Special antifouling powder paint for surface layer self peeling type building aluminum plate and preparation method thereof
A powder coating, self-peeling technology, used in powder coatings, antifouling/underwater coatings, coatings, etc., can solve problems such as difficulty in reaching more than 30 cycles and reduced fouling resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0043] a, the preparation of alkali-soluble resin:
[0044] 1) Add maleic anhydride to a three-necked flask, add 50% solvent dipropylene glycol dimethyl ether solvent, install a condensing reflux tube, raise the temperature to 85-125°C under the protection of nitrogen, heat and stir to dissolve;
[0045] 2) Dissolve the weighed hydrophobic hardening monomer, acrylate monomer and initiator in the remaining 50% of the solvent, stir evenly, pour it into a constant pressure return-type dropping funnel, and slowly add it to In the three-necked flask, the dropping time is about 1 to 1.5 hours, keep the temperature constant, and after the dropping is completed, add an initiator of 1% of the monomer mass;
[0046] 3) Continue the reflux reaction for 2 to 4 hours, add 2 times the solvent amount of acetone to dissolve, then add 2 times the solvent amount of toluene to precipitate, filter, wash with toluene again, and vacuum dry to obtain the required alkali-soluble resin; The softening...
Embodiment 1
[0063] The special antifouling powder coating for surface self-stripping architectural aluminum formwork is made of the following components by mass percentage:
[0064] Modified matrix resin 48%;
[0065] Functional filler 48%;
[0066] Adhesion promoter 1%;
[0067] Charge regulator 1%;
[0068] Leveling agent 0.5%;
[0069] Benzoin 0.5%;
[0070] Pigment 1%.
[0071] The preparation method of the special antifouling powder coating for the surface layer self-peeling type architectural aluminum formwork, the modified matrix resin is made by the following scheme:
[0072] a, the preparation of alkali-soluble resin:
[0073] 1) Add maleic anhydride to a three-necked flask, add 50% solvent dipropylene glycol dimethyl ether solvent, install a condensing reflux tube, raise the temperature to 85°C under the protection of nitrogen, heat and stir to dissolve;
[0074] 2) Dissolve the weighed hydrophobic hardening monomer, acrylate monomer and initiator in the remaining 50% of ...
Embodiment 2
[0089] The special antifouling powder coating for surface self-stripping architectural aluminum formwork is made of the following components by mass percentage:
[0090] Modified matrix resin 50%;
[0091] Functional filler 44%;
[0092] Adhesion promoter 1.5%;
[0093] Charge regulator 1.5%;
[0094] Leveling agent 1%;
[0095] Benzoin 0.6%;
[0096] Pigment 1.4%.
[0097] The preparation method of the special antifouling powder coating for the surface layer self-peeling type architectural aluminum formwork, the modified matrix resin is made by the following scheme:
[0098] a, the preparation of alkali-soluble resin:
[0099] 1) Add maleic anhydride to a three-necked flask, add 50% solvent dipropylene glycol dimethyl ether solvent, install a condensing reflux tube, raise the temperature to 90°C under the protection of nitrogen, heat and stir to dissolve;
[0100] 2) Dissolve the weighed hydrophobic hardening monomer, acrylate monomer and initiator in the remaining 50%...
PUM
Property | Measurement | Unit |
---|---|---|
softening point | aaaaa | aaaaa |
acid value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap