Platy tile adhesive

A tile adhesive and plate-shaped technology, which is applied in the field of building materials, can solve the problems of inconvenient use of tile adhesive, achieve the effect of simple and fast paving process, convenient transportation and loading and unloading, and improve early strength

Active Publication Date: 2018-06-22
FOSHAN DONGPENG CERAMIC +3
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to propose a plate-shaped tile adhesive to solve the problem of inconvenient use of tile adhesives in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Platy tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A tile adhesive in the form of a plate, which is in the form of a plate. The compressive strength of the tile adhesive is ≥1.2MPa. The thickness of the tile adhesive is 1mm.

[0049] The raw materials of the ceramic tile adhesive include plastic solid waste and bonding material, and the weight ratio of the two is 1:2. The plastic solid waste includes one or more of kaolin tailings, calcined shale and coal gangue. The raw materials of bonding material in weight percent are as follows:

[0050] raw material

cement

Quartz sand

HMPC

Redispersible latex powder

Proportion

32％

65％

0.5％

2.5％

[0051] The weight ratio of 40-70 mesh quartz sand to 80-140 mesh quartz sand is 3:1.

[0052] After the plastic solid waste is ball milled, it is granulated with water to form plastic granules, and the plastic granules and binder are mixed evenly and pressed to form a green body, and the green body is dried to obtain a plate-shaped cerami...

Embodiment 2

[0054] A tile adhesive in the form of a plate, which is in the form of a flat plate. The compressive strength of the tile adhesive is ≥1.2MPa. The thickness of the tile adhesive is 2mm.

[0055] The raw materials of the ceramic tile adhesive include plastic solid waste and bonding material, and the weight ratio of the two is 0.7:2. The plastic solid waste includes one or more of kaolin tailings, calcined shale and coal gangue. The raw materials of bonding material in weight percent are as follows:

[0056] raw material

cement

Quartz sand

HMPC

Redispersible latex powder

Proportion

45％

53％

0.1％

1.9％

[0057] The weight ratio of 40-70 mesh quartz sand to 80-140 mesh quartz sand is 3:1.

[0058] After the plastic solid waste is ball milled, it is granulated with water to form plastic granules, and the plastic granules and binder are mixed evenly and pressed to form a green body, and the green body is dried to obtain a plate-shap...

Embodiment 3

[0060] A tile adhesive in the form of a plate, which is in the form of a flat plate. The compressive strength of the tile adhesive is ≥1.2MPa. The thickness of the tile adhesive is 3mm.

[0061] The raw materials of the ceramic tile adhesive include plastic solid waste and bonding material, and the weight ratio of the two is 0.45:2. The plastic solid waste includes one or more of kaolin tailings, calcined shale and coal gangue. The raw materials of bonding material in weight percent are as follows:

[0062] raw material

cement

Quartz sand

HMPC

Redispersible latex powder

Proportion

35％

63.7％

0.3％

1％

[0063] The weight ratio of 40-70 mesh quartz sand to 80-140 mesh quartz sand is 3:1.

[0064] After the plastic solid waste is ball milled, it is granulated with water to form plastic granules, and the plastic granules and binder are mixed evenly and pressed to form a green body, and the green body is dried to obtain a plate-sha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a platy tile adhesive. The tile adhesive is in a plate shape. The tile adhesive is preformed into a plate shape and is taken whenever needed, use is convenient, the step of on-site stirring is omitted, flying dust is avoided, and time and labor are saved; in tile laying, the tile adhesive is placed on a base face, uniform spraying is performed to activate the adhesiveness of the tile adhesive, then tiles are pasted on the tile adhesive, and thus tile laying is completed; the laying process is simple and fast.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a plate-shaped ceramic tile adhesive. Background technique [0002] Existing ceramic tile adhesives are powdery, and must be mixed with water to form a paste before use. The current methods of laying tiles using powdered tile adhesives are: [0003] 1. First clean the back of the pre-selected tiles, and check the paste base surface; [0004] 2. According to the ratio agreed in advance, first pour the required clear water into the mixing container, and then slowly pour the tile adhesive powder into the mixing container; [0005] 3. Then use an electric mixer to stir until the paste-like mucilage is uniform and free of particles and precipitation. Let it stand for a few minutes and then stir slightly, then it can be used for tiling tiles; [0006] 4. Use a scraper to evenly scrape the glue on the base surface and the back of the tiles before tiling the tiles. When til...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00637C04B2201/50C04B18/12C04B14/108C04B14/06C04B24/383C04B2103/0057C04B14/068C04B14/28C04B24/38
Inventor 钟保民徐瑜
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More