A continuous macroscopic graphene nanoribbon fiber and preparation method thereof

A graphene nanoribbon and fiber technology, which is applied in the direction of graphene, nanocarbon, fiber chemical characteristics, etc., can solve the problem of unrealized macroscopic graphene nanoribbon fiber, and achieve high strength, easy regulation and high quality.

Active Publication Date: 2022-04-12
QUJING NORMAL UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the graphene nanoribbons prepared by the above method are all dispersed and free
Preparation of continuous macroscopic graphene nanoribbon fibers has not yet been realized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A continuous macroscopic graphene nanoribbon fiber and preparation method thereof
  • A continuous macroscopic graphene nanoribbon fiber and preparation method thereof
  • A continuous macroscopic graphene nanoribbon fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Weigh and mix ethanol, ferrocene, and thiophene according to the mass ratio of 150:3:1, then add deionized water, and mix well by ultrasonication for 30 minutes to obtain a uniform reaction liquid, wherein the mass fraction of water in the reaction liquid is 25%. The reaction liquid was injected into the tubular reaction furnace with 1000 sccm hydrogen carrier gas flow at a rate of 8 mL / h with a micro-syringe pump. The temperature in the reaction zone was 1150 °C. Graphene nanoribbons grew and assembled in the reaction zone to form filamentous aggregates. , moved to the end of the reaction furnace driven by the hydrogen flow, the graphene nanoribbon aggregates were pulled out from the reaction furnace, densely shrunk by water, and wound on the spinning shaft at a spinning speed of 4 m / min to obtain a continuous macroscopic Graphene nanoribbon fibers.

[0021] The continuous macroscopic graphene nanoribbon fibers prepared by the above steps and conditions can reach hundr...

Embodiment 2

[0023] Change the content of deionized water to 15%, and other experimental processes and conditions are the same as in Example 1.

[0024] Specifically: weigh and mix ethanol, ferrocene, and thiophene according to the mass ratio of 150:3:1, then add deionized water, and mix evenly by ultrasonication for 30 minutes to obtain a uniform reaction solution. The mass fraction of water in the reaction solution is 15%. The reaction liquid was injected into the tubular reaction furnace with 1000 sccm hydrogen carrier gas flow at a rate of 8 mL / h with a micro-syringe pump. The temperature in the reaction zone was 1150 °C. Graphene nanoribbons grew and assembled in the reaction zone to form filamentous aggregates. , moved to the end of the reaction furnace driven by the hydrogen flow, the graphene nanoribbon aggregates were pulled out from the reaction furnace, densely shrunk by water, and wound on the spinning shaft at a spinning speed of 4 m / min to obtain a continuous macroscopic Gra...

Embodiment 3

[0027] Change the content of deionized water to 10%, and other experimental procedures and conditions are the same as in Example 1.

[0028] Specifically: weigh and mix ethanol, ferrocene, and thiophene according to the mass ratio of 150:3:1, then add deionized water, and mix evenly by ultrasonication for 30 minutes to obtain a uniform reaction solution. The mass fraction of water in the reaction solution is 10%. The reaction liquid was injected into the tubular reaction furnace with 1000 sccm hydrogen carrier gas flow at a rate of 8 mL / h using a micro-syringe pump. The temperature in the reaction zone was 1150 °C. The reaction liquid cracked and grew in the reaction zone and assembled to form cylindrical aggregates. Driven by the hydrogen flow, it moves to the end of the reactor, pulls the aggregates out of the reactor, shrinks them densely with water, and winds them on the spinning shaft at a spinning speed of 4 m / min to produce a continuous fiber product.

[0029]The produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
widthaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a continuous macroscopic graphene nanoribbon fiber and a preparation method thereof. The invention uses a high water content reaction solution as a raw material to prepare continuous macroscopic continuous graphene nanoribbon fibers by utilizing water molecules at high temperature to interfere with and cut the growth and assembly of carbon nanotubes through chemical vapor deposition. The key process of the preparation method of the present invention is to control the mass fraction of deionized water in the reaction solution within the range of 15-40%, preferably 20-35%. The graphene nanobelt fiber prepared by the invention is uniform and continuous, has high purity and high quality. The fiber also has light weight, high strength, high electrical conductivity, and excellent flexibility, which provides a new type of macroscopic fiber material for the development of flexible wearable electronic devices. At the same time, the preparation method is a one-step dry spinning method, the preparation process is simple, easy to control, continuous preparation is possible, and large-scale production can be realized.

Description

technical field [0001] The invention relates to a continuous macroscopic graphene nanoribbon fiber and a preparation method thereof, belonging to the technical field of carbon nanomaterials and preparation thereof. Background technique [0002] Since graphene was discovered in 2004, with its excellent mechanical (theoretical fracture strength 1 TPa), electrical (theoretical electron mobility is 10 6 cm 2 •V -1 •s -1 ), thermal (theoretical thermal conductivity 5000 W·m -1 • K -1 ), optics (monolayer visible light absorption is only 2.3%) and other properties have attracted much attention. Graphene nanoribbons refer to narrow strips of graphene materials with a width of nanoscale and a certain aspect ratio. Graphene nanoribbons not only have all the structural and functional properties of graphene, but also show unique electron transport properties due to the limitation of electron transport in the width direction of the nanoscale. Its electrical properties are semico...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/186D01F9/127
CPCD01F9/1277C01B32/186C01B2204/04C01B2204/26C01B2204/32C01B2204/20C01B2204/22
Inventor 康艳茹李哲徐坤何禧佳曹义明李亚利
Owner QUJING NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap