005C21D2211/002C21D2211/005C21D2211/009
Inventor 徐伟
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com