Coated 3D resin lens and preparation method thereof

A resin lens, 3D technology, applied in glasses/goggles, instruments, optics, etc., can solve problems such as insufficient wear resistance and easy scratches on the surface

Active Publication Date: 2019-11-12
HONGGUAN BIO PHARMA CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a coated 3D resin lens and its preparation method, which solves the problem that the wear resistance of the current resin lens is not enough, and the surface is prone to scratches after long-term use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The invention provides a method for preparing a coated 3D resin lens, the preparation method comprising:

[0016] (1) mixing nano titanium particles with a surface modifier to obtain modified nano titanium particles;

[0017] (2) Mix the modified nano-titanium particles and the alcohol solvent according to the mass ratio of 1-3.5:100, and react at 20-50° C. for 15-20 min to obtain a solution containing titanium oxide nanoparticles;

[0018] (3) Mix the solution containing titanium oxide nanoparticles, ethylene glycol, tetrabutyl titanate, ethylenediamine and hardening solution, and react at 30-55°C for 10-20min to obtain a coating solution;

[0019] (4) Soak the resin lens in the coating solution and take it out, then perform the first baking and the second baking successively to obtain the coated 3D resin lens; wherein, the conditions for the first baking include: The temperature is 50-70° C., and the baking time is 10-15 minutes; the conditions for the second baking ...

Embodiment 1

[0031] Mix nano-titanium particles with octadecylamine at a mass ratio of 1:10 to obtain modified nano-titanium particles; mix modified nano-titanium particles with ethanol solvent at a mass ratio of 1:100 and react at 20°C 15min, obtain titanium oxide nanoparticle solution; 100g titanium oxide nanoparticle solution, 10g ethylene glycol, 15g tetrabutyl titanate, 5g ethylenediamine and 2g hardening solution VH-10 were ultrasonically mixed (the frequency of ultrasonic mixing 10kHz, ultrasonic mixing time is 5min), and react at 30°C for 10min to obtain the coating solution; soak the resin lens in the coating solution and take it out (the soaking time is 20min, and the soaking temperature is 30°C), and then Carry out the first baking and the second baking in sequence to obtain the coated 3D resin lens; wherein, the conditions of the first baking include: the baking temperature is 50°C, and the baking time is 10 minutes; the second baking The baking conditions include: the baking t...

Embodiment 2

[0033] Mix nano-titanium particles with hexadecylamine at a mass ratio of 1:15 to obtain modified nano-titanium particles; mix modified nano-titanium particles with ethylene glycol solvent at a mass ratio of 3.5:100, and heat at 50°C The reaction was carried out for 20 minutes to obtain a titanium oxide nanoparticle solution; 100 g of titanium oxide nanoparticle solution, 20 g of ethylene glycol, 25 g of tetrabutyl titanate, 8 g of ethylenediamine and 8 g of hardening solution VH-10 were ultrasonically mixed (ultrasonic mixing frequency of 20kHz, ultrasonic mixing time of 8min), and react at 55°C for 20min to obtain a coating solution; soak the resin lens in the coating solution and take it out (the soaking time is 30min, and the soaking temperature is 35°C) , followed by the first baking and the second baking to obtain the coated 3D resin lens; wherein, the conditions of the first baking include: the baking temperature is 70°C, and the baking time is 15 minutes; the second bak...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a coated 3D (three dimensional) resin lens and a preparation method thereof. The preparation method comprises the following steps: firstly, mixing nano titanium particles witha surfactant to obtain modified nano titanium particles; secondly, mixing the nano titanium particles with an alcohol solvent according to the mass ratio of (1 to 3.5) to 100, reacting at the temperature of 20 to 50 DEG C for 15 to 20 minutes to obtain a solution containing titanium oxide nanoparticles; thirdly, mixing the solution containing the titanium oxide nanoparticles, ethylene glycol, tetrabutyl titanate, ethanediamine and hardening liquid, reacting at the temperature of 30 to 55 DEG C for 10 to 20 minutes to obtain coating liquid; fourthly, putting a resin lens into the coating liquidfor soaking and then taking out, successively carrying out first-time baking and second-time baking to obtain the coated 3D resin lens. The coated 3D resin lens has the advantages that the problems of insufficient wear resistance and high possibility of generating scratches on the surface after long-time use in the existing resin lens are solved.

Description

technical field [0001] The invention relates to the field of VR equipment, in particular to a coated 3D resin lens and a preparation method thereof. Background technique [0002] Since the birth of resin lenses, manufacturers have been pursuing how to further improve the performance of light and transparent resin lenses. However, the quality of high-quality lenses is not only determined by the lens material, but also its surface coating plays a vital role. The wear resistance of current resin lenses is not enough, and the surface is prone to scratches after long-term use. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a coated 3D resin lens with better wear resistance and less prone to scratches after long-term use and its preparation method. Contents of the invention [0004] The purpose of the present invention is to provide a coated 3D resin lens and its preparation method, which solves the problem that the current resin le...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G02C7/02G02B1/14
CPCG02B1/14G02C7/02
Inventor 冯敏
Owner HONGGUAN BIO PHARMA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap